Electrical and Structural Properties of Grain Boundary in Polycrystalline Si*

Published online by Cambridge University Press:  15 February 2011

R. T. Young ,
J. Narayan  and
Y. K. Chang
R. T. Young
Affiliation:
Solid State Division, Oak Ridge National Laboratory, Oak Ridge, TN 37830
J. Narayan
Affiliation:
Solid State Division, Oak Ridge National Laboratory, Oak Ridge, TN 37830
Y. K. Chang
Affiliation:
Solid State Division, Oak Ridge National Laboratory, Oak Ridge, TN 37830
Get access

Abstract

A special type of high angle grain boundary with mirror symmetry of the crystallographic orientation between the two grains is examined electrically and structurally. Transmission electron microscopy investigations show the nonuniform nature of the grain boundary. Both coherent and incoherent regions are observed along the boundary plane, and the types of dislocations and their densities vary from place to place. Electrical measurements of the boundary properties indicate no measurable barrier height. Heat treatment of the sample in an oxygen atmosphere at 950°C for 30 min did not change the boundary resistance. However, recombination effects are enhanced after boron diffusion. When pulsed laser radiation was used to process this material, it was found that the grain boundary structures were modified by laser-induced surface melting, i.e., incoherent boundaries were converted to coherent boundaries in the melted region.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 5: Symposium B – Grain Boundaries in Semiconductors , 1981 , 111
Copyright
Copyright © Materials Research Society 1982

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

Footnotes

*

*Research sponsored by SERI under contract DS-0-9078-1 and by U.S. Department of Energy under contract W-7405-eng-26 with the Union Carbide Corporation.

References

REFERENCES

1. Seto, J. W. Y., J. Appl. Phys. 46, 5247 (1975).Google Scholar
2. Seager, C. H. and Castner, T. G., J. Appl. Phys. 49, 3879 (1978).Google Scholar
3. Baccurani, G., Ricco, B. and Spadini, G., J. Appl. Phys. 49, 5565 (1978).Google Scholar
4. See, for example, Haasen, P., Physical Metallurgy, (Cambridge Univ. Press, New York 1978), p. 303.Google Scholar
5. Wood, R. F., Young, R. T., Westbrook, R. D., Narayan, J., Christie, W. H. and Cleland, J. W., Solar Cells 1, 145 (1980).Google Scholar
6. Narayan, J., Bullough, R. and Willis, J. R., Proceedings of Royal Society, London (in press).Google Scholar