Chemically Prepared Lead Magnesium Niobate Dielectrics

Published online by Cambridge University Press:  10 February 2011

B. A. Tuttle ,
J. A. Voigt ,
D. L. Sipola ,
W. R. Olson  and
D. M. Goy
B. A. Tuttle
Affiliation:
Sandia National Laboratories, Albuquerque, NM 87185
J. A. Voigt
Affiliation:
Sandia National Laboratories, Albuquerque, NM 87185
D. L. Sipola
Affiliation:
Sandia National Laboratories, Albuquerque, NM 87185
W. R. Olson
Affiliation:
Sandia National Laboratories, Albuquerque, NM 87185
D. M. Goy
Affiliation:
Sandia National Laboratories, Albuquerque, NM 87185
Get access

Abstract

A chemical solution powder synthesis technique has been developed that produces fine, uniform powders of lead magnesium niobate (PMN) with 60 to 80 nm crystallite size. The synthesis technique was based on the dissolution of lead acetate and alkoxide precursors in acetic acid followed by precipitation with oxalic acid/propanol solutions. Lead magnesium niobate ceramics fabricated from these chemically derived powders had smaller, more uniform grain size and higher dielectric constants than ceramics fabricated from mixed oxide powders that were processed under similar thermal conditions. Chem-prep PMN dielectrics with peak dielectric constants greater than 22,000 and polarizations in excess of 29 μC/cm2 were obtained for 1100°C firing treatments. Substantial decreases in dielectric constant and polarization were measured for chemically prepared PMN ceramics fired at lower temperatures, consistent with previous work on mixed oxide materials.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 495: Symposium W – Chemical Aspects of Electronic Ceramics Processing , 1997 , 185
Copyright
Copyright © Materials Research Society 1998

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Swartz, S. L. and Shrout, T.R., Mater. Res. Bull. XXVII, p. 1245 (1982).Google Scholar
2. Papet, P., Dougherty, J.P., and Shrout, T.R., J. Mater. Res. 5, p. 2902 (1990).Google Scholar
3. Wang, H.C. and Schulze, W.R., J. Am. Cer. Soc. 73, p. 825 (1990).Google Scholar
4. Chaput, F., Boilot, J-P., Lejeune, M., Papiernik, R., Huber-Pfalzgraf, L.G., J. Am. Ceram. Soc. 72, p. 1355 (1989).Google Scholar
5. Jeng, D-Y., Chen, C-J., Chaudhuri, S. R., Proceedings of the Eighth US-Japan Seminar on Dielectric and Piezoelectric Ceramics, p. 227 (1997).Google Scholar
6. Voigt, J.A., Sipola, D.L., Turtle, B.A. and Anderson, M.T., Sandia Technical Disclosure, SD–6106(1997).Google Scholar
7. Haertling, G.H. and Land, C.E., Ferroelectrics, 3, p. 269 (1972).Google Scholar
8. Hatanaka, T. and Hasegawa, H., Jpn. J. Appl. Phys. 31 p. 3245 (1992).Google Scholar
9. Narendar, Y. and Messing, G.L., J. Amer. Ceram. Soc. 80, p. 915 (1997).Google Scholar
10. Cross, L.E., Ferroelectrics 76, p. 241 (1987).Google Scholar
11. Samara, G. A., Phys. Rev. 77, p. 314 (1996).Google Scholar