Stress concentration on artificial pitting holes and fatigue life for aluminum alloy 6061-T6, undergoing rotating bending fatigue tests

Published online by Cambridge University Press:  01 February 2011

Víctor H. M. Lemus ,
Gonzalo M. D. Almaraz  and
J. Jesús V. Lopez
Víctor H. M. Lemus
Affiliation:
Universidad Michoacana (UMSNH), Santiago Tapia No. 403, Morelia Michoacán, 58000, México.
Gonzalo M. D. Almaraz
Affiliation:
Universidad Michoacana (UMSNH), Santiago Tapia No. 403, Morelia Michoacán, 58000, México.
J. Jesús V. Lopez
Affiliation:
Universidad Michoacana (UMSNH), Santiago Tapia No. 403, Morelia Michoacán, 58000, México.
Get access

Abstract

This work deals with rotating bending fatigue tests on aluminum alloy 6061-T6, under loading condition close to the elastic limit of the material. Results have been obtained for three types of specimens: without artificial pitting, specimens with one artificial pitting hole and specimens with two neighboring artificial pitting holes. Results show that fatigue endurance is reduced in the case of one pitting hole and considerably for two neighboring pitting holes. In order to explain this behavior, numerical analysis by FE are carried out to determine the stress concentrations for the three types of specimens. It is found that the stress concentration for two neighboring pitting holes is an exponential function of the separation between the two holes, under uniaxial loading. The probability to find two or more neighboring pitting holes in real industrial materials, such as cast iron, corroded or pitting metallic alloys is high; then, the stress concentration for two or more neighboring pitting holes needs to be considered for the fatigue prediction life under fatigue loading and corrosion attack applications.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 1276: Advanced Structural Materials–2010 , 2010 , 26
Copyright
Copyright © Materials Research Society 2010

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Ishihara, S, Saka, S.S., Nan, Z.Y., Goshima, T. and Sunada, S., Fatigue & Fracture of Engineering Materials & Structures 2006; 29: 472–480.Google Scholar
2. Paris, P.C, Palin-Luc, T., Tada, H. and Santier, N., Crack Paths 2009, September 23–25th 2009, Vicenza, Italy: 495–502.Google Scholar
3. Cerit, M., Genel, K., Eksi, S., Numerical investigation on stress concentration of corrosion pit, Engineering Failure Analysis 2009; 16: 2467–2472.Google Scholar
4. Sadowsky, M.A., Sternberg, E., Stress concentration around an ellipsoidal cavity in an body under arbitrary plane stress perpendicular to the axis of revolution of cavity, Journal of Applied Mechanics 1947, A191–A201.Google Scholar
5. Nadot, Y., Billaudeau, T., Multiaxial Fatigue Limit Criterion for Defective Materials, Engineering Fracture Mechanics 2006; 73:112–133.Google Scholar
6. Van der Walde, K., Hillberry, B.M., Characterization of pitting damage and prediction of remaining fatigue life, International Journal of Fatigue 2008; 30:106–118.Google Scholar
7. Jones, K., Hoeppner, D.W., The interaction between pitting corrosion, grain boundaries, and constituent particles during corrosion fatigue of 7075-T6 aluminum alloy, International Journal of Fatigue 2009; 31: 686–692.Google Scholar