Photocatalytic Activity of Anatase Fiber-Mats

Published online by Cambridge University Press:  30 July 2012

Annelise K. Alves ,
Felipe A. Berutti  and
Carlos P. Bergmann
Annelise K. Alves
Affiliation:
Federal University of Rio Grande do Sul, Av. Osvaldo Aranha, 99 sl. 705C, Porto Alegre, RS, 90035190, Brazil
Felipe A. Berutti
Affiliation:
Federal University of Rio Grande do Sul, Av. Osvaldo Aranha, 99 sl. 705C, Porto Alegre, RS, 90035190, Brazil
Carlos P. Bergmann
Affiliation:
Federal University of Rio Grande do Sul, Av. Osvaldo Aranha, 99 sl. 705C, Porto Alegre, RS, 90035190, Brazil
Get access

Abstract

Nanostructured fiber-mats have large surface area, high reactivity, low weight and low agglomeration tendency. These are advantages if compared with nanoparticles for photocatalytic application. Fiber-mats can be used not only as a photocatalytic material on their own, but also incorporated in different surfaces or fabrics and as well as a filtration membrane. In this work, high temperature stable anatase titanium dioxide fiber-mats doped with silica (0.5 to 30 %) or doped with tin (0.5 to 15 %) were produced by electrospinning technology. The precursors used were titanium propoxide (TiP), tetrapropoxysilane (TPS) and tin 2-ethylhexanoate. They were hydrolyzed in acetic acid and mixed with an alcoholic solution of 10 wt% polyvinylpirrolidone. The effect of heat treatment on the microstructure characteristics and the photocatalytic activity of the fiber-mats in comparison with a commercial TiO2 powder (Evonik P-25) were studied. After the electrospinning process, a thin, porous fiber-mat was obtained. This material was dried in air at room temperature for 24h. These fibers were then heat treated from 500 to 800°C for 3 hours at a heating rate of 1.4°C/min. The fiber-mats were then characterized using N2 adsorption (BET method) for surface area measurements, X-ray diffraction for phase determination, SEM and TEM analyses for morphological characterization. The photocatalytic activity was studied using as model system the degradation of methyl orange in water (20ppm) under UV-A light. As-obtained fibers are amorphous but become crystalline after heat treatment. As the heat treatment temperature increases the surface area decreases significantly. Quite the opposite happens with the rutile to anatase ratio and the anatase and rutile crystallite sizes, which increase with higher heat treatment temperatures. The photoactivity increases with the increment in heat treatment temperature until 650°C, when the fibers start to become denser and the surface area drops due to sintering. Fibers produced at higher temperatures and with lower amounts of Si and Sn are predominantly anatase and are generally more photoactive under UV-A radiation.

Keywords

fibercatalyticphotochemical
Type
Articles
Information
MRS Online Proceedings Library (OPL) , Volume 1442: Symposium Q – Titanium Dioxide Nanomaterials--2012 , 2012 , mrss12-1442-q03-01
Copyright
Copyright © Materials Research Society 2012

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

[1] Bai, J.; Li, Y.; Li, M.;Wang, S.; Zhang, C.; Yang, Q. Electrospinning method for the preparation of silver chloride nanoparticles in PVP nanofiber. Appl. Surf. Sci. 2008, 254: 4520–4523.Google Scholar
[2] McCann, J. T.; Lim, B.; Ostermann, R.;Rycenga, M.;Marquez, M.; Xia, Y. Carbon Nanotubes by electrospinning with a polyelectrolyte and vapor deposition polymerization. Nano Lett. 2007, 7: 2470–2474.Google Scholar
[3] Riyas, S.;Krishnan, G.;Mohan, P.N. Anatase-rutile transformation in doped titania under argon and hydrogen atmospheres. Adv.Appl. Ceram. 2007, 106: 255–264.Google Scholar
[4] Egerton, T. A.; Mattinson, J.A., The influence of platinum on UV and ‘visible’ photocatalysis by rutile and Degussa P25. Journal of Photochemistry and Photobiology A: Chemistry, 2008, 194, 283–289.Google Scholar
[5] Yang, J.; Bai, H.; Jiang, Q.; Lian, J. Visible-light photocatalysis in nitrogen–carbon-doped TiO2 films obtained by heating TiO2 gel–film in an ionized N2 gas. Thin Solid Films, 2008, 516: 1736–1742.Google Scholar
[6] Sun, H.; Wang, S.; Ang, H.M.; Tadé, M.O.; Li, Q. Halogen element modified titanium dioxide for visible light photocatalysis. Chemical Engineering Journal, 2010, 162: 437–447.Google Scholar
[7] Boppana, V.B.R.; Lobo, R.F. Photocatalytic degradation of organic molecules on mesoporous visible-light-active Sn(II)-doped titania. Journal of Catalysis, 281: 156 – 168.Google Scholar
[8] Alves, A.K.; Berutti, F.A.; Clemens, F.; Graule, T.; Bergmann, C.P. Photocatalytic activity of electrospun titania fibers obtained by electrospinning. Mater. Res. Bull. 2009, 44, 312–317.Google Scholar
[9] Hassan, M. S.; Amna, T.; Yang, O-B.; Kim, H.C.; Khil, M.S. TiO2 nanofibers doped with rare earth elements and their photocatalytic activity. Ceramics International, 2012, 38, 5925–5930.Google Scholar
[10] Zhang, Y.; Li, G.; Wu, Y.; Luo, Y.; Zhang, L. The formation of mesoporous TiO2 spheres via a facile chemical process. Journal of Physical Chemistry B, 2005, 109, 5478–5481.Google Scholar