Compound Formation And Silicon Behavior In Titanium And Tantalum Layered Aluminum Films

Published online by Cambridge University Press:  26 February 2011

B. W. Shen
Affiliation:
Semiconductor Process and Design Center, Texas Instruments. Inc. P.O. Box 225621. M.S. 944, Dallas, Texas75265.
J. M. Anthony
Affiliation:
Central Research Laboratory, Texas Instruments. Inc. P.O. Box 225621. M.S. 944, Dallas, Texas75265.
P-H. Chang
Affiliation:
Central Research Laboratory, Texas Instruments. Inc. P.O. Box 225621. M.S. 944, Dallas, Texas75265.
J. Keenan
Affiliation:
Central Research Laboratory, Texas Instruments. Inc. P.O. Box 225621. M.S. 944, Dallas, Texas75265.
R. Matyi
Affiliation:
Central Research Laboratory, Texas Instruments. Inc. P.O. Box 225621. M.S. 944, Dallas, Texas75265.
H. L. Tsai
Affiliation:
Central Research Laboratory, Texas Instruments. Inc. P.O. Box 225621. M.S. 944, Dallas, Texas75265.
Get access

Abstract

Thin film interaction in the material systems of titanium and tantalum-layered Al- 1% Si films has been studied using advanced material characterization techniques. Compound phase formation was analyzed based on results from X-ray diffraction analysis. Al3Ti was identified in the titanium-layered film after 450° C sintering. TaSi2 and unreacted Ta. however, were identified after the sintering. Silicon participated in the phase formation process by incorporating itself as a solute in the Al3Ti while transforming Ta into its silicide. This behavior is to be interpreted based on available ternary phase diagrams. Cross-sectional transmission electron microscopy results indicate that well defined layered films and columnar grains of aluminum were obtained which are believed to be the primary reasons for the observed electromigration improvement over the base metal.

Type
Research Article
Copyright
Copyright © Materials Research Society 1986

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Howard, J.K., White, J.F. and Ho, P.S., J. Appl. Phys. 49, 4083 (1978)Google Scholar
2. Shen, B.W., Bonifield, T.D. and McPherson, J.W., Proc. 2nd Int'l VLSI Multilevel Interconnection Conference, 1985, IEEE, ed. by Wade, T. E.. p. 114.Google Scholar
3. Shima, S., Moriya, T. and Kashiwagi, M., Proc. First Int'l VLSI Multilevel Interconnection Conference, 1984, IEEE ed. by Wade, T.E.. p. 61.Google Scholar
4. Gardner, D.S., et al. IEEE Tran. Electron Devices. ED–32, 174 (1985).Google Scholar
5. Howard, J.K., Lever, R.F., Smith, P.J., and Ho, P.S., J. Vac. Sci. Tech. 13. 68 (1976)Google Scholar
6. Huang, H-C.W. and Wittmer, M., in Thin films and Interfaces II, MRS Symp. Proc. vol. 25. edited by Baglin, J.E.E., Campbell, D.R. and Chu, W.K. (Elsevier Science Publishers, N.Y, 1984) p. 157.Google Scholar
7. Colgan, E.G., Palmstrom, C.J., and Mayer, J.W.. J. Appl. Phys. 58, 1838(1985)Google Scholar
8. Youdelis, W. and Yang, C., Metal Science. 14. 500 (1979).Google Scholar
9. Ramon, A. and Schubert, K., Z. Metallkd. 56, 44 (1965).Google Scholar
10. Murarka, S.P., Fraserm, D.B., Lindenberger, W.S., and Sinha, A.K., J. Appl. Phys. 51, 3241 (1980).Google Scholar
11. Murarka, S.P., Fraser, D.B., Sinha, A.K. and Levinstein, H.J., IEEE-J. Solid State Circuits SC–15, 474 (1980)Google Scholar
12. Owada, N.. Horiuchi, M., Nakata, K., and Hinode, K., Proc. 2nd Int'l VLSI Multilevel Interconnection Conference, 1985, IEEE, ed. by Wade, T. E.. p. 173.Google Scholar
13. Schob, V.O., Nowotny, H. and Benesovsky, F., Planseeber. Pulv Metall. 10, 65 (1962).Google Scholar
14. Nowotny, H., Bruki, C. and Benesovsky, F., Monach. Chem. 92, 116 (1961).Google Scholar