Mechanical Enhancement Of Nanoporous Low-K Films As Interlayer Dielectrics By Ion Implantation

Published online by Cambridge University Press:  11 February 2011

Alok Nandini U. Roy ,
Zubin P. Patel ,
A. Mallikarjunan ,
H. Bakhru  and
T.-M. Lu
Alok Nandini U. Roy
Affiliation:
Department of Physics, University at Albany-SUNY, NY 12222, U.S.A
Zubin P. Patel
Affiliation:
Department of Physics, University at Albany-SUNY, NY 12222, U.S.A
A. Mallikarjunan
Affiliation:
Center for Integrated Electronics, Rensselaer Polytechnic Institute, Troy, New York, 12180
H. Bakhru
Affiliation:
Department of Physics, University at Albany-SUNY, NY 12222, U.S.A
T.-M. Lu
Affiliation:
Department of Physics, University at Albany-SUNY, NY 12222, U.S.A
Get access

Abstract

Thin films of Ultra-Low K materials such as Xerogel (K=1.76) and MSQ (K=2.2) were implanted with argon, neon, nitrogen, carbon and helium with 2 × 1015 cm−2 and 1 × 1016 cm−2 dose at energies varying from 20 to 50 keV at room temperature. In this work we showed that the surface hardness of the porous films is improved five times as compared to the as-deposited porous films sacrificing the dielectric constant up to 15% after implantation (e.g., from 1.76 to 2.0). The hardness persists after 450 °C annealing. It is also shown that implantation can prevent the penetration of chemical gases such as CVD precursors in the Ultra-Low K dielectrics during a CVD process.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 734: Symposia A/B – Defect-Mediated Phenomena in Ordered Polymers – Polymer/Metal Interfaces and Defect Mediated Phenomena in Ordered Polymers , 2002 , B5.3
Copyright
Copyright © Materials Research Society 2003

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Lee, W.W. and Ho, P.S. MRS Bulletin 22, 19 (1997)Google Scholar
2. Morgen, M., Ryan, E.T., Zhao, J-H, Hu, C., Cho, T., and Ho, P.S. Annu Rev. Mater. Sci. 30, 645 (2000)CrossRefGoogle Scholar
3. ITRS 2001 edition. International Technology Roadmap for Semiconductors Home Page, http://public.itrs.net (accessed January 2002)Google Scholar
4. Oleg, Kolosov, Kazushi, Yamanaka, Jpn. J. Appl. Phys. Vol. 32, 1993, pp. 1095–1098.CrossRefGoogle Scholar
5. Oliver, W.C. and Pharr, G.M., J. Mater. Res. 7, p.1564 (1992).Google Scholar
6. Dinelli, F., Biswas, S.K. Phys. Rev. B Vol. 61(20), May 2000 Google Scholar
7. Tsaur, B.Y., Liau, Z.L., Mayer, J.W., Appl. Phys. Lett. 34, 168 (1979)Google Scholar
8. Ziegler, J.F. and Chu, W.K., At. and Nucl. Data Tables 13, 481(1974)CrossRefGoogle Scholar
9. Modification of Low κ materials for ULSI Multilevel Interconnects by Ion Implantation MRS spring 2002, Symposium B (published)Google Scholar