Quantitative Electron Microscopy of Cellulose Nanofibril Structures from Eucalyptus and Pinus radiata Kraft Pulp Fibers

  • Gary Chinga-Carrasco (a1), Yingda Yu (a2) and Ola Diserud (a3)
Abstract
Abstract

This work comprises the structural characterization of Eucalyptus and Pinus radiata pulp fibers and their corresponding fibrillated materials, based on quantitative electron microscopy techniques. Compared to hardwood fibers, the softwood fibers have a relatively open structure of the fiber wall outer layers. The fibrillation of the fibers was performed mechanically and chemi-mechanically. In the chemi-mechanical process, the pulp fibers were subjected to a TEMPO-mediated oxidation to facilitate the homogenization. Films were made of the fibrillated materials to evaluate some structural properties. The thicknesses and roughnesses of the films were evaluated with standardized methods and with scanning electron microscopy (SEM), in backscattered electron imaging mode. Field-emission SEM (FE-SEM) and transmission electron microscopy (TEM) were performed to quantify the nanofibril morphology. In this study, we give additional and significant evidences about the suitability of electron microscopy techniques for quantification of nanofibril structures. In addition, we conclude that standard methods are not suitable for estimating the thickness of films having relatively rough surfaces. The results revealed significant differences with respect to the morphology of the fibrillated material. The differences are due to the starting raw material and to the procedure applied for the fibrillation.

Copyright
Corresponding author
Corresponding author. E-mail: gary.chinga.carrasco@pfi.no
Linked references
Hide All

This list contains references from the content that can be linked to their source. For a full set of references and notes please see the PDF or HTML where available.

K. Abe , S. Iwamoto & H. Yano (2007). Obtaining cellulose nanofibers with a uniform width of 15 nm from wood. Biomacromolecules 8, 32763278.

S. Ahola , J. Salmi , L.-S. Johansson , J. Laine & M. Österberg (2008). Model films from native cellulose nanofibrils. Preparation, swelling, and surface interactions. Biomacromolecules 9, 12731282.

G. Chinga , P.O. Johnsen , R. Dougherty , E. Lunden-Berli & J. Walter (2007a). Quantification of the 3D microstructure of SC surfaces. J Microsc 227(3), 254265.

G. Chinga , O. Solheim & K. Mörseburg (2007b). Cross-sectional dimensions of fiber and pore networks based on Euclidean distance maps. Nordic Pulp Paper Res J 22(4), 500507.

G. Chinga-Carrasco , P.O. Johnsen & K. Øyaas (2010). Structural quantification of wood fibre surfaces—Morphological effects of pulping and enzymatic treatment. Micron 41(6), 648659.

G. Chinga-Carrasco & K. Syverud (2010). Computer-assisted quantification of the multi-scale structure of films made of nanofibrillated cellulose. J Nanoparticle Res 12(3), 841851.

R.F. Egerton , P. Li & M. Malac (2004). Radiation damage in the TEM and SEM. Micron 35(6), 399409.

Ø. Eriksen , K. Syverud & Ø. Gregersen (2008). The use of microfibrillated cellulose produced from kraft pulp as a strength enhancer in TMP paper. Nord Pulp Paper Res J 23(3), 299304.

A. Frey-Wyssling (1954). The fine structure of cellulose microfibrils. Science 119, 8082.

H. Fukuzumi , T. Saito , T. Iwata , Y. Kumamoto & A. Isogai (2009). Transparent and high gas barrier films of cellulose nanofibers prepared by TEMPO-mediated oxidation. Biomacromolecules 10, 162165.

A.N. Heyn (1969). The elementary fibril and supermolecular structure of cellulose in soft wood fiber. J Ultrastructure Res 26, 5268.

H. Meier (1962). Chemical and morphological aspects of the fine structure of wood. Pure Appl Chem 5, 3752.

M. Pääkkö , M. Ankefors , H. Kosonen , A. Nykänen , S. Ahola , M. Österberg , J. Ruokolainen , J. Laine , P.T. Larsson , O. Ikkala & T. Lindström (2007). Enzymatic hydrolysis combined with mechanical shearing and high-pressure homogenization for nanoscale cellulose fibrils and strong gels. Biomacromolecules 8, 19341941.

T. Saito , Y. Nishiyama , J.L. Putaux , M. Vignon & A. Isogai (2006). Homogeneous suspensions of individualized microfibrils from TEMPO-catalyzed oxidation of native cellulose. Biomacromolecules 7(6), 16871691.

M.Ö. Seydibeyoglu & K. Oksman (2008). Novel nanocomposites based on polyurethane and micro fibrillated cellulose. Comp Techn 68, 908914.

W. Stelte & A.R. Sanadi (2009). Preparation and characterization of cellulose nanofibers from two commercial hardwood and softwood pulps. Ind Eng Chem Res 48, 1121111219.

K. Syverud , G. Chinga-Carrasco , J. Toledo & P.G. Toledo (2011). A comparative study of Eucalyptus and Pinus radiata pulp fibres as raw materials for production of cellulose nanofibrils. Carbohyd Polym 84(3), 10331038.

K. Syverud & P. Stenius (2009). Strength and barrier properties of MFC films. Cellulose 16(1), 7585.

T. Tanigushi & K. Okamura (1998). New films produced from microfibrillated natural fibres. Polym Int 47, 291294.

M. Ziabari , V. Mottaghitalab , T. Scott , A.K. McGovern & A. Haghi (2007). A new image analysis based method for measuring electrospun nanofiber diameter. Nanoscale Res Lett 2, 597600.

T. Zimmermann , N. Bordeanu & E. Strub (2010). Properties of nanofibrillated cellulose from different raw materials and its reinforcement potential. Carbohyd Polym 79(4), 10861093.

Recommend this journal

Email your librarian or administrator to recommend adding this journal to your organisation's collection.

Microscopy and Microanalysis
  • ISSN: 1431-9276
  • EISSN: 1435-8115
  • URL: /core/journals/microscopy-and-microanalysis
Please enter your name
Please enter a valid email address
Who would you like to send this to? *
×

Keywords: