The new eudialyte-group mineral amableite-(Ce), ideally Na15[(Ce1.5Na1.5)Mn3]Mn2Zr3□Si[Si24O69(OH)3](OH)2⋅H2O, was discovered in a peralkaline pegmatite at Saint-Amable Sill, Montérégie, Québec, Canada. The associated minerals are albite, microcline, aegirine, serandite, natrolite, yofortierite, and an unidentified titanosilicate forming minute grains. Amableite-(Ce) occurs as yellow equant or thick tabular crystals up to 2 mm across. The observed crystal forms are {0001}; the subordinate forms are {11$\bar{2}$0}, {10$\bar{1}$1}, and {10$\bar{1}$0}. Amableite-(Ce) is brittle, with a Mohs hardness of 5. D(meas) = 2.89(1), D(calc) = 2.899 g⋅cm–3. Amableite-(Ce) is optically anomalously biaxial (+) with α ≈ β = 1.603(2) and γ = 1.608(2). The chemical composition is (wt.%, electron microprobe, H2O measured by means of a modified Penfield method): Na2O 14.20, K2O 0.41, CaO 1.89, MnO 8.25, Fe2O3 2.40, La2O3 3.10, Ce2O3 4.19, Pr2O3 0.16, Nd2O3 0.59, SiO2 49.41, ZrO2 11.17, HfO2 0.24, TiO2 0.68, Nb2О5 1.54, Cl 0.26, H2O 1.70, –O≡Cl –0.06, total 100.13. The crystal structure was determined using single-crystal X-ray diffraction data and refined to R1 = 0.0423. Amableite-(Ce) is trigonal, space group R3, with a = 14.1340(3) Å, c = 30.3780(11) Å and V = 5255.6(3) Å3. The crystal-chemical formula is (Na12.93K0.27Ce0.06)Σ13.26[(Mn2.49Ce0.30Ca0.21)Σ3.00(Ce1.14Na1.04Ca0.82)Σ3.00](Mn1.05Fe0.90□1.05)Σ3.00(Zr2.85Ti0.12Hf0.03)Σ3.00(□0.40Nb0.36Si0.24)Σ1.00(Si0.88□0.12)Σ1.00[Si24(O70.44(OH)1.56)Σ72.00][(OH)2.20(H2O)1.27]Σ3.47Cl0.22 (Z = 3). Infrared and Raman spectra are given. The strongest lines of the powder X-ray diffraction pattern [d, Å (I, %)(hkl)] are: 11.34 (51)(101), 7.06 (76)(110), 4.312 (63)(205), 3.783 (38)(033), 3.538 (43)(027, 220), 2.963 (84)($\bar{3}$45), 2.837 (100)(404). The mineral is named after the discovery locality.

The new mineral evseevite was found in the Arsenatnaya fumarole, Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. Evseevite is represented by two chemical varieties. The variety close to the end-member Na2Mg(AsO4)F (holotype) is associated with sanidine, hematite, tenorite, aegirine, cassiterite, sylvite, halite, johillerite, badalovite, calciojohillerite, hatertite, arsmirandite, yurmarinite, axelite, polyarsite, aphthitalite, potassic-magnesio-fluoro-arfvedsonite, litidionite, ferrisanidine and tridymite. The P- and S-enriched variety (cotype) is associated with hematite, fluorophlogopite, svabite, fluorapatite, tilasite, calciojohillerite, forsterite, cassiterite, belomarinaite and aphthitalite. Evseevite occurs as prismatic, acicular or hair-like crystals up to 0.7 mm long combined in clusters up to 0.5 mm, brushes or crusts up to 2 × 2 mm. It is transparent, colourless or pale pinkish, with vitreous lustre. Dcalc is 3.377 g cm–3 for the holotype and 3.226 g cm–3 for the cotype. Evseevite is optically uniaxial (+), α = 1.545(2), β = 1.546(2), γ = 1.549(2) and 2Vmeas = 40(10)°. The empirical formulae calculated based on O+F = 5 apfu are (Na1.99Ca0.03K0.01)Σ2.03(Mg0.98Fe3+0.01Zn0.01Cu0.01)Σ1.01[(As0.98Si0.01)Σ1.01O4](F0.97O0.03) for the holotype and Na2.02(Mg1.00Fe3+0.03)Σ1.03[(As0.69P0.25S0.07)Σ1.01O4](F0.78O0.22) for the cotype. Evseevite is orthorhombic, Pbcn, a = 5.3224(1), b = 14.1255(3), c = 12.0047(3) Å, V = 902.53(4) Å3 and Z = 8. Strong reflections of the powder XRD pattern [d,Å(I)(hkl)] are: 4.001(100)(121), 3.479(56)(023), 3.041(45)(042), 2.657(44)(200), 2.642(68)(142) and 2.613(36)(104). The crystal structure was solved from single-crystal XRD data and refined on powder data by the Rietveld method, Rwp = 0.0068, Rp = 0.0047 and Robs = 0.0435. Evseevite is isostructural to moraskoite Na2Mg(PO4)F. The structure of evseevite can be described in terms of anion-centred polyhedra. F-centred octahedra [FNa4Mg2]7+ share faces to form chains [FNa2Mg]3+ and AsO4 tetrahedra are located between the chains. Evseevite belongs to a small set of minerals with antiperovskite structures and is the first natural arsenate with antiperovskite units. The mineral is named in honour of the Russian mineralogist Aleksandr Andreevich Evseev (born 1949).

The new mineral bakakinite, ideally Ca2V2O7, was found in the high-temperature (not lower than 500°C) exhalations of the Arsenatnaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It is associated with anhydrite, svabite, pliniusite, schäferite, berzeliite, diopside, hematite, powellite, baryte, fluorapatite, calciojohillerite, ludwigite, magnesioferrite, anorthite, titanite and esseneite. Bakakinite forms flattened crystals up to 30 × 5 μm, typically distorted. The mineral is transparent, colourless or pale yellow, with strong vitreous lustre. Electron microprobe analysis gave (wt.%): CaO 37.04, SrO 0.26, SiO2 0.16, P2O5 1.48, V2O5 49.47, As2O5 10.85, SO3 0.35, total 99.61. The empirical formula calculated on the basis of 7 O apfu is (Ca1.99Sr0.01)Σ2.00(V1.64As0.28P0.06Si0.01S0.01)Σ2.00O7. The Dcalc is 3.463 g cm–3. Bakakinite is triclinic, P$\bar{1}$, unit-cell parameters are: a = 6.64(2), b = 6.92(2), c = 7.01(2) Å, α = 86.59(7), β = 63.77(7), γ = 83.47(6)°, V = 287.0(5) Å3 and Z = 2. The strongest reflections of the powder X-ray diffraction pattern [d,Å(I)(hkl)] are: 4.647(27)(111, 0$\bar{1}$1), 3.138(76)(002), 3.103(100)(120, 121), 3.027(20)(021), 2.960(81)(200), 2.158(19)(031, 302), 1.791(16)(320), 1.682(16)(114) and 1.584(17)(1$\bar{3}$3, 403). Bakakinite is a natural analogue of synthetic Ca2V2O7. The mineral is named in honour of the outstanding Russian crystallographer and crystal chemist Vladimir Vasilievich Bakakin (born 1933).

Bystrite is redefined as a four-layer cancrinite-group mineral with the four-layer Losod-type framework and the end-member formula Na7Ca(Al6Si6O24)S52–Cl–. The mineral is known only at the Malo–Bystrinskoe gem lazurite deposit, Baikal Lake area, Siberia, Russia. The associated minerals are calcite, lazurite, sodalite, fluorapatite, phlogopite, diopside, dolomite and plagioclase. Bystrite is brittle, with the Mohs hardness of 5 and distinct cleavage on {10$\bar{1}$0}. The yellow colour of bystrite is due to the presence of S52– anions occurring in Losod (LOS) cages of the aluminosilicate framework with the ABAC stacking sequence. Measured and calculated density is, respectively, 2.43(1) and 2.412 g cm–3 for the holotype and 2.42(1) and 2.428 g cm–3 for the cotype sample. Bystrite is uniaxial (+), ɛ = 1.660(2) and ω = 1.584(2). The mineral was characterised by infrared and Raman spectra. The empirical formulae of the holotype and cotype samples are Na6.97K0.04Ca0.98(Si6.03Al5.97O24)(S52–)0.93[(SO42–)0.15Cl0.83] and Na6.75K0.04Ca1.11(Si6.09Al5.91O24)(S52–)1.04[(HS–)0.17Cl0.85], respectively. Bystrite is trigonal, space group P31c. The unit-cell parameters are: a = 12.8527(6) Å, c = 10.6907(5) Å, V = 1529.4(1) Å3 and Z = 2. The strongest lines of the powder X-ray diffraction pattern [d, Å (I, %) (hkl)] are: 4.821 (32) (102), 3.915 (38) (211), 3.712 (100) (300), 3.307 (50) (212), 2.782 (18) (400), 2.692 (22) (401), 2.673 (30) (004) and 2.468 (23) (402). Isomorphism and genesis of bystrite-type minerals is discussed. Bystrite and its K,HS-analogue sulfhydrylbystrite, Na5K2Ca(Al6Si6O24)S52–(HS)–, are indicators of highly reducing conditions.

The new eudialyte-group mineral selsurtite, ideally (H3O)12Na3(Ca3Mn3)(Na2Fe)Zr3□Si[Si24O69(OH)3](OH)Cl⋅H2O, was discovered in metasomatic peralkaline rock from the Flora mountain, northern spur of the Selsurt mountain, Lovozero alkaline massif, Kola Peninsula, Russia. The associated minerals are aegirine, albite and orthoclase, as well as accessory lorenzenite, calciomurmanite, natrolite, lamprophyllite and sergevanite. Selsurtite occurs as brownish-red to reddish-orange, equant or flattened on (0001) crystals up to 2 mm across and elongate crystals up to 3 cm long. The main crystal forms are {0001}, {11$\bar{2}$0}, and {10$\bar{1}$1}. Selsurtite is brittle, with the Mohs’ hardness of 5. No cleavage is observed. Parting is distinct on (001). D(meas) = 2.73(2) and D(calc) = 2.722 g⋅cm–3. Selsurtite is optically uniaxial (–), with ω = 1.598(2) and ɛ = 1.595(2). The chemical composition is (wt.%, electron microprobe): Na2O 6.48, K2O 0.27, MgO 0.10, CaO 6.83, MnO 4.73, FeO 1.18, SrO 1.88, La2O3 0.57, Ce2O3 1.07, Pr2O3 0.20, Nd2O3 0.44, Al2O3 0.29, SiO2 50.81, ZrO2 13.50, HfO2 0.45, TiO2 0.61, Nb2О5 1.10, Cl 1.01, SO3 0.29, H2O 8.10, –O≡Cl –0.23, total 99.68. The empirical formula is H25.94Na6.03K0.16Mg0.07Ca3.51Sr0.52Ce0.19La0.10Nd0.08Pr0.03Mn1.91Fe0.47Ti0.22Zr3.16Hf0.06Nb0.24Si24.40Al0.16S0.10Cl0.82O79.13. The crystal structure was determined using single-crystal X-ray diffraction data and refined to R = 0.0484. Selsurtite is trigonal, space group R3, with a = 14.1475(7) Å, c = 30.3609(12) Å, V = 5262.65(7) Å3 and Z = 3. Infrared and Raman spectra show that hydronium cations are involved in very strong hydrogen bonds and form Zundel- and Eigen-like complexes. The strongest lines of the powder X-ray diffraction pattern [d, Å (I, %)(hkl)] are: 11.38 (56)(101), 7.08 (59)(110), 5.69 (36)(202), 4.318 (72)(205), 3.793 (36)(303), 3.544 (72)(027, 220, 009), 2.970 (100)(315) and 2.844 (100)(404). The mineral is named after the discovery locality.

The new alluaudite-group mineral khrenovite with the ideal, end-member formula Na3Fe3+2(AsO4)3 was found in the Arsenatnaya fumarole, Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It is associated with aphthitalite-group sulfates, badalovite, calciojohillerite, nickenichite, johillerite, tilasite, svabite, achyrophanite, ozerovaite, pansnerite, arsenatrotitanite, anhydrite, sanidine, hematite, cassiterite, rutile and pseudobrookite. Khrenovite occurs as coarse prismatic crystals up to 0.2 × 0.3 × 0.8 mm and their clusters up to 1 mm across. It is transparent, honey-coloured, red-, orange- or yellow-brown, with vitreous lustre. Khrenovite is brittle, cleavage was not observed. Dcalc is 4.257 g cm–3. Khrenovite is optically biaxial (+), α = 1.825(7), β = 1.834(7), γ = 1.845(7) and 2Vmeas. = 80(10)°. The chemical composition (wt.%, electron-microprobe) is: Na2O 11.47, K2O 1.23, CaO 0.18, MgO 0.01, MnO 4.10, CuO 4.27, ZnO 1.99, Al2O3 0.17, Fe2O3 21.12, SiO2 0.08, P2O5 0.01, V2O5 0.10, As2O5 56.03, SO3 0.02, total 100.78. The empirical formula calculated on the basis of 12 O apfu is (Na2.26K0.16Ca0.02Mn0.35Cu0.33Zn0.15Al0.02Fe3+1.62)Σ4.91(As2.98Si0.01V0.01)Σ3.00O12. Khrenovite is monoclinic, C2/c, a = 12.2394(7), b = 12.7967(5), c = 6.6589(4) Å, β = 112.953(7)°, V = 960.37(10) Å3 and Z = 4. The crystal structure was solved from single-crystal X-ray diffraction data with R1 = 0.0287. Khrenovite is isostructural with other alluaudite-group minerals. Its structural formula simplified to the species-defining constituents is A(1)NaA(2)’NaM(1)NaM(2)Fe3+2(TAsO4)3. The mineral is named in honour of the Russian volcanologist and geologist Anatoly Petrovich Khrenov (1946–2016).

The new sodalite-group mineral bolotinaite, ideally (Na7□)(Al6Si6O24)F⋅4H2O, was discovered in a volcanic ejectum of trachitoid sanidinite collected from the In den Dellen (Zieglowski) pumice quarry, Laach Lake (Laacher See) palaeovolcano, Eifel region, Rhineland-Palatinate, Germany. The associated minerals are sanidine, nepheline, annite and zircon. Bolotinaite occurs as isolated interpenetration prismatic twins on (111) up to 1.3 mm long, complex twins, and rare non-twinned rhombic dodecahedra up to 0.2 mm across. The colour of bolotinaite is pale yellow to pinkish coloured, the streak is white and the lustre is vitreous. Weak orange–yellow fluorescence under longwave ultraviolet radiation (λ = 330 nm) is due to the presence of trace amounts of the S2•– radical anion. Bolotinaite is brittle, with a Mohs’ hardness of 5. No cleavage is observed. The fracture is uneven. D(meas) = 2.27(2) g⋅cm–3, D(calc) = 2.291 g⋅cm–3. Bolotinaite is optically isotropic, with n = 1.488(2) (λ = 589 nm). The chemical composition is (wt.%, electron microprobe, CO2 determined by quantitative IR spectroscopy analysis, H2O calculated from the empirical formula with four H2O molecules per formula unit): Na2O 18.30, K2O 3.87, CaO 0.57, Al2O3 28.85, SiO2 37.97, CO2 1.66, SO3 1.37, F 1.60, Cl 0.57, 2.22, H2O 7.21, –O≡(F,Cl) –0.80, total 101.17. The empirical formula is (Na5.92K0.82Ca0.10H0.08)(Si6.33Al5.67O24)(SO4)0.17F0.84Cl0.16(H2O)3.96(CO2)0.38. A high content of H2O and the presence of CO2 molecules and H+ cations as well as trace amounts of S2•– are confirmed by means of infrared and Raman spectroscopy. The crystal structure was determined using single-crystal X-ray diffraction data and refined to R = 0.0335. Bolotinaite is cubic, space group I$\bar{4}$3m, with a = 9.027(1) Å, V = 735.7(2) Å3 and Z = 1. The strongest lines of the powder X-ray diffraction pattern [d, Å (I, %) (hkl)] are: 6.36 (47) (110), 4.502 (10) (200), 3.679 (100) (211), 2.851 (28) (310), 2.603 (29) (222) and 2.126 (18) (330). The mineral is named in honour of the Russian crystallographer and crystal chemist Dr. Nadezhda Borisovna Bolotina (b. 1949).

Reznitskyite, ideally CaMg(VO4)F, is a new mineral species of the tilasite group from the Arsenatnaya fumarole, Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It occurs as zones (usually up to 0.05 mm thick) in crystals of V- and P-containing tilasite or as homogeneous grains up to 0.1 mm across. It was found in polymineralic sublimate encrustations in association with minerals of the svabite–fluorapatite–pliniusite system and the schäferite–berzeliite, tilasite–isokite, wagnerite–arsenowagnerite and udinaite–arsenudinaite series. The mineral assemblage also includes calciojohillerite, diopside, forsterite, titanite, rhabdoborite-(V), rhabdoborite-(W), rhabdoborite-(Mo), ludwigite, powellite, scheelite, hematite, baryte and magnesioferrite. Reznitskyite is transparent or semi-transparent, colourless, with vitreous lustre. Dcalc. = 3.453 g cm–3. Under the microscope, in reflected light reznitskyite is grey, non-pleochroic, with very weak bireflectance (ΔR589 nm = 0.5%) and distinct anisotropy. Reznitskyite is the first vanadate with a titanite-type structure. It is monoclinic, space group C2/c, a = 6.6912(7), b = 8.9395(7), c = 7.0587(8) Å, β = 113.078(13)°, V = 388.43(8) Å3 and Z = 4. The strongest reflections of the powder X-ray diffraction pattern are [d in Å(I)(hkl)]: 3.082(100)(200), 3.250(66)($\bar{1}$12, 002), 2.631(44)(022), 2.854(34)($\bar{2}$02), 2.683(33)(130), 3.686(26)(021), 2.531(25)(220), 1.749(25)($\bar{3}$32, $\bar{2}$04) and 2.344(24)(131). Electron microprobe analysis gave (wt.%) MgO 20.44, CaO 26.83, P2O5 6.24, V2O5 21.09, As2O5 18.97, SO3 0.47, F 9.42, –O=F –3.97, with a total of 99.49. The empirical formula of reznitskyite, calculated on the basis of O+F = 5 atoms per formula unit, is: Ca0.97Mg1.03(V0.47As0.33P0.18S0.01)Σ0.99O3.99F1.01. Reznitskyite is a vanadate analogue of tilasite CaMg(AsO4)F and isokite CaMg(PO4)F. The mineral is named in honour of the outstanding Russian mineralogist Leonid Zinovievich Reznitsky (born 1938) who has made significant contribution to the mineralogy of vanadium.

Calciolangbeinite, ideally K2Ca2(SO4)3, exists in two modifications, cubic and, first described in the present paper, orthorhombic. They are topologically-similar polymorphs which can be designated as calciolangbeinite-C and calciolangbeinite-O. Calciolangbeinite-O is the first natural orthorhombic langbeinite-like sulfate. It clearly differs from calciolangbeinite-C in the powder X-ray diffraction pattern, optical data and Raman spectrum. Calciolangbeinite-O is found in sublimates of the active Arsenatnaya fumarole at the Tolbachik volcano, Kamchatka, Far Eastern Region, Russia and in pyrometamorphic rocks of the Hatrurim Complex at Jabel Harmun, Judean Desert, Palestinian Autonomy and Har Parsa, Negev Desert, both in Israel. Calciolangbeinite-C is known only in fumarole sublimates at Tolbachik. Calciolangbeinite forms a continuous solid-solution system with langbeinite K2Mg2(SO4)3. The majority of the system is represented by cubic phases, and only members with compositions K2(Ca2.0–1.9Mg0.0–0.1)(SO4)3 have orthorhombic symmetry under room-temperature conditions. The crystal structure of calciolangbeinite-O was studied on a single crystal, chemically very close to K2Ca2(SO4)3, from Tolbachik (R1 = 2.75%). The unit-cell parameters are: a = 10.3330(2), b = 10.5027(2), c = 10.1763(2) Å, V = 1104.37(4) Å3 and Z = 4; space group is P212121. Calciolangbeinite-O is a low-temperature modification of K2Ca2(SO4)3 belonging to the K2Cd2(SO4)3 structure type whereas calciolangbeinite-C (space group P213), a high-temperature modification, has the langbeinite-type structure. The significant Mg admixture in calciolangbeinite-C from Tolbachik probably stabilises its cubic structure at room temperature. In both high-temperature fumaroles and pyrometamorphic rocks calciolangbeinite crystallises in the cubic modification, and during cooling its chemical variety close to the end-member K2Ca2(SO4)3 undergoes phase transition to calciolangbeinite-O, whereas the Mg-enriched varieties of the mineral remain calciolangbeinite-C.

The new alluaudite-group mineral paraberzeliite was found in the Arsenatnaya fumarole, Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. In the deepest zone of Arsenatnaya, paraberzeliite (holotype) is associated with anhydrite, diopside, hematite, svabite, berzeliite, schäferite, calciojohillerite, magnesioferrite, ludwigite, fluorapatite, powellite, baryte, and rhabdoborite-group and aphthitalite-group members. In the middle zone of the fumarole, paraberzeliite occurs with hematite, calciojohillerite, badalovite, johillerite, nickenichite, tilasite, svabite, fluorophlogopite, sanidine, cassiterite, anhydrite, metathénardite and belomarinaite. Paraberzeliite forms prismatic crystals up to 0.2 mm × 0.2 mm × 1 mm often occurring in open-work aggregates. It is transparent, brown (from light to dark brown, sometimes with purple or red hue) or green (from pale greenish to yellow–green). The mineral is brittle, cleavage was not observed. The Mohs hardness is 3½. Dcalc is 3.811 g cm–3. Paraberzeliite is optically biaxial (+), α = 1.718(4), β = 1.728(4), γ = 1.742(4) and 2Vmeas. = 85(5)°. The chemical composition (wt.%, electron-microprobe; holotype) is: Na2O 6.43, CaO 16.65, MgO 11.64, MnO 1.65, CuO 0.06, Fe2O3 2.45, V2O5 1.10, As2O5 59.46, total 99.44. The calculated empirical formula based on 12 O atoms per formula unit is (Na1.20Ca1.71Mg1.66Mn0.13Fe3+0.18)Σ4.88(As2.98V0.07)Σ3.05O12. Paraberzeliite is monoclinic, C2/c, a = 12.3143(7), b = 13.0679(5), c = 6.7717(4) Å, β = 113.657(7)°, V = 998.14(10) Å3 and Z = 4. The crystal structure was solved from single-crystal X-ray diffraction data, R = 0.0349. Paraberzeliite is isostructural with other alluaudite-group minerals. Its simplified crystal chemical formula is A(1)CaA(2)'NaM(1)CaM(2)Mg2(TAsO4)3. The idealised formula is NaCa2Mg2(AsO4)3, or, according to the actual nomenclature of alluaudite-group arsenates, NaCaCaMg2(AsO4)3. The name paraberzeliite reflects the dimorphism of this alluaudite-group mineral with the arsenate garnet berzeliite, ideally (Ca2Na)Mg2(AsO4)3.

The new sodalite-group mineral sapozhnikovite, ideally Na8(Al6Si6O24)(HS)2, was discovered in a hydrothermally altered urtite-like rock at Karnasurt Mountain, Lovozero alkaline massif, Kola Peninsula, Russia. The associated minerals are nepheline, aegirine, potassic feldspar, albite, kyanoxalite, natrolite, fluorapatite, fluorcaphite, lomonosovite (partially or completely altered to murmanite) and loparite-(Ce). Sapozhnikovite forms isolated colourless to pale greyish anhedral equant grains up to 5 mm across. The streak is white and the lustre is vitreous. Strong orange fluorescence under longwave UV radiation (λ = 330 nm) and weak yellow-orange fluorescence under shortwave UV radiation (λ = 245 nm) is observed. Sapozhnikovite is brittle, with a Mohs hardness of 5½. Cleavage is imperfect on (110). Density measured by flotation in heavy liquids is equal to 2.25(1) g⋅cm–3. The calculated density is 2.255 g⋅cm–3. Sapozhnikovite is characterised by infrared, Raman, electron spin resonance, NIR-Vis-UV absorption, and photoluminescence spectroscopy. The chemical composition is (wt.%, electron microprobe, H2O determined by gas chromatography of ignition products): Na2O 25.05, Al2O3 32.44, SiO2 37.58, HS 4.33, Cl 2.22, H2O 0.30, –O≡(Cl,HS) –1.55, total 100.37. The empirical formula is Na7.73Al6.08Si5.97O24(HS)1.25Cl0.60⋅0.16H2O. The crystal structure was determined using single-crystal X-ray diffraction data and refined to R1 = 1.62%. Sapozhnikovite is cubic, P$\bar{4}$3n, with a = 8.9146(1) Å, V = 708.45(2) Å3 and Z = 1. The new mineral is isostructural with sodalite. The strongest lines of the powder X-ray diffraction pattern [d, Å (I, %) (hkl)] are: 6.30 (37) (110), 3.638 (100) (211), 2.821 (14) (310), 2.572 (18) (222), 2.382 (16) (321) and 2.101 (29) (411). The mineral is named in honour of the Russian mineralogist and crystallographer Dr. Anatoly Nikolaevich Sapozhnikov (b. 1946).

The new wermlandite-group mineral erssonite, ideally CaMg7Fe3+2(OH)18(SO4)2⋅12H2O (or [Mg7Fe3+2(OH)18][Ca(SO4)2]⋅12H2O), was discovered in a late-stage, low-temperature assemblage in cavities of a magnetite-bearing dolomitic rock from the Långban deposit, Värmland county, Bergslagen ore province, Sweden. The associated minerals are dolomite, calcite, members of the magnetite–magnesioferrite solid-solution series, phlogopite, chrysotile, pyroaurite and norbergite. Erssonite has a vitreous lustre and forms colourless, platy hexagonal crystals flattened on [0001], up to 0.5 mm across and up to 10 μm thick, occurring mainly as aggregates in cavities of dolomitic rock. Erssonite is malleable; separate crystals are flexible and non-elastic, with a perfect, mica-like cleavage on {0001}. The calculated density is equal to 2.02 g⋅cm–3. Raman spectroscopy shows the presence of typical bands for S–O bonds attributed to intercalated SO42– anions and structural OH– anions together with the absence of C–O bonds, attributed to carbonate anions. The chemical composition is (wt.%, electron microprobe, H2O content is calculated from structure data): MgO 28.67, CaO 2.76, Al2O3 0.23, Cr2O3 0.23, Fe2O3 16.00, SiO2 0.48, SO3 14.80, H2O 35.58, total 98.75. The empirical formula based on 38 O atoms is H41.48Ca0.52Mg7.47Fe3+2.11Al0.05Cr0.03S1.94Si0.08O38. The ideal formula is CaMg7Fe3+2(OH)18(SO4)2⋅12H2O or {Mg7Fe3+2(OH)18}{[Ca(H2O)6](SO4)2(H2O)6}. The crystal structure was determined using single-crystal X-ray diffraction data and refined to R = 0.093. Erssonite is trigonal, P$\bar{3}$c1, with a = 9.3550(6), c = 22.5462(14) Å, V = 1708.8(2) Å3 and Z = 2. The strongest lines of the powder X-ray diffraction pattern [d, Å (I, %)(hkl)] are: 11.22 (90)(002), 5.63 (64)(004), 4.670 (100)(110, 104, 014), 2.626 (64)(032, 302), 2.435 (66)(034, 304) and 1.951 (45)(038, 308). The mineral is named in honour of the Swedish amateur mineralogist Dr. Anders Ersson (b. 1971).

The new mineral yurgensonite, ideally K2SnTiO2(AsO4)2, the first natural arsenate with species-defining tin, and the continuous isomorphous series between yurgensonite and katiarsite KTiO(AsO4) are described from sublimates of the Arsenatnaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. Yurgensonite and a Sn-bearing variety of katiarsite are associated closely with one another and with badalovite, pansnerite, yurmarinite, achyrophanite, arsenatrotitanite, hatertite, khrenovite, svabite, sanidine, hematite, cassiterite, rutile and aphthitalite-group sulfates. Yurgensonite occurs as sword-shaped crystals up to 0.01 mm × 0.05 mm × 1 mm or acicular to hair-like individuals up to 1 mm long, typically forming radial aggregates up to 2 mm across. It is transparent, colourless, white or pale beige, with vitreous lustre. The mineral is brittle, cleavage was not observed. Dcalc is 3.877 g cm-3. Yurgensonite is optically biaxial (–), α = 1.764(6), β = 1.780(6), γ = 1.792(6) and 2Vmeas. is large. Chemical composition (wt.%, electron-microprobe; holotype) is: Na2O 0.51, K2O 16.27, Rb2O 0.12, Al2O3 0.26, Fe2O3 4.33, SiO2 0.29, TiO2 10.17, SnO2 22.01, P2O5 0.14, V2O5 0.19, As2O5 40.20, Sb2O5 4.88, SO3 0.28, total 99.65. The empirical formula based on 10 O apfu is (K1.92Na0.09Rb0.01)Σ2.02(Sn0.81Ti0.71Fe3+0.30Sb5+0.17Al0.03)Σ2.02(As1.945Si0.03S0.02P0.01V0.01)Σ2.015O10. Yurgensonite is orthorhombic, Pna21, a = 13.2681(6), b = 6.6209(3), c = 10.8113(5) Å, V = 949.74(7) Å3 and Z = 4. The crystal structure was solved from single-crystal X-ray diffraction data, R = 5.02%. Yurgensonite belongs to the KTP-structure type. It is a Ti,Sn-ordered analogue of katiarsite. The structure contains chains of corner-linked alternating crystallographically non-equivalent octahedra M(1) and M(2). In yurgensonite, Sn4+ prevails in the M(2)O6 octahedron whereas the M(1) site is Ti4+-dominant. The new mineral is named in honour of the Russian mineralogist, geochemist and specialist in studies of ore deposits Professor Georgiy Aleksandrovich Yurgenson (born 1935).

The new alluaudite-group mineral calciojohillerite is one of the major arsenates in sublimates of the Arsenatnaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. In middle zones of the fumarole, calciojohillerite is associated with hematite, tenorite, johillerite, nickenichite, bradaczekite, badalovite, tilasite, lammerite, ericlaxmanite, aphthitalite-group sulfates, langbeinite, calciolangbeinite, anhydrite, sanidine, fluorophlogopite, fluoborite, cassiterite, pseudobrookite, rutile, sylvite and halite. In deep zones it occurs in association with anhydrite, diopside, hematite, svabite, berzeliite, schäferite, forsterite, magnesioferrite, ludwigite, rhabdoborite-group fluoroborates, powellite, baryte, fluorapatite, udinaite, arsenudinaite and paraberzeliite. Calciojohillerite forms prismatic crystals up to 1 cm long, their aggregates and crystal crusts up to 0.5 m2. It is transparent, colourless, pale green, pale yellow, light blue, pale lilac or pink, with vitreous lustre. The mineral is brittle, with imperfect cleavage. The Mohs hardness is 3½. Dcalc is 3.915 g cm–3. Calciojohillerite is optically biaxial (–), α = 1.719(3), β = γ = 1.732(3); 2Vmeas. = 15(10)°. Chemical composition (wt.%, electron-microprobe; holotype) is: Na2O 7.32, K2O 0.10, CaO 6.82, MgO 20.31, MnO 0.68, CuO 0.27, ZnO 0.02, Al2O3 0.56, Fe2O3 3.53, TiO2 0.01, SiO2 0.03, P2O5 1.25, V2O5 0.10, As2O5 58.77, SO3 0.13, total 99.90. The empirical formula based on 12 O atoms is (Na1.30K0.01Ca0.67Mg2.78Mn0.05Cu0.02Al0.06Fe3+0.24)Σ5.13(As2.83P0.10S0.01V0.01)Σ2.95O12. Calciojohillerite is monoclinic, C2/c, a = 11.8405(3), b = 12.7836(2), c = 6.69165(16) Å, β = 112.425(3)°, V = 936.29(4) Å3 and Z = 4. The crystal structure was solved from single-crystal X-ray diffraction data, R1 = 0.0227. Calciojohillerite is isostructural with other alluaudite-group minerals. Its simplified crystal chemical formula is A(1)CaA(1)′□A(2)□A(2)′NaM(1)MgM(2)Mg2(AsO4)3 (□ = vacancy). The idealised formula is NaCaMg3(AsO4)3, or, according to the nomenclature of alluaudite-group arsenates, NaCaMgMg2(AsO4)3. Calciojohillerite is named as an analogue of johillerite NaCu2+MgMg2(AsO4)3 with species-defining Ca instead of Cu in the ideal formula.

The new alluaudite-group mineral badalovite was found in the Arsenatnaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It is associated with hematite, tenorite, cassiterite, johillerite, nickenichite, calciojohillerite, bradaczekite, metathénardite, aphthitalite, langbeinite, calciolangbeinite, sanidine, fluorophlogopite, fluoborite, tilasite, anhydrite, pseudobrookite, sylvite, halite, lammerite, urusovite, ericlaxmanite, arsmirandite, svabite, krasheninnikovite, euchlorine, wulffite and alumoklyuchevskite. Badalovite forms oblique-angled prismatic crystals up to 1 mm × 1 mm × 5 mm, typically combined in groups or crusts up to several hundred cm2 in area. The mineral is transparent, green, grey, yellow or colourless, with vitreous lustre. It is brittle, the Mohs hardness is 3½. Cleavage was not observed, the fracture is uneven. Dcalc is 4.02 g cm–3. Badalovite is optically biaxial (–), α = 1.753(3), β = 1.757(3), γ = 1.758(3) and 2Vmeas. = 50(10)°. Chemical composition (wt.%, electron-microprobe; holotype) is: Na2O 9.23, K2O 0.19, CaO 2.04, MgO 13.78, MnO 0.31, CuO 0.12, ZnO 0.24, Al2O3 0.06, Fe2O3 12.77, TiO2 0.01, SiO2 0.06, P2O5 0.33, V2O5 0.05, As2O5 61.51, SO3 0.02, total 100.72. The empirical formula based on 12 O apfu is Na1.67Ca0.20K0.02Mg1.92Zn0.02Mn0.02Cu0.01Fe3+0.90Al0.01(As3.01P0.03Si0.01)Σ3.05O12. The simplified formula is Na2Mg2Fe3+(AsO4)3. Badalovite is monoclinic, C2/c, a = 11.9034(3), b = 12.7832(2), c = 6.66340(16) Å, β = 112.523(3)°, V = 936.59(4) Å3 and Z = 4. The strongest reflections of the powder XRD pattern [d,Å(I)(hkl)] are: 6.41(38)(020), 5.505(20)(200), 3.577(23)($\bar{1}$31), 3.523(25)(310), 3.211(46)($\bar{1}$12), 2.911(28)($\bar{2}$22, $\bar{3}$12), 2.765(100)(240, 400) and 2.618(26)($\bar{1}$32). The crystal structure was solved from single-crystal XRD data with an R1 of = 2.49%. Badalovite is isostructural with other alluaudite-group minerals. Its simplified crystal chemical formula is A(1)NaA(1)’□A(2) □A(2)’NaM(1)MgM(2)(Mg0.5Fe3+0.5)2(AsO4)3 (□ – vacancy) and the end-member formula is NaNaMg(MgFe3+)(AsO4)3. The mineral is named in honour of the outstanding mineralogist and geochemist Stepan Tigranovich Badalov (1919–2014).

Tourmaline from the Solnechnoe hydrothermal granitoid-related tin deposit in the Khabarovsk Krai, Russian Far East has been studied with electron microprobe, infrared and Mössbauer spectroscopy. Tourmaline formed in three distinct stages with different types of chemical substitution. Tourmaline from the first unmineralised stage is classified as dravite or schorl, which could be enriched locally in Ca, the X-site vacancy and F. This tourmaline is characterised by the Fe ↔ Mg and X vacancy + Al ↔ Na + Fe substitutions. The second, molybdenum-stage tourmaline, is schorl–dravite and fluor-schorl–fluor-dravite enriched in Ca, and a few compositions belong to the calcic group. The predominant substitution is Ca + Mg ↔ Na + Al. The third, tin-stage tourmaline, is classified as schorl–dravite with some tourmalines being fluor-schorl, oxy-schorl, foitite and magnesio-foitite. The tin-stage tourmaline is characterised by the substitutions Fe2+ ↔ Mg, Altot + O2– ↔ Fe2+ + OH–, and Fe3+ ↔ Altot. An increase of the Fe3+/Fetot value from 3–9% in the molybdenum stage to 12–16% in the tin-stage tourmalines indicates an increase in oxidation potential, which possibly contributed to cassiterite deposition. Comparison of tourmalines from greisen, porphyry and intrusion-related tin deposits worldwide shows they differ in primary chemical substitutions so can be characterised by this mechanism. The Fe3+/Fetot value in tourmaline also appears to be one of the indications for the tin deposit type. The Fe3+/Fetot value increases from <10% in greisen tourmaline through 15% in tourmaline from intrusion-related deposits to 20% in tourmaline from porphyry deposits.

The new mineral pansnerite, ideally K3Na3Fe3+6(AsO4)8, was found in the Arsenatnaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It is associated with aphthitalite, hematite, sanidine, badalovite, khrenovite, achyrophanite, arsenatrotitanite, ozerovaite, tilasite, calciojohillerite, johillerite, nickenichite, svabite, katiarsite, yurmarinite, anhydrite, rutile, cassiterite and pseudobrookite. Pansnerite forms tabular to lamellar (flattened on {010}), usually pseudo-hexagonal crystals up to 0.2 mm × 0.7 mm × 1 mm and crystal clusters up to 2 mm across. It is transparent to translucent, light green, pale greenish, yellowish–greenish or yellowish, with vitreous lustre. The mineral is brittle, with perfect {010} cleavage. The Mohs’ hardness is ca 3. Dcalc is 3.596 g cm–3. Pansnerite is optically biaxial (–), α = 1.702(4), β = 1.713(4), γ = 1.717(4), 2Vmeas = 45(10)° and 2Vcalc = 62°. Chemical composition (holotype, wt.%, electron microprobe data) is: Na2O 6.39, K2O 8.52, CaO 0.08, MgO 0.08, MnO 0.02, NiO 0.02, CuO 1.35, ZnO 0.34, Al2O3 7.35, Cr2O3 0.04, Fe2O3 16.72, SiO2 0.16, P2O5 0.22, V2O5 0.09, As2O5 57.76, SO3 0.04, total 99.20. The empirical formula based on 32 O apfu is K2.86Na3.26Ca0.02(Fe3+3.31Al2.28Cu0.27Zn0.07Mg0.03Cr0.01)Σ5.97(As7.95P0.05Si0.04V0.02S0.01)Σ8.06O32. Pansnerite is orthorhombic, Cmce, a = 10.7372(3), b = 20.8367(8), c = 6.47335(15) Å, V = 1448.27(7) Å3 and Z = 2. The strongest reflections of the X-ray powder diffraction pattern [d,Å(I)(hkl)] are: 10.49(100)(020), 5.380(88)(111), 4.793(65)(220), 3.105(46)(311, 002), 3.079(32)(112, 061), 2.932(35)(260), 2.783(65)(202) and 2.694(52)(400, 222). The crystal structure was solved from single-crystal X-ray diffraction data, R1 = 2.82%. The structure is based on heteropolyhedral layers formed by MO6 octahedra (M = Fe3+ and Al) sharing common vertices and connected by AsO4 tetrahedra. Na+ and K+ cations are located in the interlayer space. The mineral is named in honour of the German–Russian mineralogist and geographer Lavrentiy Ivanovich Pansner (1777–1851). Pansnerite forms a solid-solution series with the isotypic mineral ozerovaite, ideally KNa2Al3(AsO4)4.

The new mineral zubkovaite, Ca3Cu3(AsO4)4, was found in the Arsenatnaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It is associated with anhydrite, svabite, hematite, johillerite, tilasite, fluorophlogopite, sanidine and aphthitalite. Zubkovaite occurs as coarse prismatic crystals up to 0.01 mm × 0.01 mm × 0.2 mm combined in radiating aggregates or crusts. The mineral is transparent, bright sky-blue, turquoise-coloured or light bluish-green, with vitreous lustre. It is brittle, with imperfect cleavage. The Mohs’ hardness is ca 3. Dcalc is 4.161 g cm–3. Zubkovaite is optically biaxial (–), α = 1.747(5), β = 1.774(5), γ = 1.792(5) and 2Vmeas = 75(10)°. Chemical composition (wt.%, electron microprobe) is: CaO 19.22, CuO 27.37, As2O5 52.54, SO3 0.67, total 99.80. The empirical formula based on 16 O apfu is Ca2.96Cu2.97(As3.945S0.07)Σ4.015O16. Zubkovaite is monoclinic, C2, a = 16.836(3), b = 5.0405(8), c = 9.1173(17) Å, β = 117.388(13)°, V = 687.0(2) Å3 and Z = 2. The strongest reflections of the powder XRD pattern [d,Å (I) (hkl)] are: 7.44 (100) ($\bar 2$01), 3.727 (79) (400, $\bar 2$02, $\bar 3$11), 3.334 (92) ($\bar 1$12), 2.914 (73) (311), 2.765 (50) ($\bar 6$01, $\bar 6$02), 2.591 (96) ($\bar 3$13) and 2.521 (53) (020). The crystal structure is unique for minerals. It was solved from single-crystal X-ray diffraction data to R = 7.19%. The structure contains trimers of Cu2+-centred polyhedra (consisting of one distorted square CuO4 in the core and two distorted square pyramids CuO5) and two crystallographically independent As5+O4 tetrahedra playing different roles: As(2)O4 tetrahedra link neighbouring trimers into ribbons whereas As(1)O4 tetrahedra link adjacent ribbons into heteropolyhedral layers; Ca cations are located in the interlayer space. The mineral is named in honour of the Russian crystallographer and crystal chemist Natalia Vital'evna Zubkova (born 1976).