Effects of Growth Conditions on the Optical Properties of Heteroepitaxial ZnTe Grown by Molecular Beam Epitaxy

Published online by Cambridge University Press:  25 February 2011

Y. Zhang
Affiliation:
Department of Electrical Engineering, Arizona State University, Tempe, AZ 85287-5706
B. J. Skromme
Affiliation:
Department of Electrical Engineering, Arizona State University, Tempe, AZ 85287-5706
F. S. Turco-Sandroff
Affiliation:
Bellcore, Red Bank, NJ 07701
Get access

Abstract

We have performed low-temperature photoluminescence (PL) to characterize the properties of heteroepitaxial ZnTe grown by MBE as a function of Zn/Te flux ratio, growth temperature, ZnTe layer thickness, and type of IIl-V substrate. In contrast to most previous studies, we consider the effects of the residual thermal strain in the material and re-assign the shallow exciton peaks. The main features of the PL spectrum of ZnTe/GaAs for Te-rich growth conditions are double acceptor-bound exciton and oxygen isoelectronic center bound exciton peaks. Zn-rich conditions result in a strong shallow acceptor bound exciton peak, excitons bound to closely spaced acceptor pairs, and donor-acceptor pair peaks due to As and possibly other shallow acceptors. High growth temperature reduces the strength of peaks due to excitons bound to closely spaced acceptor pairs, oxygen related structures and a deep level peak. Thick layers are needed to avoid deep levels (possibly Ga related) which appear in the thin layers. The PL spectra for ∼1.3 µm thick ZnTe layers on GaAs and GaSb are almost identical. ZnTe/InP yields strong deep levels, which are possibly In related. Our results show that high quality ZnTe epilayers can be obtained at moderately high growth temperature under Zn-rich conditions, if the thickness is sufficiently large.

Type
Research Article
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Feldman, R.D., Austin, R.F., Bridenbaugh, P.M., Johnson, A.M., Simpson, W.M., Wilson, B.A., and Bonner, C.E., J. Appl. Phys. 64, 1191 (1988).CrossRefGoogle Scholar
2. Wilson, B.A., Bonner, C.E., Feldman, R.D., Austin, R.F., Kisker, D.W., Krajewski, I.J., and Bridenbaugh, P.M., J. Appl. Phys. M4, 3210 (1988)Google Scholar
3. Rajakarunanayake, Y., Cole, B.H., McCaldin, Y.O., Chow, D.H., Soderstrom, J.R., McGill, T.C., and Jones, C.M., AppI. Phys. Lett. 55, 1217 (1989).Google Scholar
4. Hishida, Y., Ishii, H., Toda, T., and Nina, T., J. Crystal Growth 95, 517521 (1989).CrossRefGoogle Scholar
5. Zhang, Y., Skromme, B.J., and Turco, F.S., in Electronic. Optical. and Device Properties of Layered Structures, ed. Hayes, J., Hybertsen, M.S., and Weber, E.R. (Mater. Res. Soc., Pittsburgh, 1990), Vol. EA-21, pp. 133136.Google Scholar
6. Dang, Le Si, Gobil, J., Saminadayar, K., and Tatarenko, S., Appl. Phys. Lett. 55, 235 (1989).CrossRefGoogle Scholar
7. Venghaus, H. and Dean, P.J., Phys. Rev. B 21, 1596 (1980).CrossRefGoogle Scholar
8. Dean, P.J., Kane, M.J., Magnea, N., Maigret, F de, Dang, Le Si, Nahmani, A., Romestain, R., and Skolnick, M.S., J. Phys. C: Solid State Phys. 18, 6185 (1985).Google Scholar
9. Yoneda, K., Hishida, Y., Toda, T, Ishii, H., and Niina, T., Appl. Phys. Lett. 45, 1300 (1984).Google Scholar
10. Dietz, D.E., Thomas, D.G., and Hopfield, J.J., Phys. Rev. Lett. 8, 391 (1962).Google Scholar
11. Dean, P.J. and White, A.M., Solid State Electron. 21, 1351 (1978).CrossRefGoogle Scholar
12. Molva, E. and Magnea, N., Phys. Stat. Sol. (b) 102, 475 (1980).Google Scholar