Evaluation of Adhesive Strength of Oxide Layer on Carbon Steel at Elevated Temperatures

Published online by Cambridge University Press:  31 January 2011

Manabu Satou
Manabu Satou*
Affiliation:
msatou@hi-tech.ac.jp, Tohoku University, Sendai, Japan
Get access

Abstract

Adhesive strength of the oxidation layers on carbon steel was evaluated by means of a laser shock method, which uses a pulsed laser to generate shock wave. Oxidation for 200 hours in air created 10-micron-thick magnetite on carbon steel. Typical strength of the layer was evaluated to be about 50MPa at ambient temperature. The adhesive strength was varied from around one-tenth of yield stress to the ultimate tensile strength of the base materials. The adhesive strength of the oxide layer depended on test temperature. It is possible that the adhesive strength becomes an essential parameter for the evaluation of the protective layers.

Keywords

adhesionlaseroxidation
Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1215: Symposium V – Materials Research Needs to Advance Nuclear Energy , 2009 , 1215-V16-22
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Kondo, M. Takahashi, M. Sawada, N. and Hata, K. Corrosion of Steels in Lead-Bismuth Flow, J.Nucl.Sci.Tech., 43, 107(2006)Google Scholar
2. Fazio, C. Benamati, G. Martini, C. Palombarini, G. Compatibility tests on steels in molten lead and lead-bismuth, J.Nucl. Mater., 296, 243(2001)Google Scholar
3. Kikuchi, Kenji, Kamata, Kinya, Ono, Mikinori, Kitano, Teruaki, Hayashi, Kenichi and Oigawa, Hiroyuki, Corrosion rate of parent and weld materials of F82H and JPCA steels under LBE flow with active oxygen control at 450 and 500 °C, J.Nucl. Mater., 377, 232(2008)Google Scholar
4. Gupta, V. Argon, A.S. Cornie, J.A. Parks, D.M. Measurement of interface strength by laser spallation technique, J. Mech. Phys. Solids 40, 141(1992)Google Scholar
5. Satou, M. Sato, T. Hasegawa, A. , Role of Oxide Layer on Wall Thinning Caused by Liquid Droplet Impingement, Proc. of PVP2009, ASME Pressure Vessels and Piping Division Conference (July 26-30, 2009 Prague, Czech Republic) PVP2009-77685.Google Scholar
6. Akamatsu, H. Satou, M. Sato, T. Jain, A. Gupta, V. Hasegawa, A. Evaluation of bonding strength between yttria and vanadium alloys for development of self-cooled liquid blanket, Proc. of ICFRM14, Int. Conf. Fusion Reactor Materials (Sept. 7-12, 2009, Sapporo, Japan)Google Scholar