Spontaneous Growth of Nickel Silicide Nanowires and Formation of Self-Assembled Nanobridges by the Metal Induced Growth Method

Published online by Cambridge University Press:  01 February 2011

Joondong Kim ,
Wayne A. Anderson  and
Young-Joo Song
Joondong Kim
Affiliation:
Department of Electrical Engineering, University at Buffalo, State University of New York, Buffalo, NY 14260, USA
Wayne A. Anderson
Affiliation:
Department of Electrical Engineering, University at Buffalo, State University of New York, Buffalo, NY 14260, USA
Young-Joo Song
Affiliation:
High-Speed SoC team, Electronics and Telecommunications Research Insititute, Yuseong-gu, Daejeon, 305-350, Korea
Get access

Abstract

Nickel monosilicide (NiSi) nanowires (NWs) have been fabricated by the metal induced growth (MIG) method. Ni as a catalyst was deposited on a SiO2 coated Si wafer. In a DC magnetron sputtering system, the Ni reacts at 575°C with sputtered Si to give nanowires. Different metal catalysts (Co and Pd) were used to prove the MIG NW growth mechanism. NiSi NWs were a single crystal structure, 20-80 nm in diameter and 1-10 μm in length. The linear NW growth property provided nanobridge formation in a trenched Si wafer. The trenches in a Si wafer were made by dry etching and a simple, conventional metal lift off method. The self-assembled nanobridge can be applied to form nanocontacts at relatively low temperatures. The MIG NB is a promising 1 dimensional nanoscale building block to satisfy the need of ‘self and direct’ assembled ‘bottom-up’ fabrication concepts.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 872: Symposium J – Micro- and Nanosystems—Materials and Devices , 2005 , J7.2
Copyright
Copyright © Materials Research Society 2005

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

[1] Huang, Yu, Duan, Xiangfeng, Cui, Yi, and Lieber, Charles M., Nano Letters 2 (2002) 101 Google Scholar
[2] Alaca, B. Erdem, Sehitoglu, H., and Saif, Taher, Appl. Phys. Lett. 84 (2004), 4669.Google Scholar
[3] Ziegler, Kirk J., Lyons, D.M., and Holmes, Justin D., Erts, Donats, Polyakov, Boris, Olin, Hakan, Svensson, Krister, and Olsson, Eva, Appl. Phys. Lett. 84 (2004), 4047.Google Scholar
[4] Marrian, Christie R. K., and Tennant, D. M., J. Vac. Sci. Technol. A 21 (2003), S207.Google Scholar
[5] Thong, J. T. L, Oon, C.H., Yeadon, M., and Zhang, W.D., Appl. Phys. Lett. 81 (2002), 4823.Google Scholar
[6] Decker, C. A., Solanki, R., Freeouf, J. L., Carruthers, J. R., and Evans, D. R., Appl. Phys.Lett. 84 (2004), 1389.Google Scholar
[7] Yakushiji, K., Mitani, S., Takanashi, K., Takahashi, S., Maekawa, S., Imamura, H., and Fujimori, H., Appl. Phys. Lett. 78 (2001), 515.Google Scholar
[8] Islam, M Saif, Sharma, S, kamins, T I, and Williams, R Stanley. Nanotechnology. 15 (2004), L5.Google Scholar
[9] Nastaushev, Y. V., Cavrilova, T., Kachanova, M., Nenasheva, L., Kolosanov, V., Naumova, O.V., Popov, V.P., and , Assev, Mater. Sci. Eng. C 19 (2002), 189.Google Scholar
[10] Kim, Joondong, Anderson, Wayne A., Guliants, Elena A. and Bunker, Christopher E., Morphological Changes while Growing Nickel Monosilicide Nanowires, Boston U.S.A., Nov. 28 - Dec. 2, 2004, Materials Research Society Symposium Proceeding 854E (2004) U 5. 10.Google Scholar
[11] Kim, Joondong, and Anderson, Wayne A., Thin Solid Films, (In press).Google Scholar
[12] Bartur, M. and Nicolet, M-A., J. Appl. Phys. 54 (1983) 5404.Google Scholar
[13] Finstad, T.G., Mayer, J.W., and Nicolet, M-A., Thin Solid Films 51 (1978) 391 Google Scholar
[14] Kim, Joondong, Ji, Chunhai, and Anderson, Wayne A., Silicon Nanowire Growth at Relatively Low Processing Temperature, San Francisco, U.S.A., April 12-16, 2004, Materials Research Society Symposium Proceeding 818 (2004) M 11. 11.Google Scholar