Sample geometry effects on mechanical strengths of gold micro-cantilevers are evaluated by a micro-bending test. Six micro-cantilevers with the same length of 50 μm are prepared, and the width and the thickness are varied to examine individual effects on the yield stress. The yield stress increases from 428 to 519 MPa when the thickness decreases from 11.1 to 6.0 μm. No obvious dependency is observed when varying the width. The results reveal that the thickness and the width each has a different influence on the yield stresses of micro-cantilevers evaluated by the bending test, which is the sample geometry effect.

Mechanical behavior of ultra-fine grained (UFG) steel fabricated by high pressure torsion (HPT) was investigated by micro-sized compression test of a micro-sized pillar with uniform dimensions (non-tapered, non-filleted) carefully fabricated by FIB milling. After HPT process, grains were elongated to shear direction and its grain size was decreased down to 300 nm in diameter with increasing strain amount. Compression test confirmed that the uniform elongations of ultra-fine grained materials were lower than 3% and do not depend on the grain size.