The effect of temperature on grinding-induced texture in tetragonal lead titanate (PT) has been investigated as a function of the magnitude of loading applied to the sample surface during grinding, using in situ x-ray diffraction (XRD) with an area detector. Compared to the ground PT under lower loading conditions (5 N), the ground PT under higher loading conditions (40 N) retains strong ferroelastic texture near the Curie temperature (TC) around 350 °C and undergoes smaller changes in lattice parameter or tetragonality versus temperature during in situ thermal cycling between room temperature and approximately 100 °C above the TC. Inhibited depoling of ground PT materials investigated by in situ texture measurements demonstrates the effects of residual stresses.

The effect of temperature on grinding-induced texture in tetragonal lead zirconate titanate (PZT) and lead titanate (PT) has been investigated using in situ x-ray diffraction (XRD) with an area detector. In contrast with previous results on electrical poling, mechanically-ground PT and soft PZT materials retain strong ferroelastic textures during thermal cycling, even after excursions to temperatures slightly above the Curie temperature. The relationship between the residual stresses in the surface region, caused by grinding, and those resulting from domain wall motion is elucidated by in situ texture measurements obtained during thermal cycling.