In this research, we describe the electrospinning processing of polylactic acid (PLA) and the influence of silver nanoparticles on the morphology and microstructure of produced non woven membranes thus produced. The PLA was electrospun from a chloroform solution and a filamentary and granular morphology was obtained, the filaments having an average diameter of 1.25 μm, When silver nanoparticles (of ca. 12 nm size) were incorporated, the filaments diameter was reduced to an average of 0.65 μm, and the density of beads was also reduced. The membranes were rather amorphous, as revealed by X-ray scattering, presumably due to the quenching process associated with the electrospinning process. Water contact angle measurements showed that silver nanoparticles induced significant hidrophobicity in the membranes as neat PLA membrane had a contact angle of 54° and PLA/Ag membrane exhibited an angle of 115°.
Email your librarian or administrator to recommend adding this journal to your organisation's collection.
Full text views
* Views captured on Cambridge Core between September 2016 - 25th March 2017. This data will be updated every 24 hours.