Stability of Heavily Doped Si Formed by As+ Implantation and Rapid Thermal Annealing

Published online by Cambridge University Press:  26 February 2011

Muhammad Z. Numan ,
Z. H. Lu ,
W. K. Chu ,
D. Fathy  and
J. J. Wortman
Muhammad Z. Numan
Affiliation:
Department of Physics and Astronomy, University of North Carolina, Phillips Hall 039 A, Chapel Hill, NC 27514
Z. H. Lu
Affiliation:
Institute of Low Energy Nuclear Physics, Beijing Normal University, Beijing Radiation Center, China
W. K. Chu
Affiliation:
Department of Physics and Astronomy, University of North Carolina, Phillips Hall 039 A, Chapel Hill, NC 27514
D. Fathy
Affiliation:
Microelectronics Center of North Carolina, Research Triangle Park, NC 27709
J. J. Wortman
Affiliation:
Department of Electrical and Computer Engineering, North Carolina State University, Raleigh, NC 27695
Get access

Abstract

Deactivation of ion implanted and rapid thermal annealed (RTA) metastable arsenic in silicon during subsequent furnace annealing has been studied by sheet resistance measurement, Rutherford backs cat t ering/ channeling (RBS), and transmission electron microscopy (TEM). Following RTA, thermal annealing induces deactivation of the dopant which increases the sheet resistivity monotonically with temperature for a very short time, Dislocation loops are formed near the peak of As concentration at post-anneal temperatures of 750°C or higher, where deactivation rate is fast. At lower temperatures deactivation is accompanied by displacement of As atoms, possibly forming clusters.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 52: Symposium B – Rapid Thermal Processing , 1985 , 31
Copyright
Copyright © Materials Research Society 1986

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Lietoila, A., Gibbons, J.F., and Sigmon, T.W., Appl. Phys. Lett. 36, 765 (1980).CrossRefGoogle Scholar
[2] Nobili, D., Garabelas, A., Celotti, G., and Solmi, S., J. Electrochem. Soc. 130, 922 (1983).Google Scholar
[3] Yamamoto, Y., Inada, T., Sugiyna, T., and Tamura, S., J. Appl. Phys. 53, 276 (1982).Google Scholar
[4] Lietoila, A., Gold, R.B., Gibbons, J.F., Sigmon, T.W., Scovell, P.D., and Young, J.M., J. Appl. Phys. 2, 230 (1981).Google Scholar
[5] Fair, R.B., and Weber, G. R., J. Appl. Phys. 44, 273 (1973).CrossRefGoogle Scholar
[6] Tsai, M.Y., Morehead, F.F., and Baglin, J.E.E., J. Appl. Phys. 51 3230 (1980).Google Scholar
[7] Guerrero, E., Poetzl, H., Tielert, R., Grasserbauer, M., and Stingeder, G., J. Electrochem. Soc. 129, 1826 (1982).Google Scholar
[8] Fair, R.B., in: Impurity Doping Processes in Silicon. Ed. Wang, F.F.Y., North Holland, p.364, 1981.Google Scholar
[9] Schwenker, R.O., Pan, E.S., and Lever, R.F., J. Appl. Phys. 32, 3195 (1971).CrossRefGoogle Scholar
[10] Chu, W.K., Appl. Phys. Lett. 36, 273 (1980).Google Scholar
[11] Narayan, J. and Holland, W., J. Appl. Phys. 56, 2913 (1984).Google Scholar
[12] Natsuaki, N., Tamura, M., and Tokuyama, T., J. Appl. Phys. 51, 3373 (1980).CrossRefGoogle Scholar