Engineering of a novel heterostructured oxide interface was used to enhance the oxygen surface exchange kinetics of La0.6Sr0.4Co0.2Fe0.8O3−δ (LSCF113) thin films. A single-layer decoration of mixed (LaSr)2CoO4±δ (LSC214) and La1−x Srx CoO3−δ (LSC113) and a double-layer decoration of stacked LSC214 and LSC113 grown on the LSCF113 markedly enhanced the surface exchange coefficients of the LSCF113 by up to ~1.5 orders of magnitude relative to the undecorated LSCF113. It is hypothesized that two different types of surface decorations can enable Sr segregation at the interface and surfaces of LSC113 and LSC214, leading to enhancement of the oxygen surface exchange kinetics of decorated LSCF113.

Nanostructured thermoelectric materials have attracted lots of interest in recent years, due to their enhanced performance determined by their thermoelectric dimensionless figure of merit. However, because of equipment limitations, not much work has been done on combining simultaneous transport measurements and structural characterization on individual nanostructured thermoelectric materials. With an integrated TEM-STM system, we studied the structural behavior and electrical properties of bismuth (Bi) nanobelts and nanoparticles. Results showed that clean Bi nanostructures free of oxides can be produced by in-situ high temperature electro-migration and Joule annealing processes occurring within the electron microscope. Preliminary electrical measurements indicate a conductivity of two orders of magnitude lower for Bi nanoparticles than that for bulk Bi. Such in-situ studies are highly advantageous for studying the semimetal-semiconductor transition and how this transition could enhance thermoelectric properties.