FT-IR spectra of Li(AlxCo1-x)O2 (x=0.1-0.5)

Published online by Cambridge University Press:  17 March 2011

W. Hao ,
C. Li ,
X. Meng ,
G. Chen  and
W. Xu
W. Hao
Affiliation:
Key Laboratory of Automobile Materials, Ministry of Education and Department of Materials Science, Jilin University, Changchun, 130023, People's Republic of China
C. Li
Affiliation:
Key Laboratory of Automobile Materials, Ministry of Education and Department of Materials Science, Jilin University, Changchun, 130023, People's Republic of China
X. Meng
Affiliation:
Key Laboratory of Automobile Materials, Ministry of Education and Department of Materials Science, Jilin University, Changchun, 130023, People's Republic of China
G. Chen
Affiliation:
Key Laboratory of Automobile Materials, Ministry of Education and Department of Materials Science, Jilin University, Changchun, 130023, People's Republic of China
W. Xu
Affiliation:
Institute of Optical Engineering and Physics, Chinese Academy of Science, Changchun
Get access

Abstract

FT-IR spectra from Li(AlxCo1-x)O2 (x=0.1-0.5) are reported. It was found out that there are four peaks located at 556cm−1, 601cm−1, 1438cm−1, 1498cm−1. First two peaks at 556cm−1 and 601cm−1 can be assigned to A2u and Eu vibration modes, respectively. The other two new peaks at 1438cm−1 and 1498cm−1 can not be explained clearly. With the increasing of Al concentration, all peaks position remain unchanged. However a relative change in the intensity of A2u and Eu peaks was observed.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 699: Symposium R – Electrically Based Microstructural Characterization III , 2001 , R7.3
Copyright
Copyright © Materials Research Society 2002

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1. Ceder, G., Chiang, Y.M., Sadoway, D.R., Aydinol, M.K., Jang, Y.-I. and Huang, B., Nature, 392, 694(1998)Google Scholar
2. Chen, G., Hao, W., Shi, Y., Wu, Y. and Perkowitz, S., J. Mater. Res. 15, 583 (2000)Google Scholar
3. Shi, Y., Hao, W., Chemical Journal of Chinese Universities, 21(4), 497(2000)Google Scholar
4. Hao, W., Shi, Y., Chen, G., Chemical Journal of Chinese Universities, 22(2), 175(2001)Google Scholar
5. Hewston, T.A. and Chamberland, B.L., J.Phys.Ghem.Solids, 148(2), 97(1987)Google Scholar
6. Huang, W. and Frech, R., Solid State Ionics, 395, 86(1996)Google Scholar
7. Inaba, M., Iriyama, Y., Ogumi, Z., Todzuka, Y., and Tasaka, A., J. Raman spectrosc. 28, 613(1997)Google Scholar