Arsenoústalečite, Cu12(As2Te2)Se13, a new mineral, and crystal structures of arsenoústalečite and stibioústalečite

Abstract Arsenoústalečite is a new mineral discovered in a sample collected from the abandoned Ústaleč deposit near Horažďovice, SW Bohemia, Czech Republic. It occurs as rare anhedral grains, up to 40 μm in size, in a calcite gangue, associated with stibioústalečite, hakite-(Hg), berzelianite and uraninite. Arsenoústalečite is dark grey, with a metallic lustre. Mohs hardness is ca. 3½–4; calculated density is 5.730 g/cm3. In reflected light, arsenoústalečite is pale grey with a yellowish shade; it is isotropic. Internal reflections were not observed. Reflectance values for the four COM wavelengths in air [R (%) λ (nm)] are: 33.3 (470); 33.1 (546); 33.0 (589); and 32.9 (650). The empirical formula of arsenoústalečite is (Cu5.81Ag0.17)Σ5.98(Cu5.95Fe0.02Zn0.02Hg0.01)Σ6.00(As1.40Sb0.87Te1.73)Σ4.00(Se10.30S2.32)Σ12.61. The ideal formula is Cu12(As2Te2)Se13, which requires (in wt.%) Cu 34.76, As 6.83, Te 11.63, Se 46.78, total 100.00. Arsenoústalečite is cubic, I$\bar{4}$3m, with unit-cell parameters a = 10.6580(19) Å, V = 1210.7(6) Å3 and Z = 2. The strongest reflections of the calculated powder X-ray diffraction pattern [d, Å (I, %) hkl] are: 3.077 (100) 222, 2.848 (10) 321, 1.946 (12) 521, 1.884(52) 440 and 1.608(21) 622. According to the single-crystal X-ray diffraction data (R1 = 0.0285 on the basis of 334 unique reflections with Fo > 4σFo and 24 refined parameters), arsenoústalečite is isotypic with other tetrahedrite-group minerals. The crystal structure of co-existing stibioústalečite, with an empirical formula of (Cu5.69Ag0.07)Σ5.76(Cu5.80Zn0.13Fe0.06Hg0.01)Σ6.00(Sb1.82As0.42Te1.76)Σ4.00(Se9.52S3.10)Σ12.62 and unit-cell parameters a = 10.6975(16) Å, V = 1224.2(5) Å3 and Z = 2, was refined to R1 = 0.0191 on the basis of 267 unique reflections with Fo > 4σFo and 24 refined parameters. Structural relationships and crystal-chemistry of both members of the ústalečite series are discussed. Arsenoústalečite is named after its type locality, the Ústaleč deposit and its chemical composition. The mineral and its name have been approved by the Commission on New Minerals, Nomenclature and Classification of the International Mineralogical Association (IMA2022-116).

Within this group, members of the tetrahedrite and tennantite series are the most common, whereas species having Se as the dominant anion or Te as the D chemical constituent are rare or very rare.Indeed, Se and Te are two among the chemical constituents of tetrahedrite-group minerals showing the lowest concentration in the Earth's continental crust, i.e. 120 and 5 ng/g, respectively (Wedepohl, 1995).Cadmium (100 ng/g), Ag (70 ng/g), In (50 ng/g) and Hg (40 ng/g) are rarer than Se (Wedepohl, 1995), but some of them (Ag and Hg) are particularly widespread in hydrothermal environments and are able to become dominant constituents.As discussed by Christy (2015), Ag and Hg, as well as Se, can be considered as anomalously abundant elements, whereas Cd and In are dispersed elements, owing to their geochemical behaviour.Tellurium is exceptional, being concentrated in more than 150 different mineral species notwithstanding its extreme low abundance in Nature (Christy, 2015).
Tellurium-rich members of the tetrahedrite group have been known for a long time.The first descriptions of goldfieldite were given by Sharwood (1907) and Ransome (1909).Thompson (1946) proved this mineral to be isotypic with tetrahedrite.Kato and Sakurai (1970) and Kalbskopf (1974) found that Te does not substitute for S but replaces Sb and As.Several authors have debated the actual definition of goldfieldite (e.g.Trudu and Knittel, 1998) and the debate was finally solved in the nomenclature of the tetrahedrite group by Biagioni et al. (2020).Increased Se-contents in Te-rich members was, until recently, only known in samples from the epithermal Au deposits in Kamchatka, Russia (Spiridonov and Okrugin, 1985;Pohl et al., 1996;Spiridonov et al., 2014), and from the Wild Dog epithermal Au system on Bougainville Island, Papua New Guinea (Noviello, 1989).In these findings, Se does not exceed 3.0 atoms per formula unit (apfu).The experiments carried out at 340°C by de Medicis and Giasson (1971) on the system Cu-Te-Se failed to produce the Se-bearing analogues of goldfieldite.The first Se-and Te-dominant member of the tetrahedrite group, stibioústalečite, was described from a selenide association from the Ústaleč mine near Horažďovice (Czech Republic) by Sejkora et al. (2022).In this association, a mineral with As > Sb, i.e. the As-analogue of stibioústalečite, was also detected (Sejkora et al., 2022).Further chemical and crystallographic investigations confirmed such a preliminary identification, allowing the proposal of the new mineral species arsenoústalečite.
This new mineral and its name (symbol Aúč) were approved by the Commission on New Minerals, Nomenclature and Classification of the International Mineralogical Association (IMA2022-116).Arsenoústalečite ('arseno-oostaletchite') is named after its type locality, the Ústaleč deposit near Horažďovice, Czech Republic, and its chemical composition, being the (As/ Te) end-member in the ústalečite series.The holotype material (polished section) is deposited in the mineralogical collection of the Department of Mineralogy and Petrology of the National Museum, Prague, Czech Republic (catalogue number P1P 7/2021).It is worth noting that it is the same type material containing stibioústalečite (Sejkora et al., 2022).The crystal used for the singlecrystal X-ray diffraction study is kept in the mineralogical collection of the Museo di Storia Naturale of the Università di Pisa, Via Roma 79, Calci (PI), Italy, under catalogue number 20026.
As the studied material also contained stibioústalečite, a grain of this recently approved species suitable for single-crystal X-ray diffraction study was sought and found in this investigation.In addition, Sejkora et al. (2022) had not been successful in refining the crystal structure of this species, owing to the extremely low diffraction intensities, resulting in a value of R int = 0.214.
In this paper the description of arsenoústalečite and details of the crystal structure of its Sb-isotype stibioústalečite are reported, along with discussion on some crystal-chemical and nomenclature issues.
The Ústaleč uranium deposit belongs to the Horažďovice uranium district and it is similar to several analogous ore deposits and occurrences including Újezd u Kasejovic, Nalžovské Hory, Těchonice and others.The hydrothermal uranium mineralisation is structurally controlled by the regional Horažďovice fault zone trending WNW-ESE.The deposit is hosted in metamorphic rocks of the Varied Group of the Moldanubian Complex at the contact with the Chanovice apophysis of the Central Bohemian Plutonic Complex (Litochleb et al., 1999).More details of the geological setting of the Ústaleč uranium deposit are given in Sejkora et al. (2022).
Arsenoústalečite was identified in the type material of stibioústalečite, represented by a sample of calcite gangue where it is associated with hakite-(Hg), stibioústalečite, berzelianite and uraninite.The crystallisation of arsenoústalečite is probably related to the circulation of low-temperature hydrothermal fluids during the late-stage evolution of the Ústaleč uranium deposit.

Physical and optical properties
Arsenoústalečite occurs as anhedral grains up to 40 μm in size and forms part (up to 100 μm in size) of arsenoústalečite/ stibioústalečite aggregates (Fig. 1).The mineral is dark grey in colour and opaque in transmitted light; it has a metallic lustre.The Mohs hardness is close to 3½-4, in agreement with other members of the tetrahedrite group.Arsenoústalečite is brittle, with an indistinct cleavage and a conchoidal fracture.Density was not measured, owing to the small amount of available material; on the basis of the empirical formula (Z = 2) and the single-crystal unit-cell parameters, the calculated density is 5.730 g/cm 3 .In reflected light, arsenoústalečite is isotropic, pale grey with a yellowish shade.Internal reflections were not observed.Reflectance spectra were measured in air with a TIDAS MSP400 spectrophotometer attached to a Leica microscope (50× objective) using a WTiC (Zeiss no.370) standard, with a square sample measurement field of ca. 10 × 10 μm.The results for the 400-700 nm range are given in Table 1 and plotted in Fig. 2 in comparison with data for members of the ústalečite and goldfieldite series.

X-ray diffraction data
Grains of arsenoústalečite and stibioústalečite were extracted from the polished section studied previously using electron microprobe analysis (Fig. 1) and mounted on a carbon fibre for examination with a Bruker D8 Venture single-crystal X-ray diffractometer equipped with an air-cooled Photon III area detector and microfocus MoKα radiation (Centro per l'Integrazione della Strumentazione Scientifica dell'Università di Pisa, University of Pisa).The detector-to-crystal distance was set to 38 mm for both samples and data were collected using w scan modes in 0.5°slices.Data were integrated with the Bruker SAINT software package using a narrow-frame algorithm and corrected for Lorentz-polarisation, absorption and background.The crystal structure of both arsenoústalečite and stibioústalečite were refined using Shelxl-2018 (Sheldrick, 2015), starting from the atomic coordinates of stibiogoldfieldite given by Biagioni et al. (2022).The following neutral scattering curves, taken from the International Tables for Crystallography (Wilson, 1992) were used: Cu vs. □ (vacancy) at M(2), Cu vs. □ at M(1), As vs. Te at X(3), Se vs. S at the S(1) and S(2) sites.The occurrence of racemic twinning was modelled.Crystal structure refinements are described below, whereas further details on data collection and refinement are given in Table 3. Fractional atom coordinates and equivalent isotropic parameters are reported in Table 4, whereas Table 5 shows selected bond distances.Weighted bond-valence sums, calculated using the bond-parameters of Brese and O' Keeffe (1991), are given in Table 6.For both arsenoústalečite and stibioústalečite, Crystallographic Information Files (CIF) have been deposited with the Principal Editor of Mineralogical Magazine and are available as Supplementary Materials.

Arsenoústalečite
Intensity data were collected using a short prismatic fragment, 25 × 20 × 20 μm in size.A total of 188 frames was collected with an exposure time of 40 s per frame.Unit-cell parameters, refined on the basis of the XYZ centroids of 699 reflections above 20 σI with 9.369 < 2θ < 59.87°, are a = 10.6580(19) and V = 1210.7(6)Å 3 .Several cycles of isotropic refinement, with full occupancies of Cu at M(2) and M(1), of Te at X(3), and Se at S(1) and S(2), converged to R 1 = 0.0873, thus indicating the correctness of the structural model.However, the Flack parameter (Flack, 1983) was 0.83( 16), thus indicating the necessity to invert the structure.At this stage of the refinement, a high maximum residual close to the M(2) position was found.After its addition as the split site M(2b), the R 1 value decreased to 0.0625, constraining the displacement parameter of the two sub-sites to be the same.The S(2) site showed a high U iso , thus indicating a significant replacement of Se by S. At this stage of refinement, the neutral scattering curves reported above were used, refining mixed occupancies at X(3), S(1) and S(2) sites.As chemical data indicated the occurrence of minor Ag, the site occupancies at M(2a) and M(2b) were freely refined but their sum did not deviate from the full occupancy by Cu.Similarly, the free refinement of the site occupancy at the M(1) site indicated the full occupancy by Cu.For this reason, the sum of site occupancies of M(2a) and M(2b) was constrained to be one, whereas the site occupancy at M(1) was fixed to one.The refinement of this isotropic structural model converged to R 1 = 0.0450.The anisotropic modelling of the displacement parameters of cation sites lowered the R 1 to 0.0308.At the final stage of refinement, a full anisotropic model was assumed.It converged to R 1 = 0.0285 for 334 reflections with F o > 4σ(F o ) and 24 refined parameters.
Powder X-ray diffraction data of arsenoústalečite could not be collected, due to the paucity of available material.Consequently, powder X-ray diffraction data, given in Table 7, were calculated  using the software PowderCell 2.3 (Kraus and Nolze, 1996) on the basis of the structural model given in Tables 3 and 4.

Stibioústalečite
Intensity data were collected using a short prismatic fragment, 35 × 20 × 15 μm in size.A total of 188 frames was collected with an exposure time of 30 s per frame.Unit-cell parameters, refined on the basis of the XYZ centroids of 842 reflections above 20 σI with 7.619 < 2θ < 54.813°, are a = 10.6975(16) and V = 1224.2(5)Å 3 .Several cycles of isotropic refinement, with full occupancies of Cu at M(2) and M(1), of Te at X(3), and Se at S(1) and S(2), converged to R 1 = 0.0686, thus indicating the correctness of the structural model.Also the Flack parameter (Flack, 1983), i.e. 0.04(15), indicated the goodness of the model.At this stage of the refinement, a relatively high maximum residual close to the M(2) position was found.After its addition as the split site M(2b), the R 1 value decreased to 0.0430, constraining the displacement parameters of the two sub-sites to be the same.The U iso at the S(2) site was too high, suggesting a significant replacement of Se by S. At this stage of refinement, mixed occupancies at X(3), S(1) and S(2) sites were refined.As chemical data indicated the occurrence of minor Ag at M(2), the site occupancies at M(2a) and M(2b) were freely refined but their sum did not deviate from the full occupancy by Cu.Analogously, the M(1) site was fully occupied by Cu.The refinement of this isotropic structural model converged to R 1 = 0.0287.The anisotropic modelling of the displacement parameters of cation sites lowered the R 1 to 0.0210.At the final stage of refinement, a full anisotropic model was assumed.It converged to R 1 = 0.0191 for 267 reflections with F o > 4σ(F o ) and 24 refined parameters.

Cation sites
The tetrahedrally coordinated M(1) site has an average bond distance of 2.410 Å in arsenoústalečite and 2.413 Å in stibioústalečite.These values are longer than the M(1)-S(1) distance observed in stibiogoldfieldite, i.e. 2.329 Å (Biagioni et al., 2022).The distances observed in the members of the ústalečite series are similar to the Cu-Se distance reported for other Cu-centred tetrahedra coordinated by Se, e.g.2.421 Å in eskebornite (Delgado et al., 1992).Electron microprobe data allows us to hypothesise the following site occupancies at the M(1) site of arsenoústalečite and stibioústalečite (with rounding errors): (Cu 0.992 Fe 0.003 Zn 0.003 Hg 0.002 ) and (Cu 0.967 Zn 0.022 Fe 0.010 Hg 0.001 ), respectively, corresponding to mean atomic numbers (MAN) of 29.10 and 29.04 electrons.In both cases, the site occupancy at M(1) site was refined as a pure Cu site, i.e. a MAN value of 29 electrons.Bond-valence sums at the M(1) site of arsenoústalečite and stibioústalečite are 1.32 and 1.36 valence units (vu) (Table 6).Such overbonding at the tetrahedrally coordinated site in tetrahedrite-group minerals is a well known feature (e.g.Welch et al., 2018).
As described above, in both arsenoústalečite and stibioústalečite, the M(2) site is split into two sub-positions, M(2a) and M(2b), separated by 1.00(3) Å in the former and 0.75(8) Å in the latter, with the distance of two neighbouring M(2b) positions of 1.99(6) Å and 1.51( 16) Å, respectively.The M(2b) positions are at 2.60(3) and 2.84(8) Å from the X(3) site.These distances are definitely longer than that reported by Makovicky et al. (2005) in Cu-rich unsubstituted tennantite, where a M(2b)-X(3) distance of 2.41 Å was observed, suggesting a possible interaction between the lone-pair electrons of As and Sb and the valence shells of Cu.The atom hosted at the M(2a) position shows a triangular planar coordination, whereas at M(2b) the coordination is a flat trigonal pyramid.In arsenoústalečite, average bond distances are 2.302 Å and 2.507 Å for M(2a) and M(2b), respectively; in its Sb-isotype such values are 2.310 Å and 2.42 Å, respectively.These values are larger than those observed in stibiogoldfieldite, having an average bond distance of 2.251 Å (Biagioni et al., 2022), owing to the replacement of S by Se.The M(2a) and M(2b) sub-sites were modelled as occupied by Cu only; indeed, minor Ag (∼0.03 and 0.01 atoms per site in arsenoústalečite and stibioústalečite, respectively) occurs.No detectable vacancy at these sites were observed.The sum of the bond-valence for M(2a) + M(2b) (Table 6) is 1.02 and 1.09 vu for arsenoústalečite and stibioústalečite, respectively, in agreement with the presence of monovalent Cu.
The X(3) site has an average bond distance of 2.484 Å and 2.526 Å in arsenoústalečite and stibioústalečite, respectively.In stibiogoldfieldite, the distance is 2.390 Å with the site occupancy (Sb 0.28 As 0.16 Bi 0.06 Te 0.50 ) (Biagioni et al., 2022).The refined MAN at the X(3) site of the As-and Sb-isotypes of the ústalečite series are 44.67 and 51.30 electrons, to be compared with those calculated from electron microprobe analyses, i.e. 45.13 and 49.64 electrons for arsenoústalečite and stibioústalečite, respectively, on the basis of the proposed site occupancies (As 0.35 Sb 0.22 Te 0.43 ) and (Sb 0.46 As 0.10 Te 0.44 ).Using the ideal bond valences and bond valence parameters of Brese and O'Keeffe (1991), the average distance of 2.43 Å and 2.48 Å can be calculated for arsenoústalečite and stibioústalečite, shorter than the observed ones.The weighted bond-valence sum at X(3), i.e. 3.00 and 3.03 vu for arsenoústalečite  1996) on the basis of the structural data given in Tables 3 and 4.Only reflections with I rel.≥ 1 are listed.The five strongest reflections are given in bold.
and stibioústalečite, are lower than the expected values based on the proposed site occupancies (Table 6).

Anion sites
The S(1) site is tetrahedrally coordinated by two M(1) site, one M(2) site [i.e.M(2a) or one of the two mutually exclusive M(2b) positions], and one X(3) site.The refined site occupancy at S(1) is Se 0.859 S 0.141 in arsenoústalečite and Se 0.935 S 0.065 in stibioústalečite, with bond-valence sums of 1.99 and 2.06 vu, respectively (Table 6).The S(2) site is octahedrally coordinated by six atoms hosted at M(2a)+M(2b).In both arsenoústalečite and stibioústalečite this site is S-dominant, with site occupancies S 0.69 Se 0.31 and S 0.74 Se 0.26 , respectively.This site is slightly overbonded, with bond-valence sums of 2.34 and 2.22 vu (Table 6), probably as a consequence of too short M(2)-Se distances.
It is interesting to compare the S/(S + Se) atomic ratios obtained through the crystal structure refinement with those measured through the electron microprobe analysis.In arsenoústalečite, electron microprobe data gave (Se 10.30 S 2.32 ) Σ12.61 , with a ratio of 0.184.Taking into account the site multiplicity, the anion content (Se 10.62 S 2.38 ) can be obtained from structural analysis, having a S/(S + Se) ratio of 0.183, in agreement with chemical data.In stibioústalečite, a higher S content was detected through electron microprobe analysis, with a S/(S + ratio of 0.246.Crystal structure refinement points to an undeniably lower ratio, 0.118; in type stibioústalečite such a ratio was 0.198 (Sejkora et al., 2022).

Crystal chemistry of arsenoústalečite and stibioústalečite
Arsenoústalečite and its Sb-isotype stibioústalečite (Sejkora et al., 2022) are new additions to the selenide minerals belonging to the tetrahedrite group, along with members of the hakite series, giraudite-(Zn) and pošepnýite.Moreover, they are the first Te-Se species of this group and are isotypic with arsenogoldfieldite and stibiogoldfieldite (Table 8).Pohl et al. (1996) first refined the crystal structure of a Se-bearing stibiogoldfieldite using the Rietveld method.They observed an increase in the unit-cell parameters owing to the Se-S substitution.Indeed, they reported a values ranging between 10.32 and 10.34 Å, larger than those of arsenogoldfieldite (a = 10.29 Å -Sejkora et al., 2023a) and similar to those of stibiogoldfieldite from the Mohawk mine (a = 10.35Å - Biagioni et al., 2022).In fact, the unit-cell parameters of Te-rich members of the tetrahedrite group are a function of their complex crystal chemistry (e.g.Makovicky and Karup-Møller, 2017).It is interesting to observe that the difference in unit-cell parameters between As-and Sb-members of the goldfieldite series is limited (∼0.07Å for Te = 2 apfu in synthetic products -Makovicky and Karup-Møller, 2017).The difference in the a unit-cell parameter of arsenoústalečite and stibioústalečite is ∼0.04 Å.This value seems to be in keeping with the observations on synthetic members of the goldfieldite series and does not agree with the large a value reported by Sejkora et al. (2022), i.e. 10.83 Å, with a variation of 0.17 Å with respect to arsenoústalečite.For this reason, the calculated density of stibioústalečite, given by Sejkora et al. (2022) as 5.676 g/cm 3 , should be revised to ∼5.89 g/cm 3 .
The Rietveld refinements of Pohl et al. (1996) gave another interesting result.According to them, Se is hosted at the S(1) site, whereas it was not possible to accurately determine the actual occupancy of S(2).The results obtained on both members of the ústalečite series agrees with the work of Pohl et al. (1996), clearly indicating that Se is preferentially partitioned at S(1), with S(2) being a dominant S-position.For this reason, the end-member formulae of the studied material are S(1) Se 12 S(2) S (Z = 2) for arsenoústalečite and stibioústalečite, respectively.
This result has a two-fold implication, being interesting from the point of view of mineral systematics (i.e.nomenclature issues) as well as for the genesis of members of the ústalečite series.
Actually, the different partitioning of Se and S between these two positions probably has a very important role, for instance avoiding too short M(2)-S(2) bond distances (see, for instance, what happens in pošepnýite - Škácha et al., 2020), even if few structural data are currently available to achieve an accurate picture of the Se and S partitioning in tetrahedrite-group minerals.For this reason, the occurrence of significant S contents could be highlighted, using an adjectival modifier, like, for instance, S-bearing arsenoústalečite.The future identification of S-free members of the ústalečite series would allow for a better understanding of their crystal chemistry, also possibly improving the classification scheme of tetrahedrite-group minerals.

Genesis of members of the ústalečite series
De Medicis and Giasson (1971) and Hutabalian et al. (2023) examined the phase diagram of the Cu-Te-Se system at 340°C and 500°C, respectively, but did not find anything similar to 'ústalečite'.The absence of the synthetic analogue of ústalečite-like minerals in the experiments could have a double explanation.
On the one hand, it could suggest that arsenoústalečite and stibioústalečite formed at low T conditions.This would be confirmed by the presence of Cu selenides (athabascaite, berzelianite and umangite) in the association, which are formed at temperatures below 100-123°C (Harris et al., 1970;Simon and Essene, 1996;Škácha et al., 2017).
On the other hand, structural data collected on both species clearly indicated the dominance of S at the S(2) position.If this preferential partitioning is due to structural constraints [e.g. the necessity to avoid too short M(2)-S(2) distances], it is possible that the absence of ústalečites in synthetic runs of the system Cu-Te-Se could be due to the absence of S that could play the same role of several minor chemical constituents observed in sulfosalts (e.g.Cl in dadsonite or O in meerschautite - Moëlo, 1979;Makovicky et al., 2006;Biagioni et al., 2016).Further studies will be useful to fully understand the actual compositional range of members of the ústalečite series.

Chemical variability of selenide members of the tetrahedrite group from Ústaleč
Figures 3 and 4 show the chemical composition for all studied samples of arsenoústalečite, stibioústalečite and other Se-dominant members of the tetrahedrite group from Ústaleč.Stibioústalečite is more common and it shows a wider range of As and Te contents; on the contrary, arsenoústalečite shows only a limited extent of Sb and Te contents, in the range 0.78-1.24and 1.49-1.98apfu, respectively.In other Se-dominant members of the tetrahedrite group, increased Te contents were determined only in the case of hakite-(Hg) and especially in the not-yet approved end-member 'hakite-(Cu)' (Fig. 3).The minor Ag contents for all studied grains of the ústalečite series are in the range 0.03-0.77apfu and do not correlate with Sb, Te or S contents.
*The reference wavelengths required by the Commission on Ore Mineralogy (COM) are given in bold.(σ)estimatedstandard deviation; n = number of spot analyses.

Table 3 .
Summary of data collection conditions and refinement parameters for arsenoústalečite and stibioústalečite.
Note: left and right superscripts indicate the number of equivalent bonds involving cations and anions, respectively.cat = cations; ani = anions.

Table 7 .
Calculated powder X-ray diffraction data for arsenoústalečite.Intensity and d hkl (in Å) were calculated using the software PowderCell2.3(Kraus and Nolze,