Photoluminescence of Surface Modified Silicon Carbide Nanowires

  • Polite D. Stewart (a1) (a2), Ryan Rich (a1), A. Nemashkalo (a1) and T. W. Zerda (a1)
Abstract
ABSTRACT

SiC nanowires were produced from carbon nanotubes and nanosize silicon powder in a tube furnace at temperatures between 1100°C and 1350°C. SiC nanowires had average diameter of 30 nm and very narrow size distribution. The surface of the SiC nanowires is covered by an amorphous layer composed of amorphous SiC and various carbon and silicon compounds. The objective of the research was to modify the surface structure of the SiC nanowires, a step necessary for future surface functionalization. The acid etched nanowires were analyzed using FTIR, TEM, x-ray diffraction, and photoluminescence. The concentration of Si-Ox groups in untreated specimens was estimated to account for 1% of the total mass of a 2 nm thick amorphous layer wrapping around all structures. After treatment in HF this concentration was negligibly small. TEM images show that after treatment the amorphous layer was removed but the diameter of the core remained unchanged. The surface was roughened and multiple pits formed on that surface. X-ray line broadening analysis indicates a significant contribution due to stress caused by dislocations and planar faults. After acid etching line narrowing was observed and attributed to stress reduction and elimination of the smallest wires. The photoluminescence signal from as received samples was very weak but increased greatly after acid treatment, indicating that the signal is related to surface defects. Measurements at low temperatures, 8 K, showed peaks due to point and planar defects.

Copyright
Linked references
Hide All

This list contains references from the content that can be linked to their source. For a full set of references and notes please see the PDF or HTML where available.

1.Y. Cui and C.M. Lieber , Science, 291, 851 (2001).

2.H. K. Seong , H. J. Choi , S. K. Lee , J. I. Lee , D. J. Choi , Appl. Phys. Lett. 85, 1256 (2004).

4.Y. Zhao , J. Qian , L. L. Daemen , C. Pantea , J. Zhang , G.A. Voronin , T.W. Zerda , Appl. Phys. Lett. 84, 1356 (2004).

5.W. Yang , H. Araki , C. C. Tang , S. Thaveethavorn , A. Kohyama , H. Suzuki , T. Noda , Adv. Mater. 17, 1519 (2005).

12.H.W. Shim , K.C. Kim , Y.H. Seo , K.S. Nahm , E.K. Suh , H.J. Lee , Y.G. Hwang , Appl. Phys. Lett. 70, 1757 (1997)

13.J.Y. Fan , X.L. Wu , F. Kong , T. Qiu , S. Huang , Appl. Phys. Lett. 86, 171903 (2005)

Recommend this journal

Email your librarian or administrator to recommend adding this journal to your organisation's collection.

MRS Online Proceedings Library (OPL)
  • ISSN: -
  • EISSN: 1946-4274
  • URL: /core/journals/mrs-online-proceedings-library-archive
Please enter your name
Please enter a valid email address
Who would you like to send this to? *
×

Keywords: