Indentation fracture of low-dielectric constant films: Part I. Experiments and observations

  • Dylan J. Morris (a1) and Robert F. Cook (a1)

Advanced microelectronic interconnection structures will need dielectrics of low permittivity to reduce capacitive delays and crosstalk, but this reduction in permittivity typically necessitates an increase in the porosity of the material, which is frequently accompanied by reduced mechanical reliability. Failure by brittle fracture remains a typical manufacturing and reliability hurdle for this class of materials. Part I of this two-part work explores the instrumented indentation and indentation fracture responses of a variety of organosilicate low-dielectric constant (low-κ) films. Three different chemical varieties of low-κ material were tested. The influence of film thickness on the fracture response is also explored systematically. Correlations are made between instrumented indentation responses and differing modes of fracture. It is demonstrated that the elastic response of the composite film + substrate systems can be simply tied to the fraction of the total indentation strain energy in the film. These results are then used in the companion paper, Part II [D.J. Morris and R.F. Cook, J. Mater. Res.23, 2443 (2008)], to derive and use a fracture mechanics model to measure fracture properties of low-κ films.

Corresponding author
a)Address all correspondence to this author. e-mail:
Linked references
Hide All

This list contains references from the content that can be linked to their source. For a full set of references and notes please see the PDF or HTML where available.

2G.R. Anstis , P. Chantikul , B.R. Lawn D.B. Marshall : A critical evaluation of indentation techniques for measuring fracture toughness. I. Direct crack measurements. J. Am. Ceram. Soc. 64, 5331981

4A. Arora , D.B. Marshall , B.R. Lawn M.V. Swain : Indentation deformation/fracture of normal and anomalous glasses. J. Non-Cryst. Solids 31, 4151979

5D.J. Morris R.F. Cook : Indentation fracture of low-dielectric constant films: Part II. Indentation fracture mechanics model. J. Mater. Res. 23, 24432008

11K. Ikezawa T. Maruyama : Sharp tip geometry and its effect on hardness in nanoindentation experiments. J. Appl. Phys. 91, 96892002

13K. Kese D.J. Rowcliffe : Nanoindentation method for measuring residual stress in brittle materials. J. Am. Ceram. Soc. 86, 8112003

14D.J. Morris R.F. Cook : In situ cube-corner indentation of soda-lime glass and fused silica. J. Am. Ceram. Soc. 87, 14942004

15S. Lathabai , J. Rodel , T. Dabbs B.R. Lawn : Fracture mechanics model for subthreshold indentation flaws. I. Equilibrium fracture. J. Mater. Sci. 26, 21571991

16R. Dal Maschio : Application of the Hagan model for crack nucleation to radial cracks in glass. J. Mater. Sci. Lett. 4, 9481985

17B.R. Lawn A.G. Evans : A model for crack initiation in elastic/plastic indentation fields. J. Mater. Sci. 12, 21951977

18R.F. Cook L.M. Braun : Trapped cracks at indentations. II. Fracture mechanics model. J. Mater. Sci. 29, 21921994

19D.J. Morris R.F. Cook : Radial fracture during indentation by acute probes: I, Description by an indentation wedging model. Int. J. Fract. 136, 2372005

20S. Kim , Y. Toivola , R.F. Cook , K. Char , S-H. Chu , J-K. Lee , D.Y. Yoon H-W. Rhee : Organosilicate spin-on glasses. I. Effect of chemical modification on mechanical properties. J. Electrochem. Soc. 151, 372004

21Y. Toivola , K. Suhan , R.F. Cook , K. Char , J-K. Lee , D.Y. Yoon , H-W. Rhee , S.Y. Kim M.Y. Jin : Organosilicate spin-on glasses. II. Effect of physical modification on mechanical properties. J. Electrochem. Soc. 151, 452004

22Y. Toivola , J. Thurn R.F. Cook : Structural, electrical, and mechanical properties development during curing of low-k hydrogen silsesquioxane films. J. Electrochem. Soc. 149, 92002

23R.F. Cook G.M. Pharr : Direct observation and analysis of indentation cracking in glasses and ceramics. J. Am. Ceram. Soc. 73, 7871990

24A.A. Volinsky W.W. Gerberich : Nanoindentaion techniques for assessing mechanical reliability at the nanoscale. Microelectron. Eng. 69, 5192003

25X. Huang A.A. Pelegri : Nanoindentation measurements on low-k porous silica thin films spin coated on silicon substrates. J. Eng. Mater.-T. ASME 125, 3612003

26L. Shen K. Zeng : Comparison of mechanical properties of porous and non-porous low-k dielectric films. Microelectron. Eng. 71, 2212004

28E.H. Yoffe : The elastic compliance of a surface film on a substrate. Philos. Mag. Lett. 77, 691998

29M.T. Kim : Influence of substrates on the elastic reaction of films for the microindentation tests. Thin Solid Films 283, 121996

34H. Xu G.M. Pharr : An improved relation for the effective elastic compliance of a film/substrate system during indentation by a flat cylindrical punch. Scr. Mater. 55, 3152006

Recommend this journal

Email your librarian or administrator to recommend adding this journal to your organisation's collection.

Journal of Materials Research
  • ISSN: 0884-2914
  • EISSN: 2044-5326
  • URL: /core/journals/journal-of-materials-research
Please enter your name
Please enter a valid email address
Who would you like to send this to? *