Reactive Sputter Deposition of Superhard Polycrystalline Nanolayered Coatings

Published online by Cambridge University Press:  10 February 2011

William D. Sproul
William D. Sproul*
Affiliation:
BIRL, Northwestern University, 1801 Maple Avenue, Evanston, IL 60201USAwsproul@nwu.edu
Get access

Abstract

Nanometer-scale multilayer nitride coatings, also known as polycrystalline nitride superlattice coatings, such as TiN/NbN or TiN/VN with hardnesses exceeding 50 GPa, are deposited by highrate reactive sputtering. The high hardness is achieved by carefully controlling several deposition parameters in an opposed cathode, unbalanced magnetron sputtering system: the target power, the reactive gas partial pressure, the substrate bias voltage and current density, and the substrate rotation speed. Target power controls the deposition rate and the thickness for each layer in conjunction with the reactive gas partial pressure at each target, which also affects the composition of each layer, and the substrate rotation speed. Split partial pressure control is necessary when each layer requires a different partial pressure to be stoichiometric. Fully dense, well-adhered coatings with the highest hardness are deposited when the negative substrate bias exceeds -130 V and the substrate ion current density is 4–5 mA cm−2. The work on polycrystalline superlattice coatings is being extended into oxide systems. Oxide coatings can now be sputter deposited using pulsed dc power, which prevents arcing on both the target and the substrate. Pulsed dc power along with partial pressure control of the reactive gas leads to significantly higher deposition rates for the oxide films compared to sputtering with conventional rf power.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 434: Symposium U – Layered Materials for Structural Applications , 1996 , 47
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Helmersson, U., Todorova, S., Barnett, S. A., Sundgren, J.-E., Markert, L. C., and Greene, J. E., J. Appl. Phys. 62, 481 (1987).Google Scholar
2. Shinn, M., Hultman, L., and Barnett, S. A., J. Mater. Res. 7, 901 (1992).Google Scholar
3. Chu, X., Ph. D. thesis, Northwestern University, June 1995.Google Scholar
4. Chu, X., Wong, M. S., Sproul, W. D., Rohde, S. L., and Barnett, S. A., J. Vac. Sci. Technol. A, 10, 1604 (1992).Google Scholar
5. Chu, X., Wong, M. S., Sproul, W. D., and Barnett, S. A., Mat. Res. Soc. Proc. 226, 379 (1993).Google Scholar
6. Chu, X., Barnett, S. A., Wong, M. S., and Sproul, W. D., Surf. Coat. Technol. 57, 13 (1993).Google Scholar
7. Chu, X. and Barnett, S. A., J. Appl. Phys. 77 (8), 4403 (1995).Google Scholar
8. Sproul, W. D., ”Reactive Sputter Deposition of Polycrystalline Nitride and Oxide Superlattice Coatings,” submitted for publication in Surface and Coatings Technology.Google Scholar
9. Wong, M. S., Chia, W. J., Schneider, J. M., Yashar, P., Sproul, W. D. and Barnett, S. A., ”High- Rate Reactive DC Magnetron Sputtering of ZrOx,” submitted for publication in Surface and Coatings Technology.Google Scholar
10. Schneider, J. M., Wong, M. S., Sproul, W. D., Voevodin, A. A., Matthews, A., and Paul, J., ”Deposition and Characterization of Alumina Hard Coatings by DC Pulsed Magnetron Sputtering,” submitted for publication in Surface and Coatings Technology.Google Scholar
11. Sproul, W. D., Graham, M. E., Wong, M. S., Lopez, S., Li, D., and Scholl, R. A., J. Vac. Sci. Technol. A., 13(3) 1188 (1995).Google Scholar
12. Sproul, William D., Graham, Michael E., Wong, Ming-Show, and Rudnik, Paul J., ”Reactive DC Magnetron Sputtering of the Oxides of Ti, Zr, and Hf,” accepted for publication in Surface and Coatings Technology.Google Scholar
13. Sproul, William D., Rudnik, Paul J., Graham, Michael E., and Rohde, Suzanne L., Surface and Coatings Technology, 43/44 270 (1990).Google Scholar
14. Setoyama, M., Nakayama, A., Yoshioka, T., Nomura, T., Shibata, A., Chudou, M., and Arimoto, H., Sumitomo Electric Industries, 146 91 (1995).Google Scholar
15. Schiller, S., Goedicke, K., Reschke, J., Kirchhoff, V., Schneider, S., and Milde, F., Surf. Coat. Technol. 61, 331 (1993).Google Scholar
16. Frach, P., Heisig, U., Chr., Gottfried, and Walde, H., Surf. Coat. Technol. 59, 177 (1993).Google Scholar
17. Graham, M. E. and Sproul, W. D., 37th Annual Technical Conference Proceedings, Society of Vacuum Coaters, Albuquerque, New Mexico, p. 275 (1994).Google Scholar
18. Sellers, J., ”Asymmetric Bipolar Pulsed DC,” ENI Tech Note, ENI, Division of Astec America, Inc., 100 Highpower Road, Rochester, NY 14623.Google Scholar