Solid State Reactions in the ZR-AL-CU-NI Bulk Metallic Glass Forming Alloy System

Published online by Cambridge University Press:  15 February 2011

Ralf Busch
Affiliation:
California Institute of Technology, WMKeck Laboratory of Engineering Materials, 138-78, Pasadena, CA 91125
Eric Bakke
Affiliation:
California Institute of Technology, WMKeck Laboratory of Engineering Materials, 138-78, Pasadena, CA 91125
William L. Johnson
Affiliation:
California Institute of Technology, WMKeck Laboratory of Engineering Materials, 138-78, Pasadena, CA 91125
Get access

Abstract

Diffusion couples combining a h.c.p. Zr90Al10 supersaturated solid solution with a fc.c. Cu64Ni36 solid solution were annealed at 410°C for different times. The reaction at the interface was investigated by transmission electron microscopy (TEM) and energy dispersive x-ray spectroscopy (EDAX). Cross sectional TEM images and electron diffraction patterns reveal the formation of a non-crystalline layer at the interface between the two solid solutions which grows to a maximum thickness of more than 0.3 μm. Using EDAX, the concentration profiles across the layerswere determined. The glassy layer consists of a Zr-Ni-Al alloy with a small amount of Cu.The concentration profiles reveal that two non-crystalline phases coexist in the diffusion couple. One phase is Ni-rich and the other is Zr-rich. A small gradient of the Ni concentration in the Ni-rich amorphous phase and a steeper gradient in the Zr-rich non crystalline phase indicate that the Ni diffusion constant in the Ni-rich phase is larger than the Ni diffusion constant in the Zr-rich phase. In the late stage of the reaction, the growth of a nanocrystalline layer with an average concentration of Cu 90Nij 0 is observed on the Cu-Ni side of the diffusion couple. Crystallization starts at the Zr-Al side of the diffusion couple.

Type
Research Article
Copyright
Copyright © Materials Research Society 1995

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

References:

1. Johnson, W.L., Prog. Mat. Sci. 30, 81 (1986).Google Scholar
2. Clemens, B.M., Johnson, W.L. and Schwarz, R.B., J. Non-Cryst. Solids 61, 817 (1984).Google Scholar
3. Schroder, H., Samwer, K. and Köster, U., Phys. Rev. Lett. 54, 19 (1985).Google Scholar
4. Krebs, H.U., Webb, D.J. and Marschall, A.F., Phys.Rev.B 35, 5392 (1987).Google Scholar
5. Schneider, S., Schröder, H., and Samwer, K., Thin Solid Films 174, 11 (1989).Google Scholar
6. Inoue, A., Zhang, T. and Masuoto, T., Mater. Trans. JIM 31, 425 (1990)Google Scholar
7. Inoue, A., Zhang, T., and Masumoto, T., Mater. Trans. JIM 31, 177 (1990).Google Scholar
8. Zhang, T., Inoue, A., and Masumoto, T., Mater. Trans. JIM 32, 1005 (1991).Google Scholar
9. Peker, A. and Johnson, W. L., Appl. Phys. Lett. 63, 2342 (1993).Google Scholar