Correlation Between The Mechanical Stress And Microstructure In Reactive Bias Magnetron Sputtered Silicon Nitride Films

Published online by Cambridge University Press:  10 February 2011

Joo Han Kim ,
Won Sang Lee  and
Ki Woong Chunga
Joo Han Kim
Affiliation:
LG Corporate Institute of Technology, 16 Woomyeon-Dong, Seocho-Gu, Seoul 137–140, Korea
Won Sang Lee
Affiliation:
LG Corporate Institute of Technology, 16 Woomyeon-Dong, Seocho-Gu, Seoul 137–140, Korea
Ki Woong Chunga
Affiliation:
LG Corporate Institute of Technology, 16 Woomyeon-Dong, Seocho-Gu, Seoul 137–140, Korea
Get access

Abstract

The influence of ion bombardment on the mechanical stress and microstructure of sputtered silicon nitride (SiNx) films has been systematically investigated. Applied substrate bias voltage was used to control the bombardment energy in a radio frequency (rf) reactive magnetron sputtering system. The resultant films were characterized by transmission electron microscopy (TEM), atomic force microscopy (AFM), Fourier transform infrared spectroscopy (FT-IR), Rutherford backscattering spectrometry (RBS), stress and chemical etch rate measurements. As the bias voltage was increased, the internal stress in SiNx films became increasingly compressive and reached a value of about 18.3 × 109 dyne/cm2 at higher bias voltages. These correlated well with the transition of the film microstructure from a porous microcolumnar structure containing large void to the more densely packed one. The obtained results can be explained in terms of atomic peening by energetic particles, leading to densification of the microstructure. It was also found that the amount of argon incorporated in the film is increased with increasing bias voltage, whereas the oxygen content is decreased. The lowest etch rate in buffered HF solution, approximately 1.2 Å/sec, was observed with the application of a substrate bias of -50 V.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 505 , 1997 , 421
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Parsons, G. N., Souk, J. H., and Batey, J., J. Appl. Phys. 70, 1553 (1991).Google Scholar
2.Rao, V. B. and Koyama, R. Y., J. Electrochem. Soc. 131, 1674 (1984).Google Scholar
3.Chang, E. Y., Cibuzar, G. T., Vanhove, J. M., Nagarajan, R. M., and Pande, K. P., Appl. Phys. Lett. 53, 1638 (1988).Google Scholar
4.Movchan, B. A. and Demchishin, A. V., Phys. Met. Metallogr. 28, 83 (1969).Google Scholar
5.Thornton, J. A., J. Vac. Sci. Technol. A 4, 3059 (1986).Google Scholar
6.Messier, R. and Ross, R. C., J. Appl. Phys. 53, 6220 (1982).Google Scholar
7.Comas, J. and Wolicki, E. A., J. Electrochem. Soc. 117, 1197 (1970).Google Scholar
8.Liao, W.-S., Lin, C.-H., and Lee, S.-C., Appl. Phys. Lett. 65, 2229 (1994).Google Scholar
9.Windischmann, H., J. Vac. Sci. Technol. A 9, 2431 (1991).Google Scholar
10.Claassen, W. A. P., Valkenburg, W. G. J. N., Willemsen, M. F. C., and Wijgert, W. M. v. d., J. Electrochem. Soc. 132, 893 (1985).Google Scholar
11.Fourrier, A., Bosseboeuf, A., Bouchier, D., and Gautherin, G., Jpn. J. Appl. Phys. 30, 1469 (1991).Google Scholar