Microemulsion Synthesis of Iron Core/Iron Oxide Shell Magnetic Nanoparticles and Their Physicochemical Properties

Published online by Cambridge University Press:  10 May 2012

Katsiaryna Kekalo
Affiliation:
Thayer School of Engineering at Dartmouth College, Hanover, New Hampshire, USA
Katherine Koo
Affiliation:
Thayer School of Engineering at Dartmouth College, Hanover, New Hampshire, USA
Evan Zeitchick
Affiliation:
Thayer School of Engineering at Dartmouth College, Hanover, New Hampshire, USA
Ian Baker
Affiliation:
Thayer School of Engineering at Dartmouth College, Hanover, New Hampshire, USA
Get access

Abstract

Iron magnetic nanoparticles were synthesized under an inert atmosphere via the reaction between FeCl3 and NaBH4 in droplets of water in a microemulsion consisting of octane with cetyl trimethylammonium bromide and butanol as surfactants. A thin Fe3O4 layer was produced on the iron nanoparticles using slow, controlled oxidation at room temperature. A silica shell was deposited on the Fe3O4 using 3-aminopropyltrimethoxysilane following the method of Zhang et al. [Mater. Sci. Eng. C 30 (2010) 92–97]. The structure and chemistry of the resulting nanoparticles were studied using variety of methods and their magnetic properties were determined. The diameter of the iron core was typically 8-16 nm, while the thickness of the Fe3O4 shell was 2-3 nm. The presence of the silica layer was confirmed using Fourier transform infra-red spectroscopy and the number of NH2-groups on each nanoparticle was determined based on colorimetric tests using ortho-phthalaldehyde.

Type
Research Article
Copyright
Copyright © Materials Research Society 2012

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Zhang, G., Liao, Y. and Baker, I., Materials Science and Engineering C 30(1) (2010) 9297.Google Scholar
[2] Zeng, Q., Baker, I., Loudis, J.A., Liao, Y., Hoopes, P.J. and Weaver, J.B., Appl. Phys. Lett. 90(23) (2007) 233112-1 –; 233112–3.Google Scholar
[3] Hergt, R. et al. . / J Phys Condens Matter 18(38) (2006), pp. S2919S2934 Google Scholar
[4] Klabunde, K. J. and Hadjipanayis, G. C., J. Appl. Phys., 75 (1994) 58765878.Google Scholar
[5] Pileni, M. P., Ninham, B. W., Gulik-Krzywicki, T., Tanori, J., Lisiecki, I. and Filankembo, A., Adv. Mater., 11 (1999) 13581362.Google Scholar
[6] Maillard, M., Giorgio, S. and Pileni, M. P., Adv. Mater., 14 (2002) 10841086.Google Scholar
[7] Sharma, R. K., Sharma, P. and Maitra, A., J. Colloid Interface Sci., 265 (2003) 134140.Google Scholar
[8] Brust, M., Walker, M., Bethell, D., Schiffrin, D.J. and Whyman, R.. J. Chem. Soc., Chem. Commun., 7 (1994) 801802.Google Scholar
[9] O’Connor, C.J., Kolesnichenko, V., Carpenter, E., Sangregorio, C., Zhou, W.L., Kumbhar, A., Sims, J. and Agnoli, F., Synthetic Metals, 122 (2001) 547557.Google Scholar
[10] Pham, T.A., Kumar, N.A. and Jeong, Y.T., Colloids and Surfaces A: Physicochem. Eng. Aspects 370 (2010) 95101.Google Scholar
[11] Seip, C. T. and O’Connor, C. J., NanoStructured Materials, 12 (1999) 183-1 86.Google Scholar
[12] Hoinard, C. et al. ., Spectrofluorometric method for the quantitation of amino groups on solid supports. Journal of Chromatography A, 1986. 355: p. 350353.Google Scholar
[13] Janolino, V. and Swaisgood, H., A spectrophotometric assay for solid phase primary amino groups. Applied Biochemistry and Biotechnology, 1992. 36(2): p. 8185.Google Scholar