Photocatalytic Activity of La-Containing Mixed- Metal Oxides Derived from Layered Double Hydroxides to Degrade Methylene Blue in the Presence of H2O2

Published online by Cambridge University Press:  01 January 2024

Minhong Xu*
Affiliation:
Department of Materials Engineering, Huzhou University, Huzhou 313000, China
Mengxia Qian
Affiliation:
Key Laboratory of Advanced Textile Materials and Manufacturing Technology of Ministry of Education, Zhejiang Sci-Tech University, Hangzhou 310018, China
Guoxiang Pan
Affiliation:
Department of Materials Engineering, Huzhou University, Huzhou 313000, China
Yuhua Guo
Affiliation:
Department of Materials Engineering, Huzhou University, Huzhou 313000, China
Tao Wu
Affiliation:
Department of Materials Engineering, Huzhou University, Huzhou 313000, China
*
*E-mail address of corresponding author: xumh123@163.com
Rights & Permissions [Opens in a new window]

Abstract

Photocatalytic degradation of polluted water by means of minerals, such as clays and oxides, which have surfaces that exhibit catalytic properties, has been suggested to be a useful new strategy to promote both organic and inorganic pollutant degradation. Nevertheless, much still remains to be studied about the capability of mixed metal oxides derived from lanthanum-containing layered double hydroxides to promote pollutant removal by means of photocatalytic degradation with the mineral surfaces. The objective of the present study was to investigate the synthesis of ternary MgAlLa mixed-metal oxides (MgAlLa-M) with various Mg/Al/La molar ratios through a hydrotalcite-like precursor route by co-precipitation of appropriate amounts of metal salts from homogeneous solution, followed by calcination at 600°C. The crystal structure, surface morphology, and optical properties of the samples were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), Fourier-transform infrared spectroscopy (FTIR), and UV-Vis diffuse reflectance spectroscopy (DRS). Analysis by XRD showed that MgO, La2O3, MgAl2O4, and La10Al4O21 phases coexisted in calcined samples as MgAlLa-M. The samples showed a small band gap of 3.11–3.35 eV according to DRS. The photocatalytic activities of the samples were evaluated by degradation of methylene blue (MB) under visible light irradiation. MgAlLa-M had better photocatalytic properties than hydrotalcite precursors, and the MgAlLa-0.5-M possessed the best photocatalytic activity. The photocatalytic degradation efficiency of MB dye with MgAlLa-0.5-M under visible light irradiation for 1 h was 99.89% in the presence of H2O2, which exceeded the binary MgAl-M (84.06%) under the same conditions. The high photocatalytic activity of the sample was attributed to the addition of La(III). In addition, the possible mechanism of photocatalytic degradation of MB by MgAlLa-M was discussed. The results showed that •O2 plays a major role in the MgAlLa-0.5-M/H2O2 system.

Type
Article
Copyright
Copyright © Clay Minerals Society 2019

Introduction

The pollution of water by organic contaminants, such as Methylene Blue (MB), is a serious problem because of high toxicity and persistence in the environment (Ömer et al. Reference Ömer, Kaya and Saka2015). The efficient removal of organic dyestuffs from industrial polluted water has always been a challenging issue in the field of environmental remediation and pollution control (Li et al. Reference Li, Wu, Song, Li, Shao and Cao2017; Kong et al. Reference Kong, Li, Hu, Jing, Pan and Dong2018). The removal of a binary dye mixture of Congo Red and Malachite Green from aqueous solutions using a bentonite adsorbent was proposed by Özdemir & Keskin (Reference Özdemir and Keskin2009). Moreover, photocatalysts with semiconductor properties are considered important in such key remediation processes as water photolysis, photodegradation, photooxidation of toxic compounds, and photoelectrochemical conversion (Carja et al., Reference Zhang, Dai, Zhang, Liu and Yan2013; Xu et al. Reference Xu, Pan, Meng, Guo, Wu and Chen2019), where they act as efficient eco-friendly materials for removal of hazardous species.

Layered double hydroxides (LDHs) or hydrotalcite-like materials belong to a family of anionic clays with a brucite-like layered structure (Zhou Reference Zhou2010; Zhou & Keeling Reference Zhou and Keeling2013). Compared with synthetic clay minerals, LDHs have a wider range of chemical compositions of layers based on different choices of metal and interlayer anions (Shi et al. Reference Shi, Li, Wang, Li, Evans and Duan2005; Curtius and Ufer Reference Curtius and Ufer2007; Zhou et al. Reference Zhou, Li, Ai, Tian and Hong2016). Thus, LDHs are well known for their catalytic activity in organic synthesis (Shu et al. Reference Shu, He, Chen and Wang2008; Xiang et al. Reference Xiang, Hima, Wang and Li2008; Zhou Reference Zhou2010). LDHs are also ideal precursors for obtaining various mixed-metal oxides possessing tunable compositions upon heating (Xiang et al. Reference Xiang, Hima, Wang and Li2008). Furthermore, calcination of LDH materials at moderate temperatures (300–600°C) leads to the formation of highly active mixed-metal oxide (MMO) nanocomposites with large specific surface areas and good thermal stability, which can tune the semiconductor properties of the MMO materials and facilitate the transfer of the photogenerated electrons to the surface of photocatalysts. In particular, the mixed-metal oxides prepared by thermal treatment of LDHs act as photocatalysts either for organic degradation or for water splitting, and have been the focus of attention due to their versatility of chemical composition and wide dispersion (Parida et al. Reference Parida, Satpathy and Mohapatra2012; Baliarsingh et al. Reference Baliarsingh, Mohapatra and Parida2013; Wu et al. Reference Wu, Huang and Lim2014). The effect of Cu substitution on promoted benzene oxidation over porous CuCo-based catalysts derived from LDH was discussed by Li et al. (Reference Li, Wang, Li, Wu, Tang and Chen2015). A maximum of 97.3% photocatalytic decoloration rate within 60 min was achieved from the LDHs with a Zn/Ni/Al mole ratio of 2:1:1 and calcination temperature of 500°C according to Li et al. (Reference Li, Wu, Song, Li, Shao and Cao2017). A 150 W xenon lamp with λ = 200−900 nm was used as the simulated sunlight source. Calcined samples with a Ni/Co/Fe molar ratio of 1:2:1, derived from NiCoFe Ternary LDHs, possessed the best photocatalytic activity with 96.8% degradation of MB dye under Xenon lamp irradiation for 4 h, as reported by Pan et al. (Reference Pan, Ge, Zhao, Shao, Guo and Zhang2018). Although the photocatalytic effect was greater, the illumination time was longer. In addition, calcined ZnAlTi (Sahu et al. Reference Sahu, Mohanta and Das2013), CoMgAl (Yang et al. Reference Yang, Cui, Yan, Zhang, Qiu, O'Hare and Wang2017), and Mg-Al-Fe LDHs (Heredia et al. Reference Heredia, Oliva, Agú, Zandalazini, Marchetti, Herrero and Crivello2013) were reported. Moreover, the introduction of basic rare earth elements (La, Ce, or Y) into these materials can modify the basic sites and, thus, modulate the basicity of the catalyst (Wang et al. Reference Wang, Fongarland, Lu and Essayem2014; Subhan et al. Reference Subhan, Ahmed and Uddin2015).

The rare earth elements (REE) have the characteristics of oxygen storage functionality, rapidly variable valence states, and so on. Furthermore, the rare earth oxides with cation valence, paramagnetic behavior, lattice oxygen transfer, and alkaline surfaces have properties related intrinsically to many catalytic activities. The precursor with large photocatalytic activity can be prepared by introducing rare earth elements into LDH. For the above reasons, rare earth elements were introduced into ternary hydrotalcite to make composite oxides. Ternary LDH precursors have been reported, configured with Mg-Al-Tb, Mg-Al-Eu, Zn-Al-In, Zn-In (ZnIn-LDH), or melamine mixtures. Ternary MgO/ZnO/In2O3 heterostructured photocatalysts derived from a layered precursor, MgFeCe ternary LDH, and Ce- and Pr-promoted Ni and Co catalysts from hydrotalcite-type precursors (Chen et al. Reference Chen, Zhou, Li, Wei, Dai and Chen2011; Fan et al. Reference Fan, Sun, Wang and Li2011; Muñoz et al. Reference Muñoz, Moreno and Molina2012; Carja et al. Reference Carja, Dartu, Okada and Fortunato2013; Lan et al. Reference Lan, Fan, Yang and Li2014; Chen et al. Reference Chen, Lei, Wang, Liu, Wu, Chang, Zhang and Li2015; Nivangune et al. Reference Nivangune, Ranade and Kelkar2017) have also been reported. Few reports, however, have appeared on La-containing composite oxides derived from ternary LDHs. With practical application in mind, therefore, efficient use of Earth-abundant metal elements (e.g. Mg) for synthesis of high-performance photocatalysts (Xiang et al. Reference Xiang, Xie, Li and Li2013) and broadening the use of rare metal elements (e.g. La) are of great signficance.

The purpose of the present study was to synthesize a series of ternary MgAlLa MMOs (MgAlLa-M) with various Mg/Al/La ratios and to test their photocatalytic performance in abating organic pollutants by measuring the degradation of MB in aqueous solution under visible irradiation. This study was also undertaken with the hope of broadening the field of utilization of rare earth resources in China by making full use of the exchangeability of cations on hydrotalcite laminates (Mao et al. Reference Mao, Zhou, Tong, Yu and Cynthia Lin2017) and exploiting the high photocatalytic activity of REE.

Experimental

Materials

For this work, Mg(NO3)2·6H2O, La(NO3)3·6H2O, Al(NO3)3·9H2O, NaNO3, NaOH, isopropanol, p-benzoquinone, ethylene diamine tetraacetic acid disodium salt, H2O2, and MB of analytical purity grade were purchased from Aladdin Reagent Co., Ltd (Shanghai, China). All solutions were prepared with distilled water.

Synthesis of MgAlLa-LDHs

A series of MgAlLa-LDHs with various molar ratios of Al(III)/La(III) were synthesized by the co-precipitation method. At a molar ratio M(II)/M(III) of 3.0, specific quantities of Mg(NO3)2·6H2O, Al(NO3)3·9H2O, and La(NO3)3·6H2O solid were dissolved in distilled water, as solution A. Then NaOH and NaNO3 were dissolved in distilled water; this was marked as solution B. With constant stirring, solutions A and B were added dropwise into a beaker, which was filled with distilled water. In this process, the mixed solution was adjusted with NaOH solution until the pH was between 9 and 10, after which the solution was stirred continuously for a further 30 min. Finally, the slurry obtained was subsequently aged at 65°C for 24 h. The resulting precipitates were collected by centrifugal separation and washed thoroughly with distilled water. After that, the as-obtained solid was oven-dried at 60°C overnight to obtain MgAlLa-LDHs precursors with various Mg(II)/Al(III)/La(III) (Mg/Al/La) molar ratios (i.e. 3:1:0, 3:0.8:0.2, 3:0.6:0.4, 3:0.5:0.5, 3:0.2:0.8, and 3:0:1); these precursors were denoted as MgAlLa-x-L, where x stands for the La(III) molar ratio. For example, the precursor with a Mg(II)/Al(III)/La(III) molar ratio of 3:1:0 was denoted as MgAl-L, that with a Mg(II)/Al(III)/La(III) molar ratio of 3:0.5:0.5 was specifically denoted as MgAlLa-0.5-L, and that with a Mg(II)/Al(III)/La(III) molar ratio of 3:0:1 was specifically denoted as MgLa-1-L.

Synthesis of mixed-metal oxides

The MgAlLa-LDH precursor was calcined in air at 600°C for 5 h, and allowed to cool to room temperature to obtain Mg/Al/La mixed-metal oxides, which were named MgAlLa-M. The mole ratios of Mg(II)/Al(III)/La(III) were 3:1:0, 3:0.8:0.2, 3:0.6:0.4, 3:0.5:0.5, 3:0.2:0.8, and 3:0:1, respectively. In the present study, the mixed-metal oxide with a Mg(II)/Al(III)/La(III) mole ratio of 3:0.8:0.2 was denoted specifically as MgAlLa-0.2-M.

Characterizations

The morphology of the samples was examined using a S-3400N scanning electron microscope (Hitachi, Tokyo, Japan). Elemental analysis was obtained using a Model 550i, energy dispersive X-ray fluorescence (EDX) (Model 550i, IXRF System, Austin, Texas, USA). The crystal phases in the samples were identified by XRD (CuKα, λ = 0.1545 nm, beam voltage 36 kV, beam current 20 mA) (Beijing Purkinje General Instrument Co., Ltd., Beijing, China). Infrared (FTIR) spectra were recorded using the KBr disc method on a Nicolet 5700 FTIR spectrophotometer (Thermo Scientific, Waltham, Massachusetts, USA). The sample was dried at 120°C for 1 h and then the sample was mixed with KBr at a mass ratio of 1:100 for grinding and finally pressed into thin sheets for measurement. UV-Vis diffuse reflectance spectra (DRS) of the samples were obtained using an ISA-220 UV-Vis spectrophotometer (Thermo Scientific, Waltham, Massachusetts, USA). The time-dependent UV-Vis spectra of MB solutions were measured using a UV-2600 UV-vis spectrophotometer (Shimadzu, Tokyo, Japan).

Photocatalysis

The photocatalytic activities of the samples were assessed by photodegradation of MB solution under visible light irradiation from a 150 W halogen lamp, which was preheated for 30 min. Photocatalyst (0.05 g) was mixed with 25 mL of MB (5 mg/L) aqueous solution, to which was added 0.5 mL of H2O2 (30% w/w). For each run, 0.05 g of catalyst was added to a 25 mL MB solution and stirred vigorously for 30 min in the dark to establish an adsorption/desorption equilibrium. Subsequently, the solution was stirred under visible light irradiation. The catalyst was kept suspended by a magnetic stirrer. Samples for analysis were extracted using a pipette every 10 min and centrifuged immediately. After that, the filtrates were tested by measuring the absorbance at 664 nm using 752 UV-Vis spectroscopy to determine the concentration of MB. The effects of light and the La(III) content on the catalytic degradation of MB were investigated. Blank experiments, i.e. without catalyst or in the dark, were carried out under the same conditions.

Results and Discussion

X-ray Diffraction

The powder XRD patterns of as-synthesized MgAlLa-L precursors with variable Mg(II)/Al(III)/La(III) molar ratios (Fig. 1) revealed that, as for the MgAl-L sample (Fig. 1a), the diffraction peaks at 11.7, 22.5, 34.5, 60.2, and 62.4o2θ could be assigned to the (003), (006), (009), (110), and (113) reflections of LDH, respectively, characteristic of a layered structure (Ferreira et al. Reference Ferreira, Alves, Gouveia, Filho, Paiva and Filho2004; Carvalho et al. Reference Carvalho, Ferreira, Filho, Ferreira, Soares and Oliveira2015). They were consistent with the standard card JCPDS 40-0216. Almost identical, typical structures were observed in the XRD patterns of the MgAlLa-0.2-L, MgAlLa-0.4-L, and MgAlLa-0.5-L precursors. Compared with MgAl-L, they had the characteristics of a layered structure. Besides, the diffraction peaks at 15.5, 27.3, 27.9, 39.4, and 48.6o2θ could be indexed to La(OH)3 (JCPDS 36-1481). In other words, when the initial La(III) molar ratio was in the range 0.2 to 0.5, La(OH)3 and LDHs coexisted in MgAlLa-L.

Fig. 1 XRD patterns of MgAlLa-L precursors: (a) MgAl-L, (b) MgAlLa-0.2-L, (c) MgAlLa-0.4-L, (d) MgAlLa-0.5-L, (e) MgAlLa-0.8-L, and (f) MgLa-1-L.

However, the characteristic diffraction peak of hydrotalcite did not appear in MgAlLa-0.8-L and MgLa-1-L, indicating that the materials synthesized were not hydrotalcite when the Al(III)/La(III) molar ratio was 0.2:0.8 or when Al(III) was completely replaced by La(III). Besides the diffraction peak of La(OH)3, the reflections at 18.4, 38.0, 50.8, and 58.6°2θ could be indexed to Mg(OH)2 (JCPDS 44-1482), revealing the co-existence of La(OH)3 and Mg(OH)2 in MgLa-L.

The XRD patterns of MgAlLa-x-L calcined at 600°C (Fig. 2) revealed that the reflections corresponding to LDHs had disappeared completely and new reflections had appeared after calcination of MgAlLa-LDHs. The reflections at 42.8 and 62.3°2θ could be indexed to MgO (JCPDS No. 45-0946), whereas those at 31.3, 36.8, 44.8, 59.4, and 65.2°2θ could be indexed to MgAl2O4 (JCPDS No.21-1152). The MgAl2O4 spinel formed during the calcination process, similar to the work of Ahmed et al. (Reference Ahmed, Talib, Hussein and Zakaria2012). With an increased La(III) content, the reflections at 26.1, 29.9, 39.5, 46.0, 52.1, and 55.4°2θ could be indexed to La2O3 (JCPDS No. 05-0602), whereas those at 11.4, 18.3, 27.6, 29.3, 33.4, 45.6, and 47.1°2θ could be indexed to La10Al4O21 (JCPDS No.39-0009). The La10Al4O21 spinel occurred at MgAlLa-0.4-M. These results may be ascribed to the homogeneous distribution of metal ions within MgAlLa-LDHs, which facilitated the formation of well dispersed and crystalline mixed-metal oxides through a topotactic process during calcination (Zhao et al. Reference Zhao, Zhang, Xu, Evans and Duan2010). No signal corresponding to an Al2O3 phase was detected, implying that the Al2O3 was amorphous. This was because, following the collapse of the MgAlLa-LDHs layered structure upon calcination, generation of MgO (La2O3) and Al2O3 subsequently gave rise to the formation of spinel, MgAl2O4 (La10Al4O21) (Zhao et al. Reference Zhao, Zhang, Xu, Evans and Duan2010).

Fig. 2 XRD patterns of MgAlLa-M: (a) MgAl-M, (b) MgAlLa-0.2-M, (c) MgAlLa-0.4-M, (d) MgAlLa-0.5-M, (e) MgAlLa-0.8-M, and (f) MgLa-1-M.

FTIR spectroscopy analysis

The FTIR spectra of as-synthesized LDH samples (Fig. 3) were very similar to those reported generally for hydrotalcite-like compounds. The absorption peak between 3470 and ~3640 cm–1 in the IR spectra was ascribed to the stretching vibration of the OH group with hydrogen bonding from interlayer water molecules (Yan et al. Reference Yan, Yang, Shan, Yan, Wei, Yu, Yu and Du2015). Similarly, the band observed at 1630 cm-1 was attributed to the bending mode of crystalline water. An absorption peak at 1368 cm–1 was attributed to the telescopic vibration peak of NO3 - (Scavetta et al. Reference Scavetta, Ballarin, Corticelli, Gualandi, Tonelli, Prevot, Forano and Mousty2012). The bands at ~846 and 602 cm−1 arose from the metal-oxygen bonds (M-O, M-O-M, and M-OH) vibration in the LDHs. In the case of MgAlLa-0.4-L, MgAlLa-0.5-L, MgAlLa-0.8-L, and MgLa-1-L, a new band was observed at 3603 cm−1, which corresponded to non-bonded –OH group vibrations for La(OH)3. An absorption peak at 3696 cm−1 corresponds to non-bonded –OH group vibrations for Mg(OH)2. Compared with uncalcined samples, the differences in infrared spectra might be due to the structural difference in compounds formed with different amounts of La. The above results were consistent with XRD analysis.

Fig. 3 FTIR spectra of MgAlLa-L precursors: (a) MgAl-L, (b) MgAlLa-0.2-L, (c) MgAlLa-0.4-L, (d) MgAlLa-0.5-L, (e) MgAlLa-0.8-L, and (f) MgLa-1-L.

Morphology

The morphology of the MgAlLa-L with various molar ratios before calcination was characterized using SEM (Fig. 4). The MgAl-L synthesized showed many wrinkles on the surface (Fig. 4A1). MgAlLa-0.2-L and MgAlLa-0.4-L also displayed wrinkles on the surface (Fig. 4A2 and A3). Some fragments of MgAlLa-0.4-L also appeared. The morphology of MgAlLa-0.5-L (Fig. 4A4) changed significantly, and many irregular sheets aggregated. Needle-like and granular aggregates appeared for MgAlLa-0.8-L (Fig. 4A5) and MgLa-L (Fig. 4A6). With the increase in La(III) content in MgAlLa-L, the morphologies of the synthesized samples varied greatly.

Fig. 4 SEM images of MgAl-L (A1), MgAlLa-0.2-L (A2), MgAlLa-0.4-L (A3), MgAlLa-0.5-L (A4), MgAlLa-0.8-L (A5), and MgLa-L (A6).

The morphology of the MgAlLa-M with various molar ratios (Fig. 5) showed that MgAl-M after calcination was made up of irregular, multilateral sheets and some particles. In contrast, the multilateral fragments on the surface of MgAlLa-0.2-M and MgAlLa-0.4-M were more obvious (Fig. 5B2 and B3). The morphology of MgAlLa-0.5-M collapsed from a specific structure and became regular, agglomerated platelet-like particles after calcination at 600°C; the platelets had a side length of 0.08 μm (Fig. 5B4). Fine particles appeared for MgAlLa-0.8-M (Fig. 5B5) and MgLa-M (Fig. 5B6). The change in morphology seemed to be the result of MgAlLa-M having a large specific surface area. The EDX pattern (Fig. 5B7) further confirmed the presence of Mg, Al, La, and O in MgAlLa-0.5-M (Fig. 4F); the Mg(II)/Al(III)/La(III) molar ratio was close to 3:0.5:0.5.

Fig. 5 SEM images of MgAl-M (B1), MgAlLa-0.2-M (B2), MgAlLa-0.4-M (B3), MgAlLa-0.5-M (B4), MgAlLa-0.8-M (B5), and MgLa-M (B6), along with EDX measurement of MgAlLa-0.5-M (B7).

Optical properties

The UV-Vis absorption spectra of the as-prepared samples (Fig. 6A and C) revealed that the MgAlLa-M had a better absorbance stability than MgAlLa-L, and the absorption edge was extended to ~800 nm covering the full visible light spectrum, compared with the absorption edges of MgAlLa-L. The band-gap energies of the samples before and after calcination were calculated using the onset of the UV–Vis spectra of the absorption values (Eq. 1) (Hussain et al., Reference Hussain, Russo and Saracco2011)

(1) a h v 2 = K h v Eg

Fig. 6 UV-Vis absorption spectra of the MgAlLa-L (A) and MgAlLa-M (C), and the plotting of (ahν)2 vs. based on the direct transition (B, D). MgAlLa-L (A, B): (a) MgAl-L, (b) MgAlLa-0.2-L, (c) MgAlLa-0.4-L, (d) MgAlLa-0.5-L, (e) MgAlLa-0.8-L, and (f) MgLa-1-L. MgAlLa-M (B, D): (a) MgAl-M, (b) MgAlLa-0.2-M, (c) MgAlLa-0.4-M, (d) MgAlLa-0.5-M, (e) MgAlLa-0.8-M, and (f) MgLa-1-M.

Where a is the absorption coefficient, ν represents the light frequency, Eg is the band gap energy, K is a proportionality constant, and h is Planck’s constant. The normalized graphs of (ahν)2 for the photon energy of the MgAlLa-L and MgAlLa-M samples (Fig. 6B and D) showed that all MgAlLa-M samples exhibited relatively lower band gap energy and were expected to show better photocatalytic activity compared with MgAlLa-L. The smaller band-gap might be attributed to the composite oxides formed by calcination, and the band-gap values of MgAlLa-M samples (3.11–3.35 eV) were smaller than those of MgAl-M (3.36 eV). The MgAlLa-M samples were thus expected to show better photocatalytic activity than MgAl-M under visible light. This result could be attributed to the coupling interaction among the MgO, La2O3, MgAl2O4, and La10Al4O21 phases, the optimizing content of MgO, La2O3, and the form of heterojunction structure, which led to the enhancement of utilization of light and photocatalytic activity (Zhang et al., Reference Zhang, Dai, Zhang, Liu and Yan2016).

Influence of light

The influence of light on the photocatalytic activity of MgAlLa-0.5-M was determined by degradation of MB (Fig. 7). The residual amount of MB was almost unchanged with no light, which indicated that the adsorption of MB by MgAlLa-0.5-M was weak. Another test without light demonstrated that MB could not be degraded under MgAlLa-0.5-M/H2O2, because the residual level of MB was 91.65% after reaction for 60 min. When the MB solutions were light irradiated for 60 min, however, the residual MB was only 0.11% under MgAlLa-0.5-M/H2O2. Meanwhile, the color of the MB solution was close to colorless, which led to the conclusion that photocatalytic degradation of MB in the MgAlLa-0.5-M and H2O2 system is accelerated by light irradiation.

Fig. 7 Effect of light on photocatalytic degradation of MB with MgAlLa-0.5-M.

Effect of catalyst

Under illumination only, the residual amount of MB was 84% after 1 h, and the rate of degradation was very slow (Fig. 8). When 0.5 mL H2O2 was added, the degradation rate of MB increased, and the residual amount was 70.1% after 1 h. The photocatalytic degradation efficiency of MB with 50 mg of MgAl-M was almost the same as that by MB only. The degradation efficiency of MgAlLa-0.5-M was more obvious, and the residual MB was 36.23% after 60 min. The degradation rate of MB increased significantly when the catalyst and H2O2 acted simultaneously. The results above showed that the catalytic degradation of MB by a single catalyst was not ideal, only when MgAlLa-M and H2O2 were used in concert was the best level of photocatalytic degradation achieved; photocatalytic degradation efficiency of MB dye with MgAlLa-0.5-M under visible light irradiation for 1 h was 99.89%, which exceeded the binary MgAl-M (84.06%) under the same conditions. This might be attributed to the introduction of La(III) to improve the photocatalytic activity of mixed-metal oxides.

Fig. 8 Effect of catalyst on photocatalytic degradation of MB.

Effect of MgAlLa-L/H2O2

The photocatalytic effect of MgAlLa-L with a molar ratio of Mg(II)/Al(III)/La(III) (Fig. 9) showed that MgAlLa-L possessing different molar ratios exhibited a strong catalytic degradation ability for MB, and that the La(III) content affected the photocatalytic degradation rate. The photocatalytic effect of MgAlLa-L/H2O2 increased when the La(III) content decreased. When Al(III) was completely replaced by La(III), however, the photocatalytic activity was best. According to XRD analysis, MgLa-1-L does not have a hydrotalcite structure, so the basic substances such as Mg(OH)2 and La(OH)3 in the MgLa-1-L possibly played a photocatalytic role.

Fig. 9 Photocatalytic degradation of MB with MgAlLa-L/H2O2.

Effect of MgAlLa-M/H2O2

The photocatalytic effect of La2O3 on MB (Fig. 10) was not obvious; after 60 min the residual MB was >60% (contrast experiment), which indicated that La2O3 did not play a major role in the photocatalytic process. When Mg-Al hydrotalcite was calcined to form mixed-metal oxides, the residual MB was 15.9% after photocatalytic degradation for 60 min. While Mg(II), Al(III), and La(III) coexisted in the composite oxides (the molar ratio of La(III) being from 0.2 to 0.8), the MB residue decreased and the catalytic activity of MgAlLa-M increased. When the molar ratio of Mg(II):Al(III):La(III) was 3:0.5:0.5, the photocatalytic activity of MgAlLa-0.5-M was better than that of MgAl-M and the residual MB was only 0.11% after 60 min. The photocatalytic MB effect of the mixed-metal oxides that formed when Al(III) was replaced completely by La(III) was most obvious, and the degradation was completed within 30 min. Irradiation at ~150 W from a halogen lamp was less bright than with a xenon lamp. In addition, the reaction time was 30–60 min, which shortened the illumination time and improved the photocatalytic efficiency.

Fig. 10 Photocatalytic degradation of MB with MgAlLa-M/H2O2.

The catalytic activity of MgAlLa-M for MB was obviously better than that of MgAlLa-L (Fig. 11). This was because the mixed-metal oxides contain MgO, La2O3, MgAl2O4, and La10Al4O21, which had a relatively smaller band gap than MgAlLa-L, thereby improving the visible light absorption of the mixed-metal oxides. On the other hand, the effects of photocatalytic degradation of MB by MgAlLa-L or MgAlLa-M was irregular as the La content increased, which might be related to the composition and morphology of the composite oxides.

Fig. 11 Comparison of photocatalytic activity of MgAlLa-L and MgAlLa-M with various La(III) contents.

The interface heterostructures in MgAlLa-M were different. Heterojunctions with good electron (e ) and hole (h +) transport channels could be formed at the interface of MgAlLa-M with appropriate molar ratios of Mg(II), Al(III), and La(III). Moreover, the key factor of high photocatalytic activity was the effective separation of photogenerated e and h + pairs. Consequently, when the molar ratio of Mg(II), Al(III), and La(III) was appropriate in MgAlLa-M, MgAlLa-M displayed excellent photocatalytic performance. The photocatalytic activity of MgAlLa-0.5-M on MB was slightly better than that of MgLa-1-M, and the photocatalytic performance of MgAlLa-M was better than that of MgAl-M, inferring that hydrotalcite-based mixed-metal oxides prepared with MgAl-LDHs as precursors, which added La(III), improves the degradation ability of the catalyst toward MB. Interestingly, in contrast with MgLa-0.5-M, MgLa-1-M had a higher ratio of La(III) but showed no improvement in photocatalytic activity, suggesting that the amount of La(III) was the crucial factor.

UV-Vis absorption spectra of MB

The UV-Vis absorption spectra (Fig. 12) showed a strong absorption peak at 664 nm which belonged mainly to the conjugated system of aromatic rings in the MB structure. With the prolongation of photocatalytic reaction time, the maximum absorption peak of MB solution weakened gradually. This was due to the destruction of display groups, which consist of chromophore and cochromophore in MB during the photocatalytic reaction. When photocatalysis lasted for 60 min, the absorption peak was no longer obvious, which was attributed to the interruption of the unsaturated conjugate bond of the chromophore group during the photocatalytic degradation of MB.

Fig. 12 The UV-Vis absorption spectra of MB with MgAlLa-0.5-M/H2O2.

Photocatalytic mechanism

To further elucidate the reaction mechanism, the reactive species were determined in the presence of isopropanol (IPA), p-benzoquinone (BQN), and disodium ethylenediamine tetraacetic acid (EDTA) as scavengers of hydroxyl radicals (•OH), superoxide radicals (•O2 ), and photoexcited holes (h+), respectively (Yan et al. Reference Yan, Zhu, Li, Li, Liu and Wang2013). So, in the reaction system, the mole ratio of MB to the capture agent was 1:200.

When the MB solutions (Fig. 13) were irradiated for 60 min, the residual amounts of MB were 33.78%, 10.63%, and 2.92% over BQN, EDTA, and IPA, respectively. A significant decrease of photocatalytic performance in the presence of BQN was observed, implying that •O2– played a major role in the photocatalytic reaction. Moreover, the photocatalytic performance decreased slightly in the presence of IPA and EDTA, suggesting that the •OH and h+ were the less important reactive species for the decomposition of MB.

Fig. 13 Active species trapping experiments under visible light irradiation.

The possible mechanism of photocatalytic degradation of MB is as follows. Photo-induced e /h + pairs were generated on the surface of the photocatalyst MgAlLa-M during irradiation (Eq. 1). The photoinduced h + -oxidized H2O2 molecules that were adsorbed on the photocatalyst surface into •OH species (Eq. 2), while the photoinduced e -activated H2O2 and O2 molecules adsorbed on the catalyst surface into •OH, OH species (Eq. 3) and •O2 species (Eq. 4), respectively. In addition, •OH species were also generated during irradiation of H2O2 (Eq. 5). H2O2 oxidized the active •O2 species into •OH, OH , and O2 species (equation 6). The •OH and O2 are the main active species in the photocatalytic reaction (Ishibashi et al. Reference Ishibashi, Fujishima, Watanabe and Hashimoto2000; Liu & Sun Reference Liu and Sun2011; Xiang et al. Reference Xiang, Yu and Wong2011). The MB molecules were oxidized by •OH and O2 species into small molecules (Eqs. 7 and 8).

(2) MgAlLa M + h v e + h +
(3) h + + H 2 O 2 2 OH
(4) e + H 2 O 2 OH + OH
(5) e + O 2 O 2
(6) H 2 O 2 + h v 2 OH
(7) O 2 + H 2 O 2 OH + OH + O 2
(8) OH + MB Degradation products
(9) O 2 + MB Degradation products

Based on the above discussions and the experimental results of MB degradation under different capture agents, when BQN was added to the reaction system, the •O2 was captured, so reactions 6, 7, and 8 were hindered, which would hinder the degradation process of MB. On the other hand, reaction 4 proceeded to the right while trapping •O2 . As a result, the formation of h + and •OH was accelerated. But the degradation of MB had not accelerated, implying that •O2 played a major role in the photocatalytic reaction.

When EDTA was added, the h + was captured, and reaction 2 was hindered and the amount of •OH produced was reduced, which would diminish the degradation of MB. Although the h + was captured, reaction 1 was pushed to the right, which led to the production of a large amount of e at the surface and inside the catalyst. The production of e and H2O2 and O2 in the solution is enabled by reactions 3 and 4 to produce •OH and •O2 . The •OH could effectively oxidize MB, while •O2 and H2O2 could react according to reaction 6 to produce •OH and O2, which could oxidize MB (Liu & Sun Reference Liu and Sun2011). The experimental results showed, however, that the degradation of MB slows down after adding EDTA, so one could speculate that reaction 2 was the key step in the degradation of MB.

In addition, when IPA was present, •OH in the solution was captured, which hindered the progress of reaction 7, but enabled reactions 2, 3, and 6 to proceed to the right. At the same time, reaction 1 was accelerated. A large number of e and h + were produced in the solution, which accelerated the formation of •O2 and promoted the degradation of MB. In fact, in the photocatalytic degradation of MB, many bubbles were produced in the solution, leading to speculation that MB was degraded according to reaction 8. This was consistent with the results of accelerating the degradation of MB under isopropanol.

Based on the aforementioned experimental results, a possible mechanism for the enhanced photoactivity of MgAlLa-0.5-M/H2O2 is proposed. Under visible-light irradiation, photogenerated e and h + is formed at the inside of MgAlLa-M after irradiation. These e and h + move freely within the MgAlLa-M. When they move to the surface, e interacts with O2 and H2O2 in the solution to form •O2 and •OH, and h + reacts with H2O2 to form •OH, which together promotes the oxidative decomposition of MB. In addition, in the reaction system of MgAlLa-0.5-M/H2O2, •O2 plays a major role and the h + and •OH are the less important reactive species for the decomposition of MB.

Conclusions

In this work, ternary MgAlLa mixed-metal oxides (MgAlLa-M) were synthesized via a hydrotalcite-like precursor route. Analysis by XRD showed that MgO, La2O3, MgAl2O4, and La10Al4O21 phases coexisted in calcined samples as MgAlLa-M. MgAlLa-M had a smaller band gap and stronger visible light absorption ability than binary MgAl mixed-metal oxides. The photocatalytic degradation efficiency of MB dye with MgAlLa-0.5-M under visible light irradiation for 1 h was 99.89% in the presence of H2O2, which exceeded binary MgAl-M (84.06%) under the same conditions. The high photocatalytic activity of the sample was attributed to the addition of La(III). The high activity radicals of •O2 played a major role.

Acknowledgements

This work was supported financially by the Zhejiang Provincial Natural Science Foundation of China (LQ19E040001 and LY14B060006).

Footnotes

This paper was originally presented during the World Forum on Industrial Minerals, held in Qing Yang, China, October 2018.

AE: Chun-Hui Zhou

References

Ahmed, AAA Talib, Z. A. Hussein, MZB Zakaria, A., Improvement of the crystallinity and photocatalytic property of zinc oxide as calcination product of Zn–Al layered double hydroxide Journal of Alloys and Compounds 2012 539 154160 10.1016/j.jallcom.2012.05.093.CrossRefGoogle Scholar
Baliarsingh, Niranjan Mohapatra, Lagnamayee Parida, Kulamani, Design and development of a visible light harvesting Ni–Zn/Cr–CO32− LDH system for hydrogen evolution Journal of Materials Chemistry A 2013 1 13 4236 10.1039/c2ta00933a.CrossRefGoogle Scholar
Carvalho, D. C. Ferreira, N. A. Filho, J. M. Ferreira, O. P. Soares, J. M. Oliveira, A. C., Ni–Fe and Co–Fe binary oxides derived from layered double hydroxides and their catalytic evaluation for hydrogen production Catalysis Today 2015 250 155165 10.1016/j.cattod.2014.08.010.CrossRefGoogle Scholar
Carja, G. Dartu, L. Okada, K. Fortunato, E., Nanoparticles of copper oxide on layered double hydroxides and the derived solid solutions as wide spectrum active nano-photocatalysts Chemical Engineering Journal 2013 222 6066 10.1016/j.cej.2013.02.039.CrossRefGoogle Scholar
Chen, Y. Zhou, S. Li, F. Wei, J. Dai, Y. Chen, Y., Fluorescence and phase transitions of Mg-Al-Eu ternary layered double hydroxides-dependence on annealing Clay Minerals 2011 46 487493 10.1007/s10895-011-0857-8.CrossRefGoogle Scholar
Chen, J. Lei, Z. Wang, A. Liu, J. Wu, X. Chang, T. Zhang, Y. Li, M., Structure analysis and fluorescence of Mg-Al-Tb ternary layered double hydroxides and their calcined products Journal of Metals 2015 67 354360 10.1007/s11837-014-1210-x.Google Scholar
Curtius, H. Ufer, K., Eu incorporation behavior of a Mg-Al-Cl layered double hydroxide Clays and Clay Minerals 2007 55 354360 10.1346/ccmn.2007.0550403.CrossRefGoogle Scholar
Fan, G. Sun, W. Wang, H. Li, F., Visible-light-induced heterostructured Zn–Al–In mixed metal oxide nanocomposite photocatalysts derived from a single precursor Chemical Engineering Journal 2011 174 467474 10.1016/j.cej.2011.09.054.CrossRefGoogle Scholar
Ferreira, O. P. Alves, O. L. Gouveia, D. X. Filho, AGS Paiva, JACD Filho, J. M., Thermal decomposition and structural reconstruction effect on Mg–Fe-based hydrotalcite compounds Journal of Solid State Chemistry 2004 177 30583069 10.1016/j.jssc.2004.04.030.CrossRefGoogle Scholar
Heredia, A. C. Oliva, M. I. Agú, U. Zandalazini, C. I. Marchetti, S. G. Herrero, E. R. Crivello, M. E., Synthesis, characterization and magnetic behavior of Mg–Fe–Al mixed oxides based on layered double hydroxide Journal of Magnetism and Magnetic Materials 2013 342 3846 10.1016/j.jmmm.2013.04.057.CrossRefGoogle Scholar
Hussain, M. Russo, N. Saracco, G., Photocatalytic abatement of VOCs by novel optimized TiO2 nanoparticles Chemical Engineering Journal 2011 166 138149 10.1016/j.cej.2010.10.040.CrossRefGoogle Scholar
Ishibashi, K. I. Fujishima, A. Watanabe, T. Hashimoto, K., Quantum yields of active oxidative species formed on TiO2 photocatalyst Journal of Photochemistry and Photobiology A-Chemistry 2000 134 139142 10.1016/S1010-6030(00)00264-1.CrossRefGoogle Scholar
Kong, Y. Li, Y. Hu, G. Jing, L. Pan, D. Dong, D. et al. , Preparation of polystyrene-b-poly(ethylene/propylene)-b-polystyrene grafted glycidyl methacrylate and its compatibility with recycled polypropylene/recycled high impact polystyrene blends Polymer 2018 145 232241 10.1016/j.polymer.2018.05.017.CrossRefGoogle Scholar
Lan, M. Fan, G. Yang, L. Li, F., Enhanced visible-light-induced photocatalytic performance of a novel ternary semiconductor coupling system based on hybrid Zn–In mixed metal oxide/g-C3N4 composites RSC Advances 2014 5 57255734 10.1039/C4RA07073A.CrossRefGoogle Scholar
Li, S. D. Wang, H. S. Li, W. M. Wu, X. F. Tang, W. X. Chen, Y. F., Effect of Cu substitution on promoted benzene oxidation over porous CuCo-based catalysts derived from layered double hydroxide with resistance of water vapor Applied Catalysis B Environmental 2015 166-167 260269 10.1016/j.apcatb.2014.11.040.CrossRefGoogle Scholar
Li, Y. Wu, X. Song, J. Li, J. Shao, Q. Cao, N. et al. , Reparation of recycled acrylonitrile- butadiene-styrene by pyromellitic dianhydride: reparation performance evaluation and property analysis Polymer 2017 124 4147 10.1016/j.polymer.2017.07.042.CrossRefGoogle Scholar
Liu, N. Sun, G., Photo-degradation of methylene blue in the presence of 2-anthraquinone sulfonate and cyclohexanol presence Dyes and Pigments 2011 91 215224 10.1016/j.dyepig.2011.03.018.CrossRefGoogle Scholar
Mao, N. Zhou, C. H. Tong, D. S. Yu, W. H. Cynthia Lin, C. X., Exfoliation of layered double hydroxide solids into functional nanosheets Applied Clay Science 2017 144 6078 10.1016/j.clay.2017.04.021.CrossRefGoogle Scholar
Muñoz, M. Moreno, S. Molina, R., Synthesis of Ce and Pr-promoted Ni and Co catalysts from hydrotalcite type precursors by reconstruction method International Journal of Hydrogen Energy 2012 37 1882718842 10.1016/j.ijhydene.2012.09.132.CrossRefGoogle Scholar
Nivangune, N. T. Ranade, V. V. Kelkar, A. A., MgFeCe ternary layered double hydroxide as highly efficient and recyclable heterogeneous base catalyst for synthesis of dimethyl carbonate by transesterification Catalysis Letters 2017 147 25582569 10.1007/s10562-017-2146-x.CrossRefGoogle Scholar
Ömer, Ş Kaya, M. Saka, C., Plasma-surface modification on bentonite clay to improve the performance of adsorption of methylene blue Applied Clay Science 2015 116 4653 10.1016/j.clay.2015.08.015.Google Scholar
Özdemir, A. Keskin, C. S., Removal of a binary dye mixture of congo red and malachite green from aqueous solutions using a bentonite adsorbent Clays and Clay Minerals 2009 57 695705 10.1346/CCMN.2009.0570603.CrossRefGoogle Scholar
Pan, D. Ge, S. Zhao, J. Shao, Q. Guo, L. Zhang, X. et al. , Synthesis, characterization and photocatalytic activity of mixed-metal oxides derived from NiCoFe ternary layered double hydroxides Dalton Transactions 2018 47 6578 10.1039/C8DT01045E.CrossRefGoogle ScholarPubMed
Parida, K. Satpathy, M. Mohapatra, L., Incorporation of Fe(III) into Mg/Al layered double hydroxide framework: effects on textural properties and photocatalytic activity for H2 generation Journal of Materials Chemistry 2012 22 73507357 10.1039/c2jm15658j.CrossRefGoogle Scholar
Sahu, R. K. Mohanta, B. S. Das, N. N., Synthesis, characterization and photocatalytic activity of mixed oxides derived from ZnAlTi ternary layered double hydroxides Journal of Physics and Chemistry of Solids 2013 74 12631270 10.1016/j.jpcs.2013.04.002.CrossRefGoogle Scholar
Scavetta, E. Ballarin, B. Corticelli, C. Gualandi, I. Tonelli, D. Prevot, V. Forano, C. Mousty, C., An insight into the electrochemical behavior of Co/Al layered double hydroxide thin films prepared by electrodeposition Journal of Power Sources 2012 201 360367 10.1016/j.jpowsour.2011.10.122.CrossRefGoogle Scholar
Shi, L. Li, D. Wang, J. Li, S. Evans, D. G. Duan, X., Synthesis, flame-retardant and smoke-suppressant properties of a borate-intercalated layered double hydroxide Clays and Clay Minerals 2005 53 294300 10.1346/ccmn.2005.0530309.CrossRefGoogle Scholar
Shu, X. He, J. Chen, D. Wang, Y., Tailoring of phase composition and photoresponsive properties of Ti-containing nanocomposites from layered precursor The Journal of Physical Chemistry C 2008 112 41514158 10.1021/jp711091m.CrossRefGoogle Scholar
Subhan, M. A. Ahmed, T. Uddin, N., Synthesis, structure, Pl and photocatalytic activities of La2O2CO3·CeO2·ZnO fabricated by co-precipitation method Spectrochimica Acta Part A Molecular and Biomolecular Spectroscopy 2015 138 827833 10.1016/j.saa.2014.10.114.CrossRefGoogle ScholarPubMed
Wang, Z. Fongarland, P. Lu, G. Essayem, N., Reconstructed La-, Y-, Ce-modified MgAl-hydrotalcite as a solid base catalyst for aldol condensation: investigation of water tolerance Journal of Catalysis 2014 318 108118 10.1016/j.jcat.2014.07.006.CrossRefGoogle Scholar
Wu, W. Huang, Z. H. Lim, T. T., Recent development of mixed metal oxide anodes for electrochemical oxidation of organic pollutants in water Applied Catalysis A: General 2014 480 5878 10.1016/j.apcata.2014.04.035.CrossRefGoogle Scholar
Xiang, X. Hima, H. I. Wang, H. Li, F., Facile synthesis and catalytic properties of nickel-based mixed-metal oxides with mesopore networks from a novel hybrid composite precursor Chemistry of Materials 2008 20 11731182 10.1021/cm702072t.CrossRefGoogle Scholar
Xiang, Q. Yu, J. Wong, P. K., Quantitative characterization of hydroxyl radicals produced by various photocatalysts Journal of Colloid and Interface Science 2011 357 163167 10.1016/j.jcis.2011.01.093.CrossRefGoogle ScholarPubMed
Xiang, X. Xie, L. Li, Z. Li, F., Ternary MgO/ZnO/In2O3 heterostructured photocatalysts derived from a layered precursor and visible-light-induced photocatalytic activity Chemical Engineering Journal 2013 221 222229 10.1016/j.cej.2013.02.030.CrossRefGoogle Scholar
Xu, M. Pan, G. Meng, Y. Guo, Y. Wu, T. Chen, H., Effect of Ce3+ on the photocatalytic activity of MAlCe ternary hydrotalcites-like compounds in methylene blue photodegradation Applied Clay Science 2019 170 4656 10.1016/j.clay.2019.01.011.CrossRefGoogle Scholar
Yan, T. Zhu, H. Li, R. Li, Z. Liu, J. Wang, G., Microwave synthesis of nickel/cobalt double hydroxide ultrathin flowerclusters with three-dimensional structures for high-performance supercapacitors Electrochim Acta 2013 111 7179 10.1016/j.electacta.2013.07.215.Google Scholar
Yan, L. Yang, K. Shan, R. Yan, T. Wei, J. Yu, S. Yu, H. Du, B., Kinetic, isotherm and thermodynamic investigations of phosphate adsorption onto core–shell Fe3O4@ LDH composites with easy magnetic separation assistance Journal of Colloid and Interface Science 2015 448 508516 10.1016/j.jcis.2015.02.048.CrossRefGoogle ScholarPubMed
Yang, R. Cui, Y. Yan, Q. Zhang, C. Qiu, L. O'Hare, D. Wang, Q., Design of highly efficient NOx storage-reduction catalysts from layered double hydroxides for NOx emission control from naphtha cracker flue gases Chemical Engineering Journal 2017 326 656666 10.1016/j.cej.2017.06.016.CrossRefGoogle Scholar
Zhao, X. Zhang, F. Xu, S. Evans, D. G. Duan, X., From layered double hydroxides to ZnO-based mixed metal oxides by thermal decomposition: transformation mechanism and UV-blocking properties of the product Chemistry of Materials 2010 22 39333942 10.1021/cm100383d.CrossRefGoogle Scholar
Zhang, L. Dai, C. H. Zhang, X. X. Liu, Y. N. Yan, J. H., Synthesis and highly efficient photocatalytic activity of mixed oxides derived from ZnNiAl layered double hydroxides Transactions of Nonferrous Metals Society of China 2016 26 23802389 10.1016/S1003-6326(16)64360-1.CrossRefGoogle Scholar
Zhou, C. H., Emerging trends and challenges in synthetic clay-based materials and layered double hydroxides Applied Clay Science 2010 48 14 10.1016/j.clay.2009.12.018.CrossRefGoogle Scholar
Zhou, C. H. Keeling, J., Fundamental and applied research on clay minerals: from climate and environment to nanotechnology Applied Clay Science 2013 74 39 10.1016/j.clay.2013.02.013.CrossRefGoogle Scholar
Zhou, C. H. Li, Z. Z. Ai, Q. W. Tian, H. C. Hong, P. H., Current fundamental and applied research into clay minerals in china Applied Clay Science 2016 119 37 10.1016/j.clay.2015.07.043.CrossRefGoogle Scholar
Figure 0

Fig. 1 XRD patterns of MgAlLa-L precursors: (a) MgAl-L, (b) MgAlLa-0.2-L, (c) MgAlLa-0.4-L, (d) MgAlLa-0.5-L, (e) MgAlLa-0.8-L, and (f) MgLa-1-L.

Figure 1

Fig. 2 XRD patterns of MgAlLa-M: (a) MgAl-M, (b) MgAlLa-0.2-M, (c) MgAlLa-0.4-M, (d) MgAlLa-0.5-M, (e) MgAlLa-0.8-M, and (f) MgLa-1-M.

Figure 2

Fig. 3 FTIR spectra of MgAlLa-L precursors: (a) MgAl-L, (b) MgAlLa-0.2-L, (c) MgAlLa-0.4-L, (d) MgAlLa-0.5-L, (e) MgAlLa-0.8-L, and (f) MgLa-1-L.

Figure 3

Fig. 4 SEM images of MgAl-L (A1), MgAlLa-0.2-L (A2), MgAlLa-0.4-L (A3), MgAlLa-0.5-L (A4), MgAlLa-0.8-L (A5), and MgLa-L (A6).

Figure 4

Fig. 5 SEM images of MgAl-M (B1), MgAlLa-0.2-M (B2), MgAlLa-0.4-M (B3), MgAlLa-0.5-M (B4), MgAlLa-0.8-M (B5), and MgLa-M (B6), along with EDX measurement of MgAlLa-0.5-M (B7).

Figure 5

Fig. 6 UV-Vis absorption spectra of the MgAlLa-L (A) and MgAlLa-M (C), and the plotting of (ahν)2 vs. based on the direct transition (B, D). MgAlLa-L (A, B): (a) MgAl-L, (b) MgAlLa-0.2-L, (c) MgAlLa-0.4-L, (d) MgAlLa-0.5-L, (e) MgAlLa-0.8-L, and (f) MgLa-1-L. MgAlLa-M (B, D): (a) MgAl-M, (b) MgAlLa-0.2-M, (c) MgAlLa-0.4-M, (d) MgAlLa-0.5-M, (e) MgAlLa-0.8-M, and (f) MgLa-1-M.

Figure 6

Fig. 7 Effect of light on photocatalytic degradation of MB with MgAlLa-0.5-M.

Figure 7

Fig. 8 Effect of catalyst on photocatalytic degradation of MB.

Figure 8

Fig. 9 Photocatalytic degradation of MB with MgAlLa-L/H2O2.

Figure 9

Fig. 10 Photocatalytic degradation of MB with MgAlLa-M/H2O2.

Figure 10

Fig. 11 Comparison of photocatalytic activity of MgAlLa-L and MgAlLa-M with various La(III) contents.

Figure 11

Fig. 12 The UV-Vis absorption spectra of MB with MgAlLa-0.5-M/H2O2.

Figure 12

Fig. 13 Active species trapping experiments under visible light irradiation.

Supplementary material: File

Xu et al. supplementary material
Download undefined(File)
File 174.2 KB
Supplementary material: File

Xu et al. supplementary material
Download undefined(File)
File 108.7 KB
Supplementary material: File

Xu et al. supplementary material
Download undefined(File)
File 495.3 KB