Er-Doping in Silicon by Pulsed Laser Irradiation

Published online by Cambridge University Press:  21 February 2011

Kenshiro Nakashima
Kenshiro Nakashima*
Affiliation:
Nagoya Institute of Technology, Department of Electrical and Computer Engineering, Showa-ku, Nagoya 466, Japan
Get access

Abstract

Erbium ions were successfully doped in silicon by pulsed laser irradiation above the threshold laser energy density. Photoluminescence peaks at 1.54, 1.59 and 1.64 µm from Er-optical centers were observed after annealing of Er-doped samples. The intensity of the 1.54 µm Er-emission band increased upon increase in the laser energy density, and then gradually decreased after reaching the maximum, due to the laser sputtering of the silicon substrate. Oxygen atoms, which were unintentionally codoped with Er-ions, were found to be distributed in the same region as in Er-ions, and were suggested to play roles to activate Er-optical centers. The maximum concentration of Er-ions doped in the solid state regime were estimated to be the order of 1018 cm−3 by the Rutherford backscattering measurements.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 301: Symposium E – Rare-Earth Doped Semiconductors , 1993 , 61
Copyright
Copyright © Materials Research Society 1993

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Ennen, H., Schneider, J., Pomrenke, G., and Axmann, A., Appl. Phys. Lett. 43, 943(1983).Google Scholar
2. Ennen, H., Pomrenke, G., Axmann, A., Eisele, K., Haydl, W., and Schneider, J., Appl. Phys. Lett. 46, 381(1985).Google Scholar
3. Petrov, V. V., Prosolovich, V. S., Tkachev, V. D., Tsyrulkevich, G., and Karpov, Yu. A., Soy. Phys. Semicond. 19, 474(1985).Google Scholar
4. Nakashima, K., Mater. Sci. Forum 38–41, 219(1989).Google Scholar
5. Minaev, N. S., Mudryi, A. V., and Tkachev, V. D., Sov. Phys. Semicond. 13, 233(1979).Google Scholar
6. Uebbing, R. H., Wagner, P., Baumgart, H., and Queisser, H. J., Appl. Phys. Lett. 37, 1078(1980).Google Scholar
7. Tang, Y. S., Jingping, Zhang, Heasman, K. C., and Scaly, B. J., Solid State. Commun. 72, 991(1989).Google Scholar
8. Schmidt, T. and Lischka, K., Phys. Rev. B45, 8989(1992).Google Scholar
9. Favennec, P. N., L'Haridon, H., Moutornet, D., Salvi, M., and Gauneau, M., Jpn. J. Appl. Phys. 29, 1524(1990).Google Scholar
10. Michel, J., Benton, J. L., Ferrante, R. F., Jacobson, D. C., Eaglesham, D. J., Fitzgerald, E. A., Xie, Y. H., Poate, J. M., and Kimerling, L. C., J. Appl. Phys. 70, 2672(1991).Google Scholar
11. Adler, D. A., Jacobson, D. C., Eaglesham, D. J., Marcus, M. A., Benton, J. L., Poate, J. M., and Citrin, P. H., Appl. Phys. Lett. 61, 2181(1992).Google Scholar