Growth kinetics changes of vertically aligned carbon nanostructures synthesised at low substrate temperatures

Published online by Cambridge University Press:  01 February 2011

G. Y. Chen
Affiliation:
Nano-Electronic Centre, Advanced Technology Institute, School of Electronics and Physical Science, University of Surrey, Guildford, Surrey, GU2 7XH., United Kingdom
C. H. P. Poa
Affiliation:
Nano-Electronic Centre, Advanced Technology Institute, School of Electronics and Physical Science, University of Surrey, Guildford, Surrey, GU2 7XH., United Kingdom
V. Stolojan
Affiliation:
Nano-Electronic Centre, Advanced Technology Institute, School of Electronics and Physical Science, University of Surrey, Guildford, Surrey, GU2 7XH., United Kingdom
S. Henley
Affiliation:
Nano-Electronic Centre, Advanced Technology Institute, School of Electronics and Physical Science, University of Surrey, Guildford, Surrey, GU2 7XH., United Kingdom
S. R. P. Silva
Affiliation:
Nano-Electronic Centre, Advanced Technology Institute, School of Electronics and Physical Science, University of Surrey, Guildford, Surrey, GU2 7XH., United Kingdom
Get access

Abstract

Carbon nanotubes and nanofibres are typically synthesised under substrate temperatures above 600°C. Here we investigate the influence of the substrate temperature and the plasma conditions on the growth of vertically aligned carbon nanostructures using Direct Current plasma Chemical Vapour Deposition, at temperatures below 550°C. These nanostructures are produced using a C2H2 based plasma and nickel thin film as the catalyst. We found that preferential deposition of amorphous carbon takes place as the synthesis temperature is lowered below 500°C. However, lowering the carbon concentration in the gas feedstock (<2% conc.) allows for the nucleation of nanofibre-like structures, whilst balancing the buildup of amorphous carbon. This method allows for the synthesis of vertically aligned structures at low temperatures (around 230°C) without intentional heating, while still achieving reasonable average growth rates up to 27 nm/min. The only heating was provided by the plasma, which typically consumes ∼ 4 W/cm2. It was found that by varying the applied plasma bias during high temperature synthesis, we increased the growth rate up to 165 nm/min. Based on the observations of experimental process variations and the morphology of the synthesised structures, we propose a growth mechanism for such low temperature growth and examine the resulting morphology changes.

Type
Research Article
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Khan, R.U.A., Silva, S.R.P. and Swaaij, R.A.C.M.M., Appl. Phys. Lett. 82, 3979 (2003)Google Scholar
2. Li, Y.J., Lau, S.P., Tay, B.K., Sun, Z., Chen, G.Y., Chen, J.S., Ding, X.Z. and Shi, X., Appl. Phys. Lett. 77, 2021 (2000)Google Scholar
3. Veerasamy, V.S., Luten, H.A., Petrmichi, R. H. and Thomsen, S.V., Thin Solid Films 442, 1 (2003)Google Scholar
4. Endo, M., Nishimura, Y., Takahashi, T., Takeuchi, K. and Dreselhaus, M.S., J. Phys. Chem Solids 57, 725 (1996)Google Scholar
5. Kiema, G.K. and Brett, M. J., J. Electrochem Soc. 150, E342 (2003)Google Scholar
6. Bokros, J.C., Carbon 15, 353 (1977)Google Scholar
7. Sohn, J.I., Lee, S., Song, Y.H., Choi, S.Y., Cho, K.I. and Nam, K.S., Appl. Phys. Lett. 78, 901, (2001)Google Scholar
8. Li, Y.J., Sun, Z., Lau, S.P., Chen, G.Y. and Tay, B.K., Appl. Phys. Lett. 79, 1670 (2001)Google Scholar
9. Prioli, R., Chhowalla, M. and Freire, F. L., Diamond and Related Materials 12, 2195, (2003)Google Scholar
10. Baker, R.T.L. and Barber, M.A., in Chemistry and Physics of Carbon, Vol. 14 edited by Walker, P.L. and Thrower, P.A. (Dekker, New York, 1978), pg 83 Google Scholar
11. Teo, K.B.K., Hash, D.B., Lacerda, R.G., Rupesinghe, N.L., Bell, M.S., Dalal, S.H., Bose, D., Govindan, T.R., Cruden, B.A., Chhowalla, M., Amaratunga, G.A.J., Myyappan, M. and Milne, W.I., Nano Lett. Vol 4, 921 (2004)Google Scholar
12. Kuang, M.H., Wang, Z.L., Bai, X.D., Guo, J.D., Wang, E.G., Appl. Phys. Lett. 76, 1255 (2000)Google Scholar