High-Temperature Ductility of Intermetallic Nickel Aluminide (IC-218LZr)

Published online by Cambridge University Press:  26 February 2011

A.R. Mirshams ,
R.H. Baldwin  and
V.K. Sikka
A.R. Mirshams
Affiliation:
Department of Mechanical Engineering, Southern University, Baton Rouge, LA 70813
R.H. Baldwin
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, TN 37831
V.K. Sikka
Affiliation:
Metals and Ceramics Division, Oak Ridge National Laboratory, P.O. Box 2008, Oak Ridge, TN 37831
Get access

Abstract

This paper reports the results of uniaxial and compression tests on IC-218LZr extruded bars at temperatures from 700 to 1000°C in air. Tensile results indicate reduction in ductility at temperatures between 750 to 900°C. However, the results show improvement in ductility above 950°C. Compression test results do not show a decrease in the ductility in the temperature range.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 213: Symposium Q – High-Temperature Ordered Intermetallic Alloys IV , 1990 , 649
Copyright
Copyright © Materials Research Society 1991

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Dieter, G.E., Workability Testing Techniques, ed. Dieter, G. E., (ASM International, Metals Park, Ohio) 1984, p. 1.Google Scholar
2. Liu, C.T. and Stiegler, J.O., Science, 226, 636 (1984).CrossRefGoogle Scholar
3. Kuhn, H. A., Metals Handbook, 9th edition, 14 (ASM International, Metals Park, Ohio, 1988) p. 388.Google Scholar
4. Liu, C.T. and Sikka, V.K., J. Met., 38, 19 (1986).Google Scholar
5. Mirshams, A.R., Summer Research Report, Oak Ridge National Laboratory, 1989.Google Scholar
6. Mirshams, A.R. and Sikka, V.K., J. Mater. Shaping Technol., 8, 123 (1990).CrossRefGoogle Scholar