We reported on an efficient high-power continuous-wave laser operation on the 3H4 → 3H5 transition of Tm3+ ions in a diffusion-bonded composite YVO4/Tm:GdVO4 crystal. Pumped by a laser diode at 794 nm, a maximum output power of 7.5 W was obtained from a YVO4/Tm:GdVO4 laser at 2.29 μm, corresponding to a slope efficiency of 40.3% and exceeding the Stokes limit. To the best of our knowledge, this result represents the maximum power ever achieved from a Tm laser at 2.3 μm.

We report on a power-scalable sub-100-fs laser in the 2-μm spectral range using a Tm3+-doped ‘mixed’ (Lu,Sc)2O3 sesquioxide ceramic as an active medium. Pulses as short as 58 fs at 2076 nm with an average output power of 114 mW at a pulse repetition rate of approximately 82.9 MHz are generated by employing single-walled carbon nanotubes as a saturable absorber. A higher average power of 350 mW at 2075 nm is obtained at the expense of the pulse duration (65 fs). A maximum average power of 486 mW is achieved for a pulse duration of 98 fs and an optical conversion efficiency of 22.3%, representing the highest value ever reported from sub-100-fs mode-locked Tm lasers.