Composition and Chemical Structure of Nitrided Silica Gel
Published online by Cambridge University Press: 15 February 2011
Abstract
Sol/gel derived silica thin films were thermally treated in NH3 for four hours at temperatures up to 1300C. The films were analyzed by ellipsometry, X-ray photoelectron spectroscopy (XPS) and infrared spectroscopy (IR). Over 30 mol% nitrogen was incorporated in the film treated at 1300C. Using IR and XPS analyses, -NHx groups were found to be present after low temperature treatments, while nitrogen was incorporated in an oxynitride structure after the higher temperature treatments.
- Type
- Research Article
- Information
- Copyright
- Copyright © Materials Research Society 1984
References
REFERENCES
1.
Pantano, C. G., Glaser, P. M. and Armbrust, D. J., Ultrastructure Processing of Ceramics Glass and Composites, ed. Hench, L.L. and Ulrich, D., J. Wiley and Sons, NY.
1984.Google Scholar
2.
Glaser, P. M. and Pantano, C. G., accepted for publication in J. Non Cryst. Solids.Google Scholar
3.
Brinker, C. J., and Haaland, D. M., J. Amer. Ceram. Soc., 66 (11) 758–765 (1983).CrossRefGoogle Scholar
5.
Wurzbach, J. A. and Grunthaner, F. J., J. Electrochem Soc., 130 (3) 691–699 (1983).CrossRefGoogle Scholar
6.
Wagner, C. D., Riggs, W. M., Davies, L. E. and Moulder, J. F., Handbook of X-Ray Photoelectron Spectroscopy, p. 21–22, Perkin-Elmer Corp., Eden Prairie, Mn, 1979.Google Scholar
8.
Wu, C., King, C., Lee, M. and Chen, C., J. Electrochem Soc., 129 (7) 1559–1563 (1982).Google Scholar
9.
Morrow, B. A., Cody, I. A. and Lee, L. S. M., J. Phys. Chem., 79 (11) 2405–2408 (1975).CrossRefGoogle Scholar
11.
Kuiper, A. E. T., Koo, S. W., Habraken, F. H. P. M., and Tamminga, Y., J. Vac. Sci. Technol. B, 1 (1) 62–66 (1983).Google Scholar
12.
Raider, S. I., Flitsch, R., Aboaf, J. A. and Pliskin, W. A., J. Electrochem. Soc., 123 (4) 560–565 (1976).CrossRefGoogle Scholar
14.
Brow, R. K. and Pantano, C. G., accepted for publication in J. Amer. Ceram. Soc., 67 (4) (1984).CrossRefGoogle Scholar
- 8
- Cited by