The temperature distribution in InGaN-MQW light emitting diodes was examined during operation with spatially resolved micro-Raman and micro-Electroluminescence measurements. The experimental results were compared to finite element simulations. A good agreement between the different experimental and calculated data is found. Maximum operation temperatures up to 140 °C at a moderate forward currents of 30 mA are revealed by all three independent methods. Influences of substrate thickness, different substrates, and even bond-wires are shown.

Electroluminescence (EL) is the most significant measure for light-emitting diodes since it probes the most relevant properties of the fully processed device during operation. In addition to the information gained by conventional spectrally resolved EL, scanning micro-EL provides spatially resolved information. The devices under investigation are InGaN/GaN-LEDs with single peak band-band emission at about 400 nm grown by MOVPE on sapphire substrates.

The µ-EL-characterization is performed as a function of injection current densities and the emission is investigated from the epitaxial layer as well as from substrate side. Spatially resolved wavelength images reveal emission peaks between 406 nm and 417 nm, corresponding either to In fluctuations of 1 %−1.5 % or local fluctuations of piezo electric fields. Beside the information on the emission wavelength fluctuations µ-EL is used to determine the temperature distribution in the LEDs and to investigate transparent contacts.

Electroluminescence (EL) is the most significant measure for light-emitting diodes since it probes the most relevant properties of the fully processed device during operation. In addition to the information gained by conventional spectrally resolved EL, scanning micro-EL provides spatially resolved information. The devices under investigation are InGaN/GaN-LEDs with single peak band-band emission at about 400 nm grown by MOVPE on sapphire substrates.

The μ-EL-characterization is performed as a function of injection current densities and the emission is investigated from the epitaxial layer as well as from substrate side. Spatially resolved wavelength images reveal emission peaks between 406 nm and 417 nm, corresponding either to In fluctuations of 1%–1.5% or local fluctuations of piezo electric fields. Beside the information on the emission wavelength fluctuations ν-EL is used to determine the temperature distribution in the LEDs and to investigate transparent contacts.

The temperature distribution in InGaN-MQW light emitting diodes was examined during operation with spatially resolved micro-Raman and micro-Electroluminescence measurements. The experimental results were compared to finite element simulations. A good agreement between the different experimental and calculated data is found. Maximum operation temperatures up to 140 °C at a moderate forward currents of 30 mA are revealed by all three independent methods. Influences of substrate thickness, different substrates, and even bond-wires are shown.