![Author ORCID: We display the ORCID iD icon alongside authors names on our website to acknowledge that the ORCiD has been authenticated when entered by the user. To view the users ORCiD record click the icon. [opens in a new tab]](https://www.cambridge.org/engage/assets/public/coe/logo/orcid.png){kind=logo}
Abstract
Extreme fast charging (XFC) of commercial lithium-ion batteries (LIBs) in ≤10-15 minutes will significantly advance the deployment of electric vehicles globally. However, XFC leads to considerable capacity fade, mainly due to graphite anode degradation. Non-destructive three-dimensional (3D) investigation of XFC-cycled anodes is crucial to connect degradation with capacity loss. Here, we demonstrate the viability of simultaneous neutron and X-ray tomography (NeXT) for ex-situ 3D visualization of graphite anode degradation. NeXT is advantageous because of the sensitivity of neutrons to Li and H and X-rays to Cu. We combine the neutron and X-ray tomography with micron resolution for material identification and segmentation on one pristine and one XFC-cycled graphite anode, thereby underscoring the benefits of the simultaneous nature of NeXT. Our ex-situ results pave the way for the design of NeXT-friendly LIB geometries that will allow operando and/or in-situ 3D visualization of graphite anode degradation during XFC.