CdSe Nanoparticle/Metal-Organic Inks For Printable Electronics

Published online by Cambridge University Press:  11 February 2011

Douglas L. Schulz
Douglas L. Schulz*
Affiliation:
CeraMem Corporation, Waltham, MA 02453, U.S.A.
Get access

Abstract

The research objective of this project was the spray deposition of CdSe films using a nanoparticle CdSe suspension as the precursor ink. This ink consisted of CdSe nanoparticles (nano-CdSe) mixed with a “reactive dispersant” in a non-aqueous solvent. The reactive dispersant, a metal-organic molecule, served two purposes; (1) to form a dispersed CdSe suspension at room temperature, and (2) to thermally “unzip” giving CdSe and a byproduct. The CdSe thereby formed could be deposited at the grain boundaries and serve to physically and electrically connect the CdSe nanoparticles at moderate, plastic-compatible temperatures. If electronics-grade CdSe layers could be produced at low deposition temperatures, this approach may be applicable to printed CdSe-based thin film field-effect transistors (TFTs) on flexible substrates.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 736: Symposium D – Electronics on Unconventional Substrates–Electrotextiles and Giant-Area Flexible Circuits , 2002 , D7.1
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

Brody, T.P. “CdSe – The Ideal Semiconductor for Active Matrix Displays” SPIE 1992, 1664, 2.Google Scholar
2 VanCalster, A., Vervaet, A., DeGycke, I., DeBaets, J., Vanfleteren, J. “Polycrystalline CdSe Films for Thin Film Transistors” J. Cryst. Growth 1988, 86, 924.Google Scholar
3 The observation of greater that 100% expected weight loss can be explained by residual solvent in the dried (i.e., dynamic vacuum for 48 h with one intermediate grinding) complex as was confirmed by nuclear magnetic resonance spectroscopy in deuterated solvent.Google Scholar
4 XRD and early TGA experiments utilized impure complexes as the purification step had yet to be developed. While the shape of the TGA curves for the crude samples was nearly identical to that of the purified, the total mass loss was much less. This observation might explain the impurities in the TGA residue of the crude materials.Google Scholar
5 Ripley, B.A., Nivi, B., Jacobsen, J.M. Science 1999, 286, 746–749.Google Scholar