Waveguide prism-coupling methods were used to measure the ordinary and extraordinary refractive indices of AlxGa1-xN films grown on sapphire substrates by HVPE and MOCVD. Several discrete wavelengths ranging from 442 nm to 1064 nm were used and the results were fit to one-term Sellmeier equations. The maximum standard uncertainty in the refractive index measurements was ± 0.005 and the maximum standard uncertainty in the self-consistent calculation for film thickness was ± 15 nm. Analysis of normal-incidence spectroscopic transmittance and reflectance measurements, correlated with the prism-coupling results, was used to determine the ordinary refractive index as a continuous function of wavelength from the band gap wavelength of each sample (between 252 nm and 364 nm) to 2500 nm. The Al compositions of the samples were determined using energy-dispersive X-ray spectroscopy analysis (EDS). HVPE grown samples had compositions x = 0.279, 0.363, 0.593, and 0.657. MOCVD samples had x = 0.00, 0.419, 0.507, 0.618, 0.660, and 0.666. The maximum standard uncertainty in the absolute EDS-determined value for x was ± 0.02.

Homogeneous gelled composites of iron and silica containing 5–30 wt. % Fe have been prepared by low temperature polymerization of aqueous solutions of ferric nitrate, tetraethoxysilane, and ethanol (with an HF catalyst). X-ray diffraction data, characterized by the presence of a diffuse scattering peak centered at 20≈24 degrees and the absence of any strong Bragg scattering from the iron-containing regions, indicates that these bulk materials are comprised of nanometer-sized regions of iron compounds embedded in a silica gel matrix. Scanning electron microscopy observations show that this matrix is characterized by the presence of many interconnected pores and that the size of these pores is related to the particle size of the Fe-containing regions. The paramagnetic nature of these materials at room temperature, as well as the small size of the iron-containing regions, is indicated by the appearance in many of the samples of only a high intensity central doublet in the 57Fe M6ssbauer spectra. The Mössbauer effect data demonstrates that the form of the iron can be changed by a subsequent treatment in an atmosphere of ammonia or hydrogen at elevated temperatures: for a 10 wt. % Fe sample treated with ammonia, only a central doublet was observed but with a much larger quadrupole splitting and isomer shift. Both of these subsequently treated materials became superparamagnetic at room temperature. In addition, magnetic susceptibility measurements indicate that the hydrogen treated material becomes a spin glass at low temperatures.