The 0.6(Bi0.85La0.15)FeO3-0.4PbTiO3 (BLF-PT) ceramics were prepared by tape casting method. Effects of binder (polyvinylbutyl dibutyl PVB), plasticizer (phthalate-polyethylene glycol DBP-PEG) and dispersant (triethylolamine, TEA) concentration on the rheological properties of BLF-PT slurry were investigated. The optimized component ratio for ceramics powders, binder, plasticizer, dispersant and solvent (ethanol, EtOH) in the slurry was 50 wt.%, 4 wt.%, 6 wt.%, 1 wt.% and 39 wt.%. The dielectric constant ε
, loss tanδ, and remnant polarization P
of BLF-PT ceramics laminated from the tapes were 525 (1 kHz), 1.7% (1 kHz) and 30 μC/cm2 (45 kV/cm), respectively, which were comparable to those of BLF-PT ceramics prepared by traditional solid state reaction method.