SrTiO3 Films Prepared by MOCVD Using Novel Sr Source
Published online by Cambridge University Press: 15 February 2011
Abstract
SrTiO3 thin films have been prepared by MOCVD. A novel Sr source of Sr(DPM)2-tetraen2 was used to stabilize source delivery and to reduce the vaporization temperature of Sr source. Films were deposited on Pt/Ta/Si substrates at deposition temperatures from 450 °C to 600 °C. The relative dielectric constant was about 220 at the deposition temperatures from 550 °C to 600 °C for as-deposited 90-nm-thick films. The leakage current density was in the range of 10−7 A/cm2, typically.
- Type
- Research Article
- Information
- Copyright
- Copyright © Materials Research Society 1995
References
REFERENCES
[1]
Miyasaka, Y. and Matsubara, S.: Proc. 7th Int. Symp. Applicasions Ferroelectrics, 1990 (IEEE, Piscataway, 1991) p. 121.Google Scholar
[2]
Yamamichi, S., Sakuma, T., Takemura, K. and Miyasaka, Y.: Jpn. J. Appl. Phys.
30 (1991) 2193.Google Scholar
[3]
Van Buskirk, P.C., Gardiner, R., Kirlin, P.S. and Krupanidhi, S.: Proc. 8th Int. Symp. Applications Ferroelectrics, Greenville (1992) p. 340.Google Scholar
[4]
Kimura, T., Yamauchi, H., Machida, H., Kokubun, H. and Yamada, M.: Jpn. J. Appl. Phys.
33 (1994) 5119.Google Scholar
- 1
- Cited by