Hydroxylbastnäsite-(La), the OH- and La-dominant member of the bastnäsite group, in fact known for many years, was studied in detail and has been approved by the IMA–CNMNC as a new mineral species with the ideal, end-member formula La(CO3)(OH). The holotype originates from the Vuoriyarvi (another spelling: Vuorijärvi) alkaline-ultrabasic complex, Northern Karelia, and the cotype from the Mochalin Log REE deposit, Potaniny Mts, South Urals, both in Russia. At Vuoriyarvi, hydroxylbastnäsite-(La) occurs as clusters (up to 1 mm) of light brown, honey-yellow or colourless hexagonal tabular to short-prismatic crystals up to 0.15 mm associated with fluorite and ancylite-(Ce) in cavities of calcite–dolomite carbonatites. At Mochalin Log, hydroxylbastnäsite-(La) forms light brown grains up to 0.2 mm included in massive aggregates of other LREE minerals: bastnäsite-(Ce), bastnäsite-(La), percleveite-(Ce), percleveite-(La), biraite-(Ce), biraite-(La), törnebohmite-(La), ferriperbøeite-(Ce), allanite-(Ce), etc. Dmeas is 4.75(2) and Dcalc is 4.778 g cm–3 (holotype). Hydroxylbastnäsite-(La) is optically uniaxial (+), ω = 1.76(1) and ε = 1.86(1) (holotype). The chemical composition (wt.%, electron microprobe, CO2 and H2O calculated: holotype/cotype) is: CaO 0.23/0.00, SrO 0.07/0.00, La2O3 39.47/39.58, Ce2O3 33.51/31.99, Pr2O3 1.03/1.51, Nd2O3 1.95/2.38, F 0.76/3.33, CO2 20.49/20.34, H2O 3.77/2.58, –O=F 0.32/1.40, total 100.96/100.31. The empirical formulae, calculated based on the sum of metal cations of 1 apfu and one CO3 group pfu, are (La0.52Ce0.44Nd0.02Pr0.01Ca0.01)Σ1.00(CO3)[(OH)0.90F0.09]Σ0.99 (holotype) and (La0.53Ce0.42Nd0.03Pr0.02)Σ1.00(CO3)[(OH)0.62F0.38]Σ1.00 (cotype). Hydroxylbastnäsite-(La) is hexagonal, P6̅, unit-cell parameters (from powder XRD data, holotype/cotype) are: a = 12.537(3)/12.533(1), c = 9.968(2)/9.908(1) Å, V = 1356.8(5)/1347.9(3) Å3 and Z = 18. Strong reflections of the powder XRD pattern [d,Å(I)(hkl)] are (holotype): 4.98(39)(002), 3.616(88)(300), 2.926(100)(302), 2.089(41)(330), 2.052(46)(304) and 1.927(40)(332). The crystal structure of holotype hydroxylbastnäsite-(La) was refined by the Rietveld method, Rwp = 0.0071, Rp = 0.0050, Robs = 0.0466. It is isostructural to hydroxylbastnäsite-(Ce) and synthetic bastnäsite-type hydroxyl-carbonates REE3+(CO3)(OH) (REE = La–Er), but differs from fluorine-dominant bastnäsites which adopt the space group P6̅2c.

A new mineral cuprodobrovolskyite, ideally Na4Cu(SO4)3, was found in sublimates of the Arsenatnaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It is associated with petrovite, saranchinaite, euchlorine, krasheninnikovite, langbeinite, calciolangbeinite, anhydrite, sanidine, tenorite and hematite. Cuprodobrovolskyite occurs as coarse hexagonal tabular or equant, typically skeletal crystals up to 1 mm and their clusters or crusts up to 1.5 cm × 2.5 cm in area. The mineral is transparent, light blue or greenish-bluish to almost colourless with vitreous lustre. Cuprodobrovolskyite is optically uniaxial (+) with ω = 1.509(3) and ε = 1.528(3). The empirical formula calculated on the basis of 12 O apfu is (Na3.64K0.09Pb0.03)Σ3.76(Cu0.51Ca0.22Mg0.16Zn0.07Al0.01Mn0.01)Σ0.98S3.04O12. The unit-cell parameters of cuprodobrovolskyite calculated from the powder X-ray diffraction data are: a = 15.702(2), c = 22.017(5) Å, V = 4701.0(2) Å3, space group R3 and Z = 18. The crystal structure was studied using the Rietveld method, Rp = 0.0246, Rwp = 0.0325, R1 = 0.0521 and wR2 = 0.0770. Cuprodobrovolskyite is an isostructural analogue of dobrovolskyite Na4Ca(SO4)3 with Cu prevailing over Ca. One of the main features of cuprodobrovolskyite is Cu2+ in 7-fold coordination. On the basis of relationships with saranchinaite Na2Cu(SO4)2 and petrovite Na12Cu2(SO4)8 in the Arsenatnaya fumarole and the results of heating experiments, cuprodobrovolskyite is considered as the highest-temperature phase among anhydrous Na–Cu sulfate minerals.

Napoliite, ideally Pb2OFCl, is a new fluoroxychloride mineral found in a specimen from a fumarole formed subsequent to the 1944 eruption of Vesuvius volcano, Naples Province, Italy. It occurs as well-shaped lamellar crystals up to 0.25 × 0.25 × 0.01 mm typically forming clusters up to 0.4 × 0.4 mm on the surface of volcanic scoria in association with anglesite, artroeite, atacamite, calcioaravaipaite, cerussite, challacolloite, cotunnite, hephaistosite, manuelarossiite, matlockite and susannite. Napoliite is colourless with white streak and adamantine lustre. It is brittle and has a laminated fracture. Cleavage is perfect on {001}. Dcalc = 7.797 g cm–3. The calculated mean refractive index is 2.10. Chemical composition (wt.%, electron microprobe) is: PbO 91.71, F 3.89, Cl 7.34, –O=(F+Cl) –3.30, total 99.64. The empirical formula calculated on the basis of 3 anions is Pb1.999O0.997F0.996Cl1.007. Raman spectroscopy confirms the absence of OH– groups and H2O molecules in the mineral. Napoliite is tetragonal, space group P42/mcm, a = 5.7418(11), c = 12.524(4) Å, V = 412.9(2) Å3 and Z = 4. The strongest lines of the powder X-ray diffraction pattern [d, Å (I, %) (hkl)] are: 3.860 (85) (111); 3.139 (20) (004); 2.914 (100) (113); 2.866 (63) (200); 2.118 (19) (204); 2.027 (19) (220); 1.665 (20) (313); and 1.642 (23) (117). The crystal structure was refined to R1 = 0.024 for 222 reflections with F > 4σ(F). It is based on lead oxide blocks derived from that of litharge PbO, which alternate with layers of chloride ions. Napoliite represents a new structure type with a unique order/disorder pattern of fluorine and oxygen atoms. The new mineral is dimorphous with rumseyite. It is named after the city of Naples (Napoli in Italian).

The new mineral bakakinite, ideally Ca2V2O7, was found in the high-temperature (not lower than 500°C) exhalations of the Arsenatnaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It is associated with anhydrite, svabite, pliniusite, schäferite, berzeliite, diopside, hematite, powellite, baryte, fluorapatite, calciojohillerite, ludwigite, magnesioferrite, anorthite, titanite and esseneite. Bakakinite forms flattened crystals up to 30 × 5 μm, typically distorted. The mineral is transparent, colourless or pale yellow, with strong vitreous lustre. Electron microprobe analysis gave (wt.%): CaO 37.04, SrO 0.26, SiO2 0.16, P2O5 1.48, V2O5 49.47, As2O5 10.85, SO3 0.35, total 99.61. The empirical formula calculated on the basis of 7 O apfu is (Ca1.99Sr0.01)Σ2.00(V1.64As0.28P0.06Si0.01S0.01)Σ2.00O7. The Dcalc is 3.463 g cm–3. Bakakinite is triclinic, P$\bar{1}$, unit-cell parameters are: a = 6.64(2), b = 6.92(2), c = 7.01(2) Å, α = 86.59(7), β = 63.77(7), γ = 83.47(6)°, V = 287.0(5) Å3 and Z = 2. The strongest reflections of the powder X-ray diffraction pattern [d,Å(I)(hkl)] are: 4.647(27)(111, 0$\bar{1}$1), 3.138(76)(002), 3.103(100)(120, 121), 3.027(20)(021), 2.960(81)(200), 2.158(19)(031, 302), 1.791(16)(320), 1.682(16)(114) and 1.584(17)(1$\bar{3}$3, 403). Bakakinite is a natural analogue of synthetic Ca2V2O7. The mineral is named in honour of the outstanding Russian crystallographer and crystal chemist Vladimir Vasilievich Bakakin (born 1933).

The new alluaudite-group mineral khrenovite with the ideal, end-member formula Na3Fe3+2(AsO4)3 was found in the Arsenatnaya fumarole, Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It is associated with aphthitalite-group sulfates, badalovite, calciojohillerite, nickenichite, johillerite, tilasite, svabite, achyrophanite, ozerovaite, pansnerite, arsenatrotitanite, anhydrite, sanidine, hematite, cassiterite, rutile and pseudobrookite. Khrenovite occurs as coarse prismatic crystals up to 0.2 × 0.3 × 0.8 mm and their clusters up to 1 mm across. It is transparent, honey-coloured, red-, orange- or yellow-brown, with vitreous lustre. Khrenovite is brittle, cleavage was not observed. Dcalc is 4.257 g cm–3. Khrenovite is optically biaxial (+), α = 1.825(7), β = 1.834(7), γ = 1.845(7) and 2Vmeas. = 80(10)°. The chemical composition (wt.%, electron-microprobe) is: Na2O 11.47, K2O 1.23, CaO 0.18, MgO 0.01, MnO 4.10, CuO 4.27, ZnO 1.99, Al2O3 0.17, Fe2O3 21.12, SiO2 0.08, P2O5 0.01, V2O5 0.10, As2O5 56.03, SO3 0.02, total 100.78. The empirical formula calculated on the basis of 12 O apfu is (Na2.26K0.16Ca0.02Mn0.35Cu0.33Zn0.15Al0.02Fe3+1.62)Σ4.91(As2.98Si0.01V0.01)Σ3.00O12. Khrenovite is monoclinic, C2/c, a = 12.2394(7), b = 12.7967(5), c = 6.6589(4) Å, β = 112.953(7)°, V = 960.37(10) Å3 and Z = 4. The crystal structure was solved from single-crystal X-ray diffraction data with R1 = 0.0287. Khrenovite is isostructural with other alluaudite-group minerals. Its structural formula simplified to the species-defining constituents is A(1)NaA(2)’NaM(1)NaM(2)Fe3+2(TAsO4)3. The mineral is named in honour of the Russian volcanologist and geologist Anatoly Petrovich Khrenov (1946–2016).

Reznitskyite, ideally CaMg(VO4)F, is a new mineral species of the tilasite group from the Arsenatnaya fumarole, Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It occurs as zones (usually up to 0.05 mm thick) in crystals of V- and P-containing tilasite or as homogeneous grains up to 0.1 mm across. It was found in polymineralic sublimate encrustations in association with minerals of the svabite–fluorapatite–pliniusite system and the schäferite–berzeliite, tilasite–isokite, wagnerite–arsenowagnerite and udinaite–arsenudinaite series. The mineral assemblage also includes calciojohillerite, diopside, forsterite, titanite, rhabdoborite-(V), rhabdoborite-(W), rhabdoborite-(Mo), ludwigite, powellite, scheelite, hematite, baryte and magnesioferrite. Reznitskyite is transparent or semi-transparent, colourless, with vitreous lustre. Dcalc. = 3.453 g cm–3. Under the microscope, in reflected light reznitskyite is grey, non-pleochroic, with very weak bireflectance (ΔR589 nm = 0.5%) and distinct anisotropy. Reznitskyite is the first vanadate with a titanite-type structure. It is monoclinic, space group C2/c, a = 6.6912(7), b = 8.9395(7), c = 7.0587(8) Å, β = 113.078(13)°, V = 388.43(8) Å3 and Z = 4. The strongest reflections of the powder X-ray diffraction pattern are [d in Å(I)(hkl)]: 3.082(100)(200), 3.250(66)($\bar{1}$12, 002), 2.631(44)(022), 2.854(34)($\bar{2}$02), 2.683(33)(130), 3.686(26)(021), 2.531(25)(220), 1.749(25)($\bar{3}$32, $\bar{2}$04) and 2.344(24)(131). Electron microprobe analysis gave (wt.%) MgO 20.44, CaO 26.83, P2O5 6.24, V2O5 21.09, As2O5 18.97, SO3 0.47, F 9.42, –O=F –3.97, with a total of 99.49. The empirical formula of reznitskyite, calculated on the basis of O+F = 5 atoms per formula unit, is: Ca0.97Mg1.03(V0.47As0.33P0.18S0.01)Σ0.99O3.99F1.01. Reznitskyite is a vanadate analogue of tilasite CaMg(AsO4)F and isokite CaMg(PO4)F. The mineral is named in honour of the outstanding Russian mineralogist Leonid Zinovievich Reznitsky (born 1938) who has made significant contribution to the mineralogy of vanadium.

Calciolangbeinite, ideally K2Ca2(SO4)3, exists in two modifications, cubic and, first described in the present paper, orthorhombic. They are topologically-similar polymorphs which can be designated as calciolangbeinite-C and calciolangbeinite-O. Calciolangbeinite-O is the first natural orthorhombic langbeinite-like sulfate. It clearly differs from calciolangbeinite-C in the powder X-ray diffraction pattern, optical data and Raman spectrum. Calciolangbeinite-O is found in sublimates of the active Arsenatnaya fumarole at the Tolbachik volcano, Kamchatka, Far Eastern Region, Russia and in pyrometamorphic rocks of the Hatrurim Complex at Jabel Harmun, Judean Desert, Palestinian Autonomy and Har Parsa, Negev Desert, both in Israel. Calciolangbeinite-C is known only in fumarole sublimates at Tolbachik. Calciolangbeinite forms a continuous solid-solution system with langbeinite K2Mg2(SO4)3. The majority of the system is represented by cubic phases, and only members with compositions K2(Ca2.0–1.9Mg0.0–0.1)(SO4)3 have orthorhombic symmetry under room-temperature conditions. The crystal structure of calciolangbeinite-O was studied on a single crystal, chemically very close to K2Ca2(SO4)3, from Tolbachik (R1 = 2.75%). The unit-cell parameters are: a = 10.3330(2), b = 10.5027(2), c = 10.1763(2) Å, V = 1104.37(4) Å3 and Z = 4; space group is P212121. Calciolangbeinite-O is a low-temperature modification of K2Ca2(SO4)3 belonging to the K2Cd2(SO4)3 structure type whereas calciolangbeinite-C (space group P213), a high-temperature modification, has the langbeinite-type structure. The significant Mg admixture in calciolangbeinite-C from Tolbachik probably stabilises its cubic structure at room temperature. In both high-temperature fumaroles and pyrometamorphic rocks calciolangbeinite crystallises in the cubic modification, and during cooling its chemical variety close to the end-member K2Ca2(SO4)3 undergoes phase transition to calciolangbeinite-O, whereas the Mg-enriched varieties of the mineral remain calciolangbeinite-C.

The new alluaudite-group mineral paraberzeliite was found in the Arsenatnaya fumarole, Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. In the deepest zone of Arsenatnaya, paraberzeliite (holotype) is associated with anhydrite, diopside, hematite, svabite, berzeliite, schäferite, calciojohillerite, magnesioferrite, ludwigite, fluorapatite, powellite, baryte, and rhabdoborite-group and aphthitalite-group members. In the middle zone of the fumarole, paraberzeliite occurs with hematite, calciojohillerite, badalovite, johillerite, nickenichite, tilasite, svabite, fluorophlogopite, sanidine, cassiterite, anhydrite, metathénardite and belomarinaite. Paraberzeliite forms prismatic crystals up to 0.2 mm × 0.2 mm × 1 mm often occurring in open-work aggregates. It is transparent, brown (from light to dark brown, sometimes with purple or red hue) or green (from pale greenish to yellow–green). The mineral is brittle, cleavage was not observed. The Mohs hardness is 3½. Dcalc is 3.811 g cm–3. Paraberzeliite is optically biaxial (+), α = 1.718(4), β = 1.728(4), γ = 1.742(4) and 2Vmeas. = 85(5)°. The chemical composition (wt.%, electron-microprobe; holotype) is: Na2O 6.43, CaO 16.65, MgO 11.64, MnO 1.65, CuO 0.06, Fe2O3 2.45, V2O5 1.10, As2O5 59.46, total 99.44. The calculated empirical formula based on 12 O atoms per formula unit is (Na1.20Ca1.71Mg1.66Mn0.13Fe3+0.18)Σ4.88(As2.98V0.07)Σ3.05O12. Paraberzeliite is monoclinic, C2/c, a = 12.3143(7), b = 13.0679(5), c = 6.7717(4) Å, β = 113.657(7)°, V = 998.14(10) Å3 and Z = 4. The crystal structure was solved from single-crystal X-ray diffraction data, R = 0.0349. Paraberzeliite is isostructural with other alluaudite-group minerals. Its simplified crystal chemical formula is A(1)CaA(2)'NaM(1)CaM(2)Mg2(TAsO4)3. The idealised formula is NaCa2Mg2(AsO4)3, or, according to the actual nomenclature of alluaudite-group arsenates, NaCaCaMg2(AsO4)3. The name paraberzeliite reflects the dimorphism of this alluaudite-group mineral with the arsenate garnet berzeliite, ideally (Ca2Na)Mg2(AsO4)3.

The new beudantite-group mineral oberwolfachite, ideally SrFe3+3(AsO4)(SO4)(OH)6, was discovered in two localities: Clara mine, Oberwolfach, Schwarzwald, Baden-Württemberg, Germany (holotype) and Monterniers mine, Lantignié, Rhône, Auvergne-Rhône-Alpes, France (cotype). The associated minerals are quartz, baryte, hematite, illite, goethite, beudantite and dussertite (Clara) and arsenogoyazite, jarosite, graulichite-(Ce), goethite and hematite (Monterniers). Oberwolfachite forms yellow to brown platy crystals up to 1 mm across or thick outer zones of mixed (oberwolfachite–beudantite) crystals up to 3 mm across. The lustre is adamantine and the streak is yellow. A distinct cleavage on {0001} is observed. Calculated density is 3.874 g⋅cm–3. The infrared spectra are given. The chemical composition of the holotype/cotype samples are (wt.%, b.d.l. = below detection limit): K2O 1.25/1.86, SrO 6.41/11.15, BaO 8.13/0.45, PbO 2.18/b.d.l., Al2O3 0.16/0.23, Fe2O3 38.99/39.98, La2O3 1.68/not determined, Ce2O3 1.28/2.06, P2O5 0.12/b.d.l., As2O5 17.55/16.55, SO3 12.86/14.99, H2O (calculated) 8.72/9.05, total 99.33/96.62. The empirical formula of the holotype sample is (Sr0.38Ba0.33K0.16Pb0.06La0.06Ce0.05)Σ1.04(Fe3+3.03Al0.02)Σ3.05[(SO4)1.00(AsO4)0.95(PO4)0.01](O6.16H6.00). The crystal structures of both samples were determined using single-crystal X-ray diffraction data and refined to R = 3.13% (holotype, 293 K) and 2.65% (cotype, 170 K). Oberwolfachite is trigonal, R${\bar 3}$m, with a = 7.3270(3) Å, c = 17.0931(9) Å and V = 794.70(8) Å3 (holotype), and a = 7.298(2) Å, c = 16.908(3) Å and V = 779.8(4) Å3 (cotype); Z = 3. The strongest lines of the powder X-ray diffraction pattern of holotype [d, Å (I, %)(hkl)] are: 5.95 (56)(101), 3.664 (37)(110), 3.117 (16)(021), 3.082 (100)(113), 2.548 (15)(024), 2.280 (22)(107), 1.983 (26)(303) and 1.832 (19)(220).

The new alluaudite-group mineral calciojohillerite is one of the major arsenates in sublimates of the Arsenatnaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. In middle zones of the fumarole, calciojohillerite is associated with hematite, tenorite, johillerite, nickenichite, bradaczekite, badalovite, tilasite, lammerite, ericlaxmanite, aphthitalite-group sulfates, langbeinite, calciolangbeinite, anhydrite, sanidine, fluorophlogopite, fluoborite, cassiterite, pseudobrookite, rutile, sylvite and halite. In deep zones it occurs in association with anhydrite, diopside, hematite, svabite, berzeliite, schäferite, forsterite, magnesioferrite, ludwigite, rhabdoborite-group fluoroborates, powellite, baryte, fluorapatite, udinaite, arsenudinaite and paraberzeliite. Calciojohillerite forms prismatic crystals up to 1 cm long, their aggregates and crystal crusts up to 0.5 m2. It is transparent, colourless, pale green, pale yellow, light blue, pale lilac or pink, with vitreous lustre. The mineral is brittle, with imperfect cleavage. The Mohs hardness is 3½. Dcalc is 3.915 g cm–3. Calciojohillerite is optically biaxial (–), α = 1.719(3), β = γ = 1.732(3); 2Vmeas. = 15(10)°. Chemical composition (wt.%, electron-microprobe; holotype) is: Na2O 7.32, K2O 0.10, CaO 6.82, MgO 20.31, MnO 0.68, CuO 0.27, ZnO 0.02, Al2O3 0.56, Fe2O3 3.53, TiO2 0.01, SiO2 0.03, P2O5 1.25, V2O5 0.10, As2O5 58.77, SO3 0.13, total 99.90. The empirical formula based on 12 O atoms is (Na1.30K0.01Ca0.67Mg2.78Mn0.05Cu0.02Al0.06Fe3+0.24)Σ5.13(As2.83P0.10S0.01V0.01)Σ2.95O12. Calciojohillerite is monoclinic, C2/c, a = 11.8405(3), b = 12.7836(2), c = 6.69165(16) Å, β = 112.425(3)°, V = 936.29(4) Å3 and Z = 4. The crystal structure was solved from single-crystal X-ray diffraction data, R1 = 0.0227. Calciojohillerite is isostructural with other alluaudite-group minerals. Its simplified crystal chemical formula is A(1)CaA(1)′□A(2)□A(2)′NaM(1)MgM(2)Mg2(AsO4)3 (□ = vacancy). The idealised formula is NaCaMg3(AsO4)3, or, according to the nomenclature of alluaudite-group arsenates, NaCaMgMg2(AsO4)3. Calciojohillerite is named as an analogue of johillerite NaCu2+MgMg2(AsO4)3 with species-defining Ca instead of Cu in the ideal formula.

The rhodonite-group mineral with the idealised, end-member formula MnMn4[Si5O15] and the crystal chemical formula VIIM(5)MnVIM(1–3)Mn3VIIM(4)Mn[Si5O15] (Roman numerals indicate coordination numbers) is defined as a valid mineral species named vittinkiite after the type locality Vittinki (Vittinge) mines, Isokyrö, Western and Inner Finland Region, Finland. Vittinkiite is an isostructural analogue of rhodonite, ideally CaMn4[Si5O15], with Mn2+ > Ca at the M(5) site. Besides Vittinki, vitiinkiite was found in more than a dozen rhodonite deposits worldwide, however, it is significantly less common in comparison with rhodonite. The mineral typically forms pink to light pink massive, granular aggregates and is associated with quartz, rhodonite, tephroite, pyroxmangite and Mn oxides. Vittinkiite is optically biaxial (+), with α = 1.725(4), β = 1.733(4), γ = 1.745(5) and 2Vmeas = 75(10)° (589 nm). The chemical composition of the holotype (wt.%, electron microprobe) is: MgO 0.52, CaO, 0.93, MnO 51.82, FeO 1.26, ZnO 0.11, SiO2 46.48, total 101.12. The empirical formula calculated based on 15 O apfu is Mn4.71Ca0.11Fe0.11Mg0.08Zn0.01Si4.99O15. Vittinkiite is triclinic, space group P$\bar{1}$, with a = 6.6980(3), b = 7.6203(3), c = 11.8473(5) Å, α = 105.663(3), β = 92.400(3), γ = 94.309(3)°, V = 579.38(7) Å3 and Z = 2. The crystal structure is solved on a single crystal to R1 = 3.85%. Polymorphism of MnSiO3 (rhodonite-, pyroxmangite-, garnet- and clinopyroxene-type manganese metasilicates) is discussed, as well as the relationship between vittinkiite and pyroxmangite, ideally Mn7[Si7O21], and the application of infrared spectroscopy for the identification of manganese pyroxenoids.

The new alluaudite-group mineral badalovite was found in the Arsenatnaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It is associated with hematite, tenorite, cassiterite, johillerite, nickenichite, calciojohillerite, bradaczekite, metathénardite, aphthitalite, langbeinite, calciolangbeinite, sanidine, fluorophlogopite, fluoborite, tilasite, anhydrite, pseudobrookite, sylvite, halite, lammerite, urusovite, ericlaxmanite, arsmirandite, svabite, krasheninnikovite, euchlorine, wulffite and alumoklyuchevskite. Badalovite forms oblique-angled prismatic crystals up to 1 mm × 1 mm × 5 mm, typically combined in groups or crusts up to several hundred cm2 in area. The mineral is transparent, green, grey, yellow or colourless, with vitreous lustre. It is brittle, the Mohs hardness is 3½. Cleavage was not observed, the fracture is uneven. Dcalc is 4.02 g cm–3. Badalovite is optically biaxial (–), α = 1.753(3), β = 1.757(3), γ = 1.758(3) and 2Vmeas. = 50(10)°. Chemical composition (wt.%, electron-microprobe; holotype) is: Na2O 9.23, K2O 0.19, CaO 2.04, MgO 13.78, MnO 0.31, CuO 0.12, ZnO 0.24, Al2O3 0.06, Fe2O3 12.77, TiO2 0.01, SiO2 0.06, P2O5 0.33, V2O5 0.05, As2O5 61.51, SO3 0.02, total 100.72. The empirical formula based on 12 O apfu is Na1.67Ca0.20K0.02Mg1.92Zn0.02Mn0.02Cu0.01Fe3+0.90Al0.01(As3.01P0.03Si0.01)Σ3.05O12. The simplified formula is Na2Mg2Fe3+(AsO4)3. Badalovite is monoclinic, C2/c, a = 11.9034(3), b = 12.7832(2), c = 6.66340(16) Å, β = 112.523(3)°, V = 936.59(4) Å3 and Z = 4. The strongest reflections of the powder XRD pattern [d,Å(I)(hkl)] are: 6.41(38)(020), 5.505(20)(200), 3.577(23)($\bar{1}$31), 3.523(25)(310), 3.211(46)($\bar{1}$12), 2.911(28)($\bar{2}$22, $\bar{3}$12), 2.765(100)(240, 400) and 2.618(26)($\bar{1}$32). The crystal structure was solved from single-crystal XRD data with an R1 of = 2.49%. Badalovite is isostructural with other alluaudite-group minerals. Its simplified crystal chemical formula is A(1)NaA(1)’□A(2) □A(2)’NaM(1)MgM(2)(Mg0.5Fe3+0.5)2(AsO4)3 (□ – vacancy) and the end-member formula is NaNaMg(MgFe3+)(AsO4)3. The mineral is named in honour of the outstanding mineralogist and geochemist Stepan Tigranovich Badalov (1919–2014).

The new mineral pansnerite, ideally K3Na3Fe3+6(AsO4)8, was found in the Arsenatnaya fumarole at the Second scoria cone of the Northern Breakthrough of the Great Tolbachik Fissure Eruption, Tolbachik volcano, Kamchatka, Russia. It is associated with aphthitalite, hematite, sanidine, badalovite, khrenovite, achyrophanite, arsenatrotitanite, ozerovaite, tilasite, calciojohillerite, johillerite, nickenichite, svabite, katiarsite, yurmarinite, anhydrite, rutile, cassiterite and pseudobrookite. Pansnerite forms tabular to lamellar (flattened on {010}), usually pseudo-hexagonal crystals up to 0.2 mm × 0.7 mm × 1 mm and crystal clusters up to 2 mm across. It is transparent to translucent, light green, pale greenish, yellowish–greenish or yellowish, with vitreous lustre. The mineral is brittle, with perfect {010} cleavage. The Mohs’ hardness is ca 3. Dcalc is 3.596 g cm–3. Pansnerite is optically biaxial (–), α = 1.702(4), β = 1.713(4), γ = 1.717(4), 2Vmeas = 45(10)° and 2Vcalc = 62°. Chemical composition (holotype, wt.%, electron microprobe data) is: Na2O 6.39, K2O 8.52, CaO 0.08, MgO 0.08, MnO 0.02, NiO 0.02, CuO 1.35, ZnO 0.34, Al2O3 7.35, Cr2O3 0.04, Fe2O3 16.72, SiO2 0.16, P2O5 0.22, V2O5 0.09, As2O5 57.76, SO3 0.04, total 99.20. The empirical formula based on 32 O apfu is K2.86Na3.26Ca0.02(Fe3+3.31Al2.28Cu0.27Zn0.07Mg0.03Cr0.01)Σ5.97(As7.95P0.05Si0.04V0.02S0.01)Σ8.06O32. Pansnerite is orthorhombic, Cmce, a = 10.7372(3), b = 20.8367(8), c = 6.47335(15) Å, V = 1448.27(7) Å3 and Z = 2. The strongest reflections of the X-ray powder diffraction pattern [d,Å(I)(hkl)] are: 10.49(100)(020), 5.380(88)(111), 4.793(65)(220), 3.105(46)(311, 002), 3.079(32)(112, 061), 2.932(35)(260), 2.783(65)(202) and 2.694(52)(400, 222). The crystal structure was solved from single-crystal X-ray diffraction data, R1 = 2.82%. The structure is based on heteropolyhedral layers formed by MO6 octahedra (M = Fe3+ and Al) sharing common vertices and connected by AsO4 tetrahedra. Na+ and K+ cations are located in the interlayer space. The mineral is named in honour of the German–Russian mineralogist and geographer Lavrentiy Ivanovich Pansner (1777–1851). Pansnerite forms a solid-solution series with the isotypic mineral ozerovaite, ideally KNa2Al3(AsO4)4.

The new mineral antofagastaite, ideally Na2Ca(SO4)2·1.5H2O, was found in the oxidation zone of sulfide–quartz veins at the abandoned Coronel Manuel Rodríguez mine, Mejillones, Antofagasta Province, Antofagasta Region, Chile. It is associated with sideronatrite, metasideronatrite, aubertite, gypsum, ferrinatrite, glauberite, amarillite and an unidentified Fe phosphate. Antofagastaite occurs as prismatic crystals up to 0.5 mm × 1 mm × 5 mm, elongated along [010], typically combined in open-work aggregates up to 1 cm across. Antofagastaite is transparent and colourless, with vitreous lustre. It is brittle; the Mohs’ hardness is ca 3. Cleavage is distinct on (001). Dmeas. is 2.42(1) and Dcalc. is 2.465 g cm−3. Antofagastaite is optically biaxial (–), α = 1.489(2), β = 1.508(2), γ = 1.510(2) and 2Vmeas. = 40(10)°. The IR spectrum is reported. Chemical composition (wt.%, electron microprobe, H2O determined by gas chromatography) is: Na2O 20.85, CaO 17.42, SO3 52.56, H2O 7.93, total 98.76. The empirical formula (based on 8 O atoms belonging to sulfate anions per formula unit with all H belonging to H2O molecules) is Na2.06Ca0.95S2.01O8·1.35H2O. Antofagastaite is monoclinic, P21/m, a = 6.4596(4), b = 6.8703(5), c = 9.4685(7) Å, β = 104.580(4)°, V = 406.67(5) Å3 and Z = 2. The strongest reflections of the powder XRD pattern [d, Å (I, %) (hkl)] are: 9.17 (100) (001), 5.501 (57) (011), 3.437 (59) (020), 3.058 (43) (003), 2.918 (50) (2¯11), 2.795 (35) (013) and 2.753 (50) (121, 201). The crystal structure was solved based on single-crystal X-ray diffraction data, R1 = 5.71%. The structure of antofagastaite consists of ordered and disordered blocks and is related to syngenite K2Ca(SO4)2·H2O. Incorporation of additional H2O molecules in the syngenite-type structure results in disorder of the one of the two tetrahedral sulfate groups occurring in antofagastaite. In addition to the above-reported type material, antofagastaite together with syngenite and blödite occurs in the Arsenatnaya fumarole, Tolbachik volcano, Kamchatka, Russia.