Preparation and Cracterization of Alu1Inur Titanate Plabra Spray Powder

Published online by Cambridge University Press:  25 February 2011

L. J. Shyu ,
V. T. Brice ,
F. M. Cambria ,
B. M. Su ,
C. Tirendi  and
J. Wandass
L. J. Shyu
Affiliation:
Akzo Chemicals Inc., 1 Livingstone Ave., Dobbs Ferry, NY. 10522
V. T. Brice
Affiliation:
Akzo Chemicals Inc., 1 Livingstone Ave., Dobbs Ferry, NY. 10522
F. M. Cambria
Affiliation:
Akzo Chemicals Inc., 1 Livingstone Ave., Dobbs Ferry, NY. 10522
B. M. Su
Affiliation:
Akzo Chemicals Inc., 1 Livingstone Ave., Dobbs Ferry, NY. 10522
C. Tirendi
Affiliation:
Akzo Chemicals Inc., 1 Livingstone Ave., Dobbs Ferry, NY. 10522
J. Wandass
Affiliation:
Akzo Chemicals Inc., 1 Livingstone Ave., Dobbs Ferry, NY. 10522
Get access

Abstract

Aluminum titanate ceramic powder, used in plasma spray coating as a wear resistant material, was prepared from a gel precursor followed by high temperature calcination. The chemically derived gel was made from aluminum sulfate and titanium isopropoxide in an oxalic acid aqueous system. The soluble complex was studied by 13C NMR spectroscopy which showed that the mole ratio of oxalic acid bound to Al and Ti was 2:1. A coprecipitation took place when ammonium hydroxide was added. The gel was examined by solid-state NMR spectroscopy which suggested that aluminum titanium hydroxyl oxalate was present with Al in a distorted octahedral environment. EDX mapping showed that Al and Ti were evenly distributed throughout the gel particles. Thermal analysis indicated that dehydration and combustion of organic groups took place between 100 and 400 ° C. Gel which was heat treated at 1500 °C was identified as a pure AI2TiO5 crystalline phase by XRD.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 249: Symposium Q – Synthesis and Processing of Ceramics: Scientific Issues , 1991 , 115
Copyright
Copyright © Materials Research Society 1992

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Kato, E., Daimon, K. and Takahasi, J., 63[5-6], 355–356 (1980).CrossRefGoogle Scholar
2. Ishitsuka, M., Sato, T., Endo, T. and Shimada, M., J. Am. Ceram. Soc., 70[2], 69–71 (1987).CrossRefGoogle Scholar
3. Kladnig, W.F. and Mayer, H., J. Mat. Sci.,25, 1973–1977 (1990).Google Scholar
4. Woignier, T., Lespade, P., Phalippou, J. and Rogier, R., J. of Non-Crystalline Solids, 100, 325–329 (1988).Google Scholar
5. Brugger, P. A. and Mocellin, A., J. Mat. Sci. 21, 4431–4435, (1986).Google Scholar
6. Yamaguchi, O. and Mukaida, Y., J. Am. Ceram. Soc., 72[2[, 330–333 (1989).Google Scholar
7. Mani, T. V., Varma, H. K., Warrier, K. G. and Damodaran, A. D., J. Am. Ceram. Soc., 74[8], 1807–1810 (1991).Google Scholar
8. Fay, R. C. and Lowry, R. N., Inorg. Chem. 6(8), 1512–1519 (1967).Google Scholar
9. Shyu, L. J. and Cambria, F. M., Mat. Res. Soc. Symp. Proc. 180, 837–841 (1990).Google Scholar
10. Jaber, M., Bertin, F. and Thomas-David, G., Can. J. Chem. 55, 3689, (1977).CrossRefGoogle Scholar