Micr owave Dielectric Properties of (1-x)CaTiO3-xNd(Mg1/2Ti1/2)O3 Ceramics System

  • Cheng-Liang Huang (a1), Yuan-Bin Chen (a1) and Ching-Wen Lo (a1)
Abstract
ABSTRACT

The microwave dielectric properties of (1-x)CaTiO3-xNd(Mg1/2Ti1/2)O3 (0.1≤x≤1.0) have been investigated. The system forms a solid solution throughout the entire compositional range. The dielectric constant decreases from 152 to 27 as x varies from 0.1 to 1.0. In the (1-x)CaTiO3-xNd(Mg1/2Ti1/2)O3 system, the microwave dielectric properties can be effectively controlled by varying the x value. A maximum quality factor Qxf=43000GHz (where f is the resonant frequency) was achieved for samples with x=0.9, although the dielectric properties varied with sintering temperature. The Qxf value of (1-x)CaTiO3-xNd(Mg1/2Ti1/2)O3 almost increased up to 1500°C, after which it decreased. At 1400°C, 0.1CaTiO3-0.9Nd(Mg1/2Ti1/2)O3 ceramics gives a dielectric constant εr of 42, a Qxf value of 35000 (GHz) and a τf value of -10 (ppm/°C).

Copyright
References
Hide All
1. Solomon S., Sreemoolanadhan H., Sebastian M.T., Mohanan P., Mater. Lett. 28 (1996) 107.
2. Takata M., Kagayeman K., J. Am. Ceram. Soc. 72(1989) 1995.
3. Sreemoolanadhan H., Ratheesh R., Sebastian M.T., Mohanan P., Mater. Lett. 33 (1997) 161.
4. Kajfez D., Guillon P., Dielectric Resonators, Artech House, Massachusettls, 1986.
5. Harshe G., Bhalla A.S., Cross L.E., Mater. Lett 18 (1994)
6. Cho S.Y., Seo M.K., Hong K.S., Park S.J., I.T. kim. Mater. Res. Bull. 32(1997) 725.
7. Cho S.Y., Kim C.H., Hong K.S., Kim J.H., J. Mater. Res 14 (1999) 2484.
Recommend this journal

Email your librarian or administrator to recommend adding this journal to your organisation's collection.

MRS Online Proceedings Library (OPL)
  • ISSN: -
  • EISSN: 1946-4274
  • URL: /core/journals/mrs-online-proceedings-library-archive
Please enter your name
Please enter a valid email address
Who would you like to send this to? *
×

Metrics

Full text views

Total number of HTML views: 0
Total number of PDF views: 3 *
Loading metrics...

Abstract views

Total abstract views: 19 *
Loading metrics...

* Views captured on Cambridge Core between September 2016 - 13th December 2017. This data will be updated every 24 hours.