1 Introduction
Frequency conversion of high-energy, high average power (HE-HAP) diode pumped laser systems opens up new applications from underwater laser shock peening of complex samples[ Reference Sano, Mukai, Yoda, Uehara, Chida and Obata 1 ] and laser induced damage testing at broader wavelength ranges to pumping of Ti:sapphire and optical parametric chirped pulse amplification (OPCPA) systems[ Reference Haefner, Bayramian, Betts, Bopp, Buck, Cupal, Drouin, Erlandson, Horacek, Horner, Jarboe, Kasl, Kim, Koh, Koubikova, Maranville, Marshall, Mason, Menapace, Miller, Mazurek, Naylon, Novak, Peceli, Rosso, Schaffers, Sistrunk, Smith, Spinka, Stanley, Steele, Stolz, Suratwala, Telford, Thoma, VanBlarcom, Weiss and Wegner 2 – Reference Archipovaite, Galletti, Oliveira, Ahmad, Clarke, Neely, Booth, Heathcote, Galimberti, Musgrave and Hernandez-Gomez 4 ]. Recently, the HE-HAP frequency conversion has gained even more importance due to the success of inertial confinement fusion experiments[ 5 ].
Currently, many laser systems with second harmonic conversion operate at, or above, kilowatt average power, but only with low pulse energy of a few mJ[ Reference Röcker, Loescher, Bienert, Villeval, Lupinski, Bauer, Killi, Graf and Ahmed 6 ] or J[ Reference Chi, Wang, Davenport, Menoni and Rocca 7 ]. The highest energy achieved around wavelength of 500 nm on a high average power system before this work was 60 J[ Reference Phillips, Banerjee, Mason, Smith, Spear, Vido, Ertel, Butcher, Quinn, Clarke, Edwards, Hernandez-Gomez and Collier 8 ].
In this paper we report second harmonic generation (SHG) of 95 J at a repetition rate of 10 Hz from the laser system Bivoj/DiPOLE[ Reference Mason, Divoký, Ertel, Pilař, Butcher, Hanuš, Banerjee, Phillips, Smith, De Vido, Lucianetti, Hernandez-Gomez, Edwards, Mocek and Collier 9 , Reference Divoký, Pilař, Hanuš, Navrátil, Denk, Severová, Mason, Butcher, Banerjee, De Vido, Edwards, Collier, Smrž and Mocek 10 ], which corresponds to 950 W of average power. It is, to the best of our knowledge, the highest average power in a high-energy system with energy of more than 1 J with a wavelength around 500 nm and corresponds to 58% increase in the state-of-the-art. Conversion efficiency of 79% was achieved by using flat top beam and pulse profiles and by successful optimization of depolarization by the polarimetric method[ Reference Slezák, Sawicka-Chyla, Divoký, Pilař, Smrž and Mocek 11 ].
2 Experiment
The output from a high average power ytterbium-doped yttrium aluminum garnet (Yb:YAG) laser system, Bivoj/DiPOLE, at 1030 nm was frequency converted to 515 nm using type-I phase matching in a lithium triborate (LBO) crystal. The LBO crystal (Coherent, Inc.) was optimized for SHG from 1030 nm laser radiation. The crystal had an aperture of 60 mm × 60 mm, thickness of 13 mm and cut angle theta of 90° and phi of 13.6°. Dual band anti-reflection (AR) coatings of 1030 and 515 nm were used on both faces to minimize total transmission losses to 0.25% and 0.75%, respectively. The crystal was placed into a windowless oven (IB Photonics) for temperature stabilization. The temperature was set to 30°C. Higher temperatures provided better conversion stability, as the oven uses ambient air to cool down the crystal, but with a lower conversion efficiency, because the large difference between the ambient temperature and the oven temperature creates higher temperature gradients in the crystal. A laser beam from the laser system is propagated to the harmonic conversion setup through a series of telescopes. They de-magnify the laser beam 1.56 times from 77 mm × 77 mm to 49 mm× 49 mm to increase the energy fluence on the crystal. The layout of the harmonic conversion setup can be seen in Figure 1. A pair of zero-order waveplates (λ/2, λ/4) was used to adjust the polarization at the input of the crystal to improve the conversion efficiency by maximizing the energy in the polarization parallel with the principal plane of the crystal. After passing through the crystal, the high-power beam containing unconverted fundamental and converted second harmonic beams was terminated in a water-cooled absorption beam dump. The 1030 nm light was absorbed in water and the 515 nm light was absorbed in colored glass filters suspended in a water tank. Glass plates with different absorption bands were used to distribute the energy absorption equally among them. In front of the beam dump, a sampling wedge (dielectrically coated R ~ 1% at 1030 and 515 nm) was placed so that a low-power reflection could be acquired and used for diagnostics. The diagnostic beam was divided according to wavelength by a dichroic mirror. Each diagnostic line contained an energy meter (Gentec-EO QE25LP) and diagnostic cameras (AVT Manta 145B) to monitor the image-relayed beam profiles.
The laser was operated with output energy of 130 J at a repetition rate of 10 Hz. The pulse duration of the flat top pulses was 10 ns with a rise/fall time of 0.75 ns. The spectrum was centered at 1029.8 nm and the bandwidth was around 1 pm. The polarization homogeneity was not uniform across the beam. The main reason for this is the heat dissipated in the amplifier head that generates stresses in the Yb:YAG gain media that create birefringence and change the polarization state of the beam with spatial variability over the beam cross-section. This polarization change is sometimes referred to as depolarization, although this term should be reserved for cases where polarized light is changed into non-polarized light. When this beam propagates through a linear polarizer, a portion of its energy is inevitably rejected, and this contributes to energy losses. In the main power amplifier of Bivoj, these losses can be as high as 50% (Figures 2(a) and 2(b)) if linear polarization is used at the amplifier input and without waveplates at the output. We placed a pair of zero-order waveplates (λ/2, λ/4) after the Faraday isolator after the main cryogenic pre-amplifier (10 J) of the Bivoj/DiPOLE system to change the input linear polarization into the main cryogenic power amplifier (100 J); the output polarization was adjusted by a similar pair in the harmonic conversion setup. By tweaking the input polarization only, the energy losses are decreased to 35% (Figures 2(c) and 2(d)). If only the output polarization is optimized, the energy losses decrease further to 32% (Figures 2(e) and 2(f)). By using a custom polarimetric technique to evaluate the Mueller matrix of the Bivoj system[ Reference Slezák, Sawicka-Chyla, Divoký, Pilař, Smrž and Mocek 11 ], we were able to estimate numerically the optimal input polarization to further decrease the energy losses to around 3% (Figures 2(g) and 2(h)). These results were obtained for output energy of 90 J, helium flow rate of 150 gps (gallons per second) and temperature of 120 K. We optimized the polarization homogeneity at lower energy output to avoid changes to the beam, as the maximum output energy is close to laser induced damage threshold of the optical components. The pump energy was adjusted to operate at the maximum energy extraction from the amplifier. At the maximum output energy of 130 J, we used more intense pumping and increased the flow rate to 180 gps. We adjusted the polarization homogeneity by slightly tweaking all waveplates and the energy losses dropped from around 5% to around 3% with similar profiles as in Figures 2(g) and 2(h). Once the polarization homogeneity was optimized, it did not require any adjustments at the given energy output. Note that vertical polarization is used for SHG.
After the optimization of polarization homogeneity, the LBO crystal was inserted into the position and aligned using a low-energy beam. Then the energy was gradually increased up to 130 J at the output of the laser (121 J on the crystal; the transmission of the optics from the output of the laser to the LBO crystal was 93.4%) and the phase matching angles were optimized. Energy conversion and conversion efficiency dependence are shown in Figure 3 and the temporal development is shown in Figure 4. The energy of SHG at 515 nm reached the value of 96 J and the conversion efficiency of 79% ± 0.6%. If we would count only the input energy on the polarization that is converted to the second harmonic (i.e., neglect the depolarization losses), the conversion efficiency would reach 81.5% ± 0.6%. Since the oven controls the temperature of the crystal holder, after the beam is propagated through the crystal, the absorption causes the average temperature of the crystal to rise above the set temperature. During this thermalization of the crystal, the converted energy and efficiency dropped, so we re-aligned the phase matching angles several times. While we could compensate for the overall temperature increase in the crystal by adjusting the phase matching angle, the induced temperature gradients could not be compensated for in such a way. Therefore, the output energy dropped to 94–95 J with conversion efficiency of 76% ± 0.6%, because of the temperature gradients. Converted energy steadily decreased over time because of the overall temperature increase, on the order of minutes, but it could be recovered by consecutive phase matching angle optimization. Energy stability of the input beam at fundamental frequency was 0.1% RMS (root mean square) and 0.6% P-t-P (peak-to-peak). The energy stability of the second harmonic beam at the beginning of the experiment was 1.5% RMS and 8% P-t-P (shots 1900–4100) and was caused by rapid heating of the crystal. After thermalization of the crystal and re-optimization of the phase matching, the energy stability improved to 0.8% RMS and 6% P-t-P (shots 7500–10,000). A further increase in energy stability could be achieved by improving the temperature control of the crystal or automatic phase matching angle optimization, which will be studied in detail in future work. The near-field beam profile of the input beam on the fundamental frequency and the corresponding converted beam at the energy of 95 J is shown in Figures 5(a) and 5(b).
3 Conclusion
The output of SHG of 95 J at 10 Hz at 515 nm was achieved for the first time and represents a 58% increase to the state-of-the-art. The SHG process was achieved using an LBO crystal placed in a temperature-controlled holder. The good uniformity of the near-field profile of the converted beam and high conversion efficiency has been achieved mainly by addressing the problem of stress induced non-uniform polarization changes originating from within the amplifier chain and their successful mitigation. The reported energy stability of SHG output is of the order of 0.8% RMS, which is below the laser performance capability and is caused mainly by the unstable temperature within the LBO crystal due to the high average power nature of the working beam. The instability of the crystal temperature will be addressed in the future by optimized design of the temperature stabilization controller.
Acknowledgements
This work was supported by the European Regional Development Fund and the state budget of the Czech Republic project HiLASE CoE (CZ.02.1.01/0.0/0.0/15_006/0000674) and the Horizon 2020 Framework Programme (H2020) (739573).