The influence of Mn2+ on the formation of Fe oxides at pHs of 6.0 and 8.0 and varying Mn/Fe molar ratios (0, 0.1, 1.0, and 10.0) in the FeCl2-NH4OH and FeSO4-NH4OH systems was studied by X-ray powder diffraction (XRD), infrared absorption, transmission electron microscopic, and chemical analyses. In the absence of Mn2+, lepidocrocite (γ-FeOOH) and maghemite (γ-Fe2O3) were the crystalline species formed at pHs of 6.0 and 8.0, respectively, in the FeCl2 system, whereas lepidocrocite and goethite (α-FeOOH) and lepidocrocite were the crystalline species formed at pHs of 6.0 and 8.0, respectively, in the FeSO4 system. The amount of Mn coprecipitated with Fe (as much as 8.1 mole % in the FeCl2 system and 15.0 mole % in the FeSO4 system) increased as the initial solution Mn/Fe molar ratio increased from 0 to 10.0, resulting in the perturbation of the crystallization processes of the hydrolytic products of Fe formed. At pH 6.0, the perturbation led to the formation of poorly ordered lepidocrocite, as reflected in the increasing broadening of its characteristic peaks in the XRD patterns. At pH 8.0, poorly ordered iepidocrocite and a honessite-like mineral (Mn-Fe-SO4-H2O) formed in the FeCl2 and FeSO4 systems, respectively.

The influence of manganese oxide minerals (cryptomelane, hausmannite, and pyrolusite) on the formation of iron oxides was studied in the FeCl2-NH4OH system at different Mn/Fe molar ratios (0, 0.01, 0.1, and 1.0) and pHs (3.0, 4.0, 5.0, and 6.0) by X-ray powder diffraction, infrared absorption, transmission electron microscopic, and chemical analyses. In the absence of Mn minerals, lepidocrocite (γ-FeOOH) precipitated at pHs 5.0 and 6.0; however, no precipitate formed at lower pHs. All the Mn minerals studied promoted the precipitation of iron oxides and oxyhydroxides. In the presence of Mn oxides, Fe2+ was oxidized to Fe3+, which hydrolyzed and precipitated as noncrystalline and/or different crystalline iron oxides and oxyhydroxides, depending on the nature of the Mn oxides present in the system. Simultaneously, Mn2+ was detected in solution after the reaction by electron spin resonance spectroscopy. The presence of cryptomelane and hausmannite resulted in the formation of åkaganeite (β-FeOOH) and magnetite (Fe3O4), respectively. Thus, the effect of Mn oxides on the formation of Fe oxide minerals in the weathering zone merits attention.

The rate of Fe(II) oxidation at a constant rate of oxygen supply in the presence of citrate was measured at pH 6.0 at various citrate/Fe(II) molar ratios at 23.5°C in 0.01 M ferrous Perchlorate system. The kinetics followed a first-order reaction with respect to Fe(II) concentration at constant pH (6.0) and aeration (5 ml/min). The rate constant decreased exponentially from 41.3 × 10-4 to 7.6 × 10-4/min with an increase in the citrate/Fe(II) molar ratio from 0 to 0.1.

The nature of the hydrolytic products formed after 120 min of oxidation was arrived at by X-ray powder diffraction (XRD), infrared spectrometry (IR), and transmission electron microscopic (TEM) analyses. In the absence of citrate, goethite (α-FeOOH) and poorly crystalline lepidocrocite (γ-FeOOH) were the oxidation products formed at pH 6.0. The formation of lepidocrocite was promoted at the expense of goethite at citrate/Fe(II) molar ratios of 0.0005 to 0.005. The formation of lepidocrocite was especially pronounced at a citrate/Fe(II) molar ratio of 0.001, as observed from the width at half height (WHH) and the area of the 020 XRD peak of lepidocrocite. At a citrate/Fe(II) molar ratio of 0.01, however, the crystallization was perturbed resulting in the formation of noncrystalline Fe oxides, and no precipitate was observed at a citrate/Fe molar ratio of 0.1. The strong complexation of Fe(II) with citrate retarded the kinetics of Fe(II) oxidation and the formation and hydrolysis of Fe(III). The complexation, electrostatic, and steric effects of the coexisting citrate anions in solution apparently influenced the oxygen coordination and the way by which the double rows of edge-sharing Fe(O,OH)6 octahedra linked during crystallization, resulting in the formation of lepidocrocite.

Solutions containing AlCl3 and Si(OH)4 (concentrations ≤ 1.5 mM with molar Si:Al ratios of 1:2, 1:1 and 3:1) and FeCl2 (0, 0.5 and 1.0 mM) were adjusted to pH 8 with Ca(OH)2, and incubated at 23°C and 89°C without exclusion of air in the presence of CaCO3 for 8–12 weeks. The products were characterized by infrared spectroscopy and X-ray diffraction. Systems with 3:1 and 1:1 Si:Al ratios without Fe gave hydrous feldspathoids at 23° and 89°C. Systems with 3:1 Si:Al ratios containing Fe gave aluminous nontronites at 89°C and noncrystalline, nontronite-like products at 23°C. Systems with 1:1 Si:Al ratios with added Fe gave Fe(III)-substituted hydrous feldspathoids at 23°C. At 89°C, the system with 1:1 Si:Al ratios and 0.5 mM Fe produced a “protohalloysite,” while that with 1.0 mM Fe gave a poorly ordered nontronite-like layer silicate. In systems with 1:2 Si:Al ratios, the formation of “protoimogolite” at 23°C was little affected by additions of Fe. At 89°C, the “protoimogolite” decomposed to boehmite and poorly-ordered layer silicate phases. Inclusion of 1 mM MgCl2 in the above systems had no effect on the products at 23°C, but at 89°C produced saponites and a mixed layer saponite-chlorite in the 3:1 Si:Al systems, and saponite-like layer structures in the 1:1 and 1:2 Si:Al systems.

Polynuclear Al13 tridecamer species are the major hydrolyzed species of aluminum, but their occurrence in terrestrial environments has not been established. X-ray diffraction (XRD), 27Al nuclear magnetic resonance (NMR), and scanning electron microscope (SEM) analyses show that the presence of tartaric acid (concentration range of 10−5–10−3 M), one of the commonly occurring low-molecular-weight organic acids, inhibits the formation of the Al13 tridecamer species.

In the absence of tartaric acid, the basic aluminum sulfate crystals were of tetrahedral morphology and conformed to isometric symmetry with a = 17.748 Å and space group of P4232. Increasing amounts of tartaric acid [tartaric acid/Al molar ratio (R) ranging from 0.01 to 0.05] modified the crystal morphology from the tetrahedral particles of isometric symmetry (R = 0) to rod-shaped particles of monoclinic symmetry (R = 0.01) to irregularly shaped X-ray noncrystalline microparticles (R = 0.05). Failure to detect the presence of Al13 tridecamer, the dominant hydrolyzed species of aluminum, in terrestrial environments may be partially attributed to the presence of low-molecular-weight organic acids, which inhibit the formation of Al13 tridecamer species.

The Al13 polycation is the predominant hydroxy-Al species in partially neutralized solutions. However, the existence of the Al13 species and the factors governing its formation in terrestrial environments still remain obscure. The objective of this study was to investigate the influence of pyrogallol, a common polyphenol in soils, on the formation of Al13 tridecamer. Hydroxy-Al solutions with an OH/Al molar ratio of 2.2 (pH 4.53) at pyrogallol/Al molar ratios of 0, 0.01, 0.05, 0.1 and 0.5 were prepared and mixed with 0.5 M sodium sulfate to form aluminum sulfate precipitation products. The solid-state 27Al nuclear magnetic resonance (NMR) spectra of the precipitates show that the pyrogallol perturbed the formation of Al13 tridecamer species as indicated by the decrease in the intensity of resonance peak, observed at 62.5 ppm, with increase in the pyrogallol/Al molar ratio. The crystallization of the precipitated Al sulfates was also hampered by pyrogallol, resulting in the formation of X-ray non-crystalline products at a pyrogallol/Al molar ratio of 0.50. The absorbance at 465 and 650 nm of the hydroxy-Al-pyrogallol solutions, the C coprecipitated, the electron spin resonance and 13C CPMAS-NMR spectra of the precipitates indicate the concomitant enhanced abiotic humification of pyrogallol by the X-ray amorphous Al species.

Goethite and maghemite are the stable species of Fe oxyhydroxides-oxides formed an acidic and alkaline environments from the oxidation of Fe(II) perchlorate solutions. The influence of montmorillonite on the oxidation products of 0.02 M ferrous perchlorate at pHs of 6.0 and 8.0 was studied by X-ray diffraction, infrared and transmission electron microscopic analyses. Increased rate of OH consumption during the oxidation at constant pH indicated that the presence of montmorillonite accelerated the rate of Fe(II) oxidation. The presence of montmorillonite, with high surface reactivity, at an initial montmorillonite/Fe (w/w) ratios of 1.4 and 3.4 retarded the formation of goethite, lepidocrocite and maghemite, and maghemite and goethite, and promoted the formation of ferrihydrite and lepidocrocite at pHs of 6.0 and 8.0, respectively. Kaolinite, on the other hand, with relatively low surface reactivity had no influence on the nature of the Fe(II) oxidation products formed at either pH.