Effect of nanohydroxyapatite, antibiotic, and mucosal defensive agent on the mechanical and thermal properties of glass ionomer cements for special needs patients

  • Manila Chieruzzi (a1), Stefano Pagano (a2), Guido Lombardo (a2), Lorella Marinucci (a3), José M. Kenny (a1), Luigi Torre (a1) and Stefano Cianetti (a2)...
Abstract

Special needs patients often require specific dental treatments and modified restorative materials that reduce clinical discomfort. Starting from glass ionomer cements (GICs), some different fillers were added to improve their mechanical and clinical performances. The effect of nanohydroxyapatite, antibiotic, and mucosal defensive agent on the mechanical and thermal properties of GICs was investigated. Compressive tests, calorimetric analysis, and morphological investigation were conducted. The middle percentages of fillers increased the elastic modulus while the highest decreases are recorded for highest percentages. Filler and environment also influence the compressive strengths and toughness. The introduction of fillers led to a reduction of the enthalpy with a maximum decrease with the middle percentage. The morphological characterization showed a good dispersion of the fillers. The filler percentages should be selected with a compromise between the elastic modulus, the compressive strength, and the curing time. Obtaining new materials with good clinical and mechanical properties can represent an innovative aspect of this work with positive implication in clinical practice, mainly in uncollaborative patients in which the use of traditional protocols is problematic.

Copyright
Corresponding author
a) Address all correspondence to this author. e-mail: stefano.pagano@unipg.it
Footnotes
Hide All

Contributing Editor: Jinju Chen

Footnotes
References
Hide All
1. Deepalakshmi, M., Poorni, S., Migliani, R., Rajamani, R., and Ramachandran, S.: Evaluation of the antibacterial and physical properties of glass ionomer cements containing chlorhexidine and cetrimide: An in vitro study. Indian J. Dent. Res. 21, 552 (2010).
2. Frencken, J. and van Amerongen, W.: The Atraumatic Restorative Treatment Approach, Dental Caries: The Disease and its Clinical Management (Blackwell Munksgaard, Oxford, 2008); p. 427.
3. Chieruzzi, M., Pagano, S., Moretti, S., Pinna, R., Milia, E., Torre, L., and Eramo, S.: Nanomaterials for tissue engineering in dentistry. Nanomaterials 6, 134 (2016).
4. Lucas, M.E., Arita, K., and Nishino, M.: Toughness, bonding and fluoride-release properties of hydroxyapatite-added glass ionomer cement. Biomaterials 24, 3787 (2003).
5. Weng, Y., Guo, X., Chong, V., Howard, L., Gregory, R., and Xie, D.: Synthesis and evaluation of a novel antibacterial dental resin composite with quaternary ammonium salts. J. Biomed. Sci. Eng. 4, 147 (2011).
6. Deligeorgi, V., Wilson, N.H.F., and Mjor, I.A.: An overview of reasons for the placement and replacement of restorations. J. Dent. Res. 77, 714 (1998).
7. Marti, L., Lata, M., Ferraz-Santos, B., Azevedo, E., Giro, E., and Zuanon, A.: Addition of chlorhexidine gluconate to a glass ionomer cement as study on mechanical, physcial and antibacterial properties. Braz. Dent. J. 25, 33 (2014).
8. de Castilho, A.R.F., Duque, C., Negrini, T.D., Sacono, N.T., de Paula, A.B., Costa, C.A.D., Spolidorio, D.M.P., and Puppin-Rontani, R.M.: In vitro and in vivo investigation of the biological and mechanical behaviour of resin-modified glass-ionomer cement containing chlorhexidine. J. Dent. 41, 155 (2013).
9. Chieruzzi, M., Pagano, S., De Carolis, C., Eramo, S., and Kenny, J.M.: Scanning electron microscopy evaluation of dental root resorption associated with granuloma. Microsc. Microanal. 21, 1264 (2015).
10. Mittal, S., Soni, H., Sharma, D., Mittal, K., Pathania, V., and Sharma, S.: Comparative evaluation of the antibacterial and physical properties of conventional glass ionomer cement containing chlorhexidine and antibiotics. J. Int. Soc. Prev. Community Dent. 5, 268 (2015).
11. Goenka, S., Balu, R., and Kumar, T.S.S.: Effects of nanocrystalline calcium deficient hydroxyapatite incorporation in glass ionomer cements. J. Mech. Behav. Biomed. Mater. 7, 69 (2012).
12. Gu, Y.W., Yap, A.U.J., Cheang, P., and Khor, K.A.: Effects of incorporation of HA/ZrO2 into glass ionomer cement (GIC). Biomaterials 26, 713 (2005).
13. Garcia-Contreras, R., Scougall-Vilchis, R.J., Contreras-Bulnes, R., Sakagami, H., Morales-Luckie, R.A., and Nakajima, H.: Mechanical, antibacterial and bond strength properties of nano-titanium-enriched glass ionomer cement. J. Appl. Oral Sci. 23, 321 (2015).
14. Nicholson, J.W., Hawkins, S.J., and Smith, J.E.: The incorporation of hydroxyapatite into glass-polyalkenoate (glass-ionomer) cements—A preliminary-study. J. Mater. Sci.: Mater. Med. 4, 418 (1993).
15. Yap, A.U.J., Pek, Y.S., Kumar, R.A., Cheang, P., and Khor, K.A.: Experimental studies on a new bioactive material: HA ionomer cements. Biomaterials 23, 955 (2002).
16. Arita, K., Lucas, M.E., and Nishino, M.: The effect of adding hydroxyapatite on the flexural strength of glass ionomer cement. Dent. Mater. J. 22, 126 (2003).
17. Chae, M.H., Lee, Y.K., Kim, K.N., Lee, J.H., Choi, B.J., Choi, H.J., and Park, K.T.: The effect of hydroxyapatite on bonding strength in light curing glass ionomer dental cement Key Engin. Mater. 309–311, 881884 (2006).
18. Moshaverinia, A., Ansari, S., Moshaverinia, M., Roohpour, N., Darr, J.A., and Rehman, I.U.: Effects of incorporation of hydroxyapatite and fluoroapatite nanobioceramics into conventional glass ionomer cements (GIC). Acta Biomater. 4, 432 (2008).
19. Moshaverinia, A., Ansari, S., Movasaghi, Z., Billington, R.W., Darr, J.A., and Rehman, I.U.: Modification of conventional glass-ionomer cements with N-vinylpyrrolidone containing polyacids, nano-hydroxy and fluoroapatite to improve mechanical properties. Dent. Mater. 24, 1381 (2008).
20. Mu, Y., Zang, G., Sun, H., and Wang, C.: Effect of nano-hydroxyapatite to glass ionomer cement. Hua xi kou qiang yi xue za zhi 25, 544 (2007).
21. Takahashi, Y., Imazato, S., Kaneshiro, A.V., Ebisu, S., Frencken, J.E., and Tay, F.R.: Antibacterial effects and physical properties of glass-ionomer cements containing chlorhexidine for the ART approach. Dent. Mater. 22, 647 (2006).
22. Sanders, B.J., Gregory, R.L., Moore, K., and Avery, D.R.: Antibacterial and physical properties of resin modified glass-ionomers combined with chlorhexidine. J. Oral Rehabil. 29, 553 (2002).
23. Yesilyurt, C., Er, K., Tasdemir, T., Buruk, K., and Celik, D.: Antibacterial activity and physical properties of glass-ionomer cements containing antibiotics. Oper. Dent. 34, 18 (2009).
24. Pinheiro, S.L., Simionato, M.R.L., Imparato, J.C.P., and Oda, M.: Antibacterial activity of glass-ionomer cement containing antibiotics on caries lesion microorganisms. Am. J. Dent. 18, 261 (2005).
25. Ferreira, J., Pinheiro, S., Sampaio, F., and Menezes, V.: Use of glass ionomer cement containing antibiotics to seal off infected dentin: A randomized clinical trial. Braz. Dent. J. 24, 68 (2013).
26. Katayama, S., Nishizawa, K., Hirano, M., Yamamura, S., and Momose, Y.: Effect of polaprezinc on heating of acetic acid-induced stomatitis in hamsters. J. Pharm. Pharmaceut. Sci. 3, 113 (2000).
27. Farrugia, C. and Camilleri, J.: Antimicrobial properties of conventional restorative filling materials and advances in antimicrobial properties of composite resins and glass ionomer cements—A literature review. Dent. Mater. 31, E89 (2015).
28. Botelho, M.G.: Inhibitory effects on selected oral bacteria of antibacterial agents incorporated in a glass ionomer cement. Caries Res. 37, 108 (2003).
29. Mueller, H.J., Bapna, M.S., and Fan, P.L.: Heats of reactions between dentin bonding agents and tooth components. J. Oral Rehabil. 21, 699 (1994).
30. Bjorndal, L. and Larsen, T.: Changes in the cultivable flora in deep carious lesions following a stepwise excavation procedure. Caries Res. 34, 502 (2000).
31. Duque, C., Negrini, T.D., Sacono, N.T., Spolidorio, D.M.P., Costa, C.A.D., and Hebling, J.: Clinical and microbiological performance of resin-modified glass-ionomer liners after incomplete dentine caries removal. Clin. Oral Invest. 13, 465 (2009).
32. Pinto, A.S., de Araujo, F.B., Franzon, R., Figueiredo, M.C., Henz, S., Garcia-Godoy, F., and Maltz, M.: Clinical and microbiological effect of calcium hydroxide protection in indirect pulp capping in primary teeth. Am. J. Dent. 19, 382 (2006).
33. Poggio, C., Arciola, C.R., Cepurnykh, S., Chiesa, M., Scribante, A., Selan, L., Imbriani, M., and Visai, L.: In vitro antibacterial activity of different self-etch adhesives. Int. J. Artif. Organs 35, 487 (2012).
34. Imazato, S., Kuramoto, A., Takahashi, Y., Ebisu, S., and Peters, M.C.: In vitro antibacterial effects of the dentin primer of Clearfil Protect Bond. Dent. Mater. 22, 527 (2006).
35. Beyth, N., Yudovin-Farber, I., Bahir, R., Domb, A.J., and Weissa, E.: Antibacterial activity of dental composites containing quaternary ammonium polyethylenimine nanoparticles against streptococcus mutans. Biomaterials 27, 3995 (2006).
36. Melo, M.A.S., Guedes, S.F.F., Xu, H.H.K., and Rodrigues, L.K.A.: Nanotechnology-based restorative materials for dental caries management. Trends Biotechnol. 31, 459 (2013).
37. Choudhary, K. and Nandhal, B.: Comparative evaluation of shear bond strength of nano-hydroxyapatite incorporated glass ionomer cement and conventional glass ionomer cement on dense synthetic hydroxyapatite disk: An in vitro study. Indian J. Dent. Res. 26, 170 (2015).
Recommend this journal

Email your librarian or administrator to recommend adding this journal to your organisation's collection.

Journal of Materials Research
  • ISSN: 0884-2914
  • EISSN: 2044-5326
  • URL: /core/journals/journal-of-materials-research
Please enter your name
Please enter a valid email address
Who would you like to send this to? *
×

Keywords

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 0 *
Loading metrics...

Abstract views

Total abstract views: 0 *
Loading metrics...

* Views captured on Cambridge Core between <date>. This data will be updated every 24 hours.

Usage data cannot currently be displayed