Epitaxial Nickel Disilicide Formation by Electron Beam Annealing

Published online by Cambridge University Press:  22 February 2011

R.E. Harper ,
E.A. Maydell-Ondrusz ,
I.H. Wilson  and
K.G. Stephens
R.E. Harper
Affiliation:
University Of Surrey, Guildford, Surrey, U.K.
E.A. Maydell-Ondrusz
Affiliation:
University Of Surrey, Guildford, Surrey, U.K.
I.H. Wilson
Affiliation:
University Of Surrey, Guildford, Surrey, U.K.
K.G. Stephens
Affiliation:
University Of Surrey, Guildford, Surrey, U.K.
Get access

Abstract

A multiply-scanned electron beam was used to form nickel silicides from thin nickel films on unimplanted and arsenic implanted silicon (100) substrates. Films of thickness 300, 660 and 1000Å were annealed using a power density of 7.9Wcm−2 and irradiation times of 5 to 150 secs.

Rutherford backscattering and channelling techniques were used to determine the stoichiometry, thickness and epitaxial quality of the annealed films. The thinnest gave a Xminof ∼ 18% and the thickest a Xmin of ∼ 40%. Resistivities were measured by the four-probe technique. Chemical composition was determined by X-ray and glancing angle electron diffraction (RHEED). Transmission electron microscopy (TEM) was used to estimate grain size of the disilicide phase and scanning electron microscopy (SEM) to study surface textures. The effect of arsenic implantation on growth rate, epitaxial quality and surface texture is demonstrated.

Type
Research Article
Information
MRS Online Proceedings Library (OPL) , Volume 25: Symposium C – Thin Films and Interfaces II , 1983 , 105
Copyright
Copyright © Materials Research Society 1984

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1. Tu, K.N. and Mayer, J.W., in: Thin Films - Interdiffusion and Reactions (ed. Poate, J.M., Tu, K.N. and Mayer, J.W.) Wiley N.Y. 1978, p. 359.Google Scholar
2. Murarka, S.P., Silicides for VLSI Applications, Academic Press, N.Y. 1983.Google Scholar
3. Wittmer, M. and Seidel, T.E., J. Appl. Phys. 49, 5827, 1979.Google Scholar
4. Ting, K.Y., Wittmer, M. and Tu, K.N., Proc. Ist Int. Symp. on VLSI Science and Technology Detroit 1982, p. 242 .Google Scholar
5. Wei, C.Y., Katz, W. and Smith, G., Thin Solid Films, 104, 215, 1983.Google Scholar
6. Ishiwara, H., Proc. Symp. Thin Solid Film Interfaces and Interactions, eds. Baglin, J.E.E. and Poate, J.M., (Electrochem. Soc. Inc., N.J., 1980, p.159).Google Scholar
7. Murarka, S.P., J. Vac. Sci. Technology 17, 775, 1980.CrossRefGoogle Scholar
8. Saitoh, S., Ishiwara, H. and Furukawa, S., Jpn. J. Appl. Phys. 20, Suppl. 20–1, 49, 1981.Google Scholar
9. Saitoh, S., Ishiwara, H., Asano, T. and Furukawa, S., Jpn. J. Appl. Phys. 20, 1649, 1981.Google Scholar
10. Chui, K.C.R., Poate, J.M., Rowe, J.E., Sheng, T.T. and Cullis, A.G., Appl. Phys. Lett. 38, 988, 1981.CrossRefGoogle Scholar
11. Chen, L.J., Mayer, J.W., Tu, K.N. and Sheng, T.T., Thin Solid Films, 93, 91 and , Chui, K.C.R., Poate, J.M., Rowe, J.E., Sheng, T.T. and Cullis, A.G., Appl. Phys. Lett.38 988, 1981135, 1982.Google Scholar
12. Tung, R.T., Gibson, J.M. and Poate, J.M., Phys. Rev. Lett., 50, 429, 1983.Google Scholar
13. Tung, R.T., Gibson, J.M., Jacobson, D.C. and Poate, J.M., Appl. Phys. Lett. 43, 476, 1983.Google Scholar
14. Lintech Instr. Co., Cambridge, England.Google Scholar
15. Maydell-Ondrusz, E.A., Harper, R.E., Abid, A., Hemment, P.L.F. and Stephens, K.G., this volume.Google Scholar
16. Lau, S.S. and Cheung, N.W., Thin Solid Films, 71, 117, 1980.Google Scholar