Chemical and Structural Characterization of the Ni-Ti Alloy/6H-SiC Contacts

Published online by Cambridge University Press:  15 February 2011

M. Levit
Affiliation:
Department of Materials Engineering, Technion - Israel Institute of Technology, Haifa 32000, Israel
I. Grimberg
Affiliation:
Department of Materials Engineering, Technion - Israel Institute of Technology, Haifa 32000, Israel
B.-Z. Weiss
Affiliation:
Department of Materials Engineering, Technion - Israel Institute of Technology, Haifa 32000, Israel
M. Eizenberg
Affiliation:
Department of Materials Engineering, Technion - Israel Institute of Technology, Haifa 32000, Israel
Get access

Abstract

Ni-Ti alloy is a promising candidate for high-temperature contact metallization for SiC electronic devices. In the present study Ni-Ti alloy thin films (100 nm) of two different compositions (Ni90Ti10 and Ni50Ti50) were coevaporated on 6H-SiC substrate. Interfacial reactions, microstructure, compositional changes, and phase formation were investigated as functions of heat-treatments in the range of 400–800 °C. The study was carried out using Auger electron spectroscopy, x-ray diffraction, and analytical transmission electron microscopy. In the case of the Ni90Ti10 alloy the interaction was found to begin at 450 °C. Ni and C are the dominant diffusing species. The reaction zone is divided into three layers. In the first layer, adjacent to the SiC substrate, the presence of a Ni-rich silicide, Ni2Si, and C precipitates, was observed. The second layer is composed mainly of TiC, while the third - of Ni2 Si. In the case of the Ni50 Ti50 alloy the interaction began at 800 °C. Carbon is the dominant diffusant. The reaction zone is divided into two layers. The first, next to the substrate layer is composed of epitaxially grown TiC and the second - of Ni3Ti2Si compound. A thin (∼5 nm) amorphous discontinuous layer was found at the TiC/SiC interface. Factors controlling phase formation in the Ni-Ti/SiC system are discussed.

Type
Research Article
Copyright
Copyright © Materials Research Society 1996

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Edgar, J. H., J. Mater. Res. 7, 235 (1992).Google Scholar
2. Alok, D., McLarty, P. K., and Baliga, B. J., Appl. Phys. Lett. 64, 2845 (1994).Google Scholar
3. Crofton, J., Ferrero, J. M., Barnes, P. A., Williams, J. R., Bozack, M. J., Tin, C. C., Ellis, C. D., Spitznagel, J. A., and McMullin, P. G., in 4th. Int. Conf. Amorphous and Crystalline SiC, Santa Clara, CA, Oct. 10–11, 1991.Google Scholar
4. Zeller, M. V., Bellina, J. J., Saha, N., Filar, J., Hargraeves, J., and Will, H., Mat. Res. Soc. Symp. Proc. 97, 283 (1987).Google Scholar
5. Ohdomari, I., Sha, S., Aochi, H., Chikyow, T., and Suzuki, S., J. Appl. Phys. 62, 3747 (1987).Google Scholar
6. Shor, J. S., Weber, R. A., Provost, L. G., Goldstein, D., and Kurtz, A. D., J. Electrochem. Soc. 141, 579 (1994).Google Scholar
7. Porter, L. M., Glass, R. C., Davis, R. F., Bow, J. S., Kim, M. J., and Carpenter, R. W., Mat. Res. Soc. Symp. Proc. 282, 471 (1993).Google Scholar
8. Bellina, J. J. Jr. and Zeller, M. V., Mat. Res. Soc. Symp. Proc. 97, 265 (1987).Google Scholar
9. Villars, P. and Calvert, L. D., Pearson's Handbook of Crystallographic Data for Intermetallic Phases, (ASM, Metals Park, OH, 1985).Google Scholar
10. Levit, M., Grimberg, I., Weiss, B. -Z., and Eizenberg, M., J. Appl. Phys. 79, 1 (1996).Google Scholar
11. Levit, M., Grimberg, I., and Weiss, B. -Z., and Eizenberg, M., accept. J. Appl. Phys.Google Scholar
12. Basin, Y. M., Kuznetsov, V. M., Markov, V. T., and Guzei, L. S., Russ. Metall. 4, 197 (1988).Google Scholar