Effect of storage in aqueous environments on polymer–metal interfacial fracture

Published online by Cambridge University Press:  03 March 2011

Yvete Toivola ,
Brian P. Somerday ,
Renée Shediac  and
Robert F. Cook
Yvete Toivola
Affiliation:
Department of Chemical Engineering and Materials Science, University of Minnesota, Minneapolis, Minnesota 94551
Brian P. Somerday
Affiliation:
Sandia National Laboratories, Livermore, California 55455
Renée Shediac
Affiliation:
Sandia National Laboratories, Livermore, California 55455
Robert F. Cook
Affiliation:
Department of Chemical Engineering and Materials Science, University of Minnesota, Minneapolis, Minnesota 94551
Get access

Abstract

The effect of environmental exposure on the fracture characteristics of two polymer–metal interfaces was measured using a four-point bend delamination test. Films of high-molecular-weight polymethylmethacrylate (PMMA) resin were spin-cast on metal-coated silicon wafer substrates, for which the metal was either titanium or aluminum. Sandwich beam specimens were fabricated and stored in one of the following conditions prior to the bending tests: vacuum desiccator at 25 °C, vacuum desiccator at 65 °C, distilled water at 25 °C, or distilled water at 65 °C. Load–displacement behavior measured during bending revealed significant differences between the delamination characteristics of the two PMMA–metal interfaces after vacuum exposure which were eliminated after the degrading effects of water exposure. Three distinctive load–displacement behaviors were observed: plateau, fracture at a single load; R-curve, fracture at increasing load with crack extension; and stick-slip, cycles of gradual load increase and sudden load drop with crack extension. PMMA–Al samples stored in vacuum desiccator at 25 °C exhibited R-curve fracture and the largest average crack driving force, GC, 12.2 (±0.5) J/m2, of all samples tested. After storage in 25 °C water, these PMMA–Al samples exhibited stick-slip fracture and GC decreased to 7.1 (±2.6) J/m2; storage in 65 °C water further decreased GC to 2.1 (±0.7) J/m2. PMMA–Ti samples exhibited stick-slip fracture after storage in vacuum desiccator at 25 °C, with an average GC of 8.0 (±2.6) J/m2; storage in 65 °C water resulted in a transition to plateau fracture and a decrease in GC to 1.6 (±0.3) J/m2. The initial difference and subsequent similarity are interpreted in terms of surface roughness and hydrolysis, respectively.

Keywords

AdhesionThin filmMicroelectrical mechanical (MEMS)
Type
Articles
Information
Journal of Materials Research , Volume 19 , Issue 2 , February 2004 , pp. 557 - 567
Copyright
Copyright © Materials Research Society 2004

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1Hruby, J.: MRS Bull. 26 337 (2001).CrossRefGoogle Scholar
2 Images courtesy of Sandia National Laboratories, Livermore, California.Google Scholar
3Kinloch, A.J.: J. Mater. Sci. 15 2141 (1980).Google Scholar
4Kinloch, A.J.: J. Mater. Sci. 17 617 (1982).CrossRefGoogle Scholar
5Brewis, D.M.Surface Analysis and Pretreatment of Plastics and Metals (Macmillan, New York, 1982), p. 1.Google Scholar
6Davis, G.D. in Polymer/Inorganic Interfaces, edited by Opila, R.L., Boerio, F.J., and Czanderna, A.W. (Mater. Res. Soc. Symp. Proc. 304 Pittsburgh, PA, 1993), p. 3.Google Scholar
7Bajaj, R., Zutshi, A., Surana, R., Naik, M. and Pan, T.: MRS Bull. 27 776 (2002).Google Scholar
8Ray, G.W. in Low–Dielectric Constant Materials IV, edited by Chiang, C., Ho, P.S., Lu, T-M., and Wetzel, J.T. (Mater. Res. Soc. Symp. Proc. 511 Warrendale, PA, 1998), p. 199.Google Scholar
9Snodgrass, J.M., Hotchkiss, G. and Dauskardt, R.H. in Electronic Packaging Materials Science X, edited by Belton, D.J., Gaynes, M., Jacobs, E.G., Pearson, R., and Wu, T., (Mater. Res. Soc. Symp. Proc. 515 Warrendale, PA, 1998), p. 37.Google Scholar
10Yeung, D.T.S., Yuen, M.M.F., Lam, D.C.C. and Chan, P.C.H.: J. Electronics Manufacturing 10 139 (2000).Google Scholar
11Marsh, W.E., Kanakarajan, K. and Osborn, G.D. in Polymer/Inorganic Interfaces, edited by Opila, R.L., Boerio, F.J., and Czanderna, A.W. (Mater. Res. Soc. Symp. Proc., 304 Pittsburgh, PA, 1993), p. 91.Google Scholar
12Lee, K-W. and Viehbeck, A.: IBM J. Res. Develop. 38 457 (1994).CrossRefGoogle Scholar
13Suo, Z. and Hutchinson, J.W.: Mater. Sci. Eng. A 107 135 (1989).Google Scholar
14Charalambides, P.G., Lund, J., Evans, A.G. and McMeeking, R.M.: J. Appl. Mech. 56 77 (1989).Google Scholar
15Charalambides, P.G., Cao, H.C., Lund, J. and Evans, A.G.: Mech. Mater. 8 269 (1990).CrossRefGoogle Scholar
16Snodgrass, J.M., Pantelidis, D., Jenkins, M.L., Bravman, J.C. and Dauskardt, R.H.: Acta Materialia 50 2395 (2002).Google Scholar
17Lee, J.A., Wetzel, J.T., Merrill, C. and Ho, P.S. in Silicon Materials—Processing, Characterization and Reliability, edited by Veteran, J., O’Meara, D.L., Misra, V., and Ho, P. (Mater. Res. Soc. Symp. Proc. 716 Warrendale, PA, 2002), p. B12.12.1.Google Scholar
18Tsui, T., Goldberg, C., Braeckelman, G., Filipiak, S., Ekstrom, B.M., Lee, J.J., Jackson, E., Herrick, M., Iacoponi, J., Martin, J. and Sieloff, D. in Materials, Technology and Reliability for Advanced Interconnects and Low-k Dielectrics, edited by Oehrlein, G.S., Maex, K., Joo, Y-C., Ogawa, S., and Wetzel, J.T. (Mater. Res. Soc. Symp. Proc. 612 Warrendale, PA, 2001), p. D1.2.1.Google Scholar
19Hughey, M.P., Morris, D.J., Cook, R.F., Bozeman, S.P., Kelly, B.L., Chakravarty, S.L.N., Harkens, D.P. and Stearns, L.C.: Eng. Fract. Mech. 71 245 (2003).CrossRefGoogle Scholar
20Lucksanasombool, P., Higgs, W.A.J., Higgs, R.J.E.D. and Swain, M.V.: Biomaterials 24 1159 (2003).Google Scholar
21Ohashi, K.L., Yerby, S.A. and Dauskardt, R.H.: J. Biomed. Mater. Res. 54 419 (2001).3.0.CO;2-3>CrossRefGoogle Scholar
22Wang, H-F., Gerberich, W.W. and Angelo, J.E.: J. Mater. Res. 10 2367 (1995).Google Scholar
23Katipelli, L.R., Agarwal, A. and Dahotre, N.B.: Mater. Sci. Eng. A 289 34 (2000).Google Scholar
24Claybourn, M. in Infrared Reflection Spectroscopy of Polymers: Analysis of Films, Surfaces and Interfaces, edited by Urban, M.W. (Global Press, Chicago, IL, 1998).Google Scholar
25Anderson, T.L.Fracture Mechanics: Fundamentals and Applications (CRC Press, Boca Raton, 1995), pp. 47–48, 142–148.Google Scholar
26Bader, M.G., Hamerton, I., Hay, J.N., Kemp, M. and Winchester, S.: Composites: Part A 31 603 (2000).Google Scholar
27Shih, H-H. and Hamed, G.R.: J. Appl. Polymer Sci. 63 333 (1997).Google Scholar
28Paek, S-H., Lee, S-W. and Durning, C.J.: J. Adhesion Sci. Technol. 13 423 (1999).Google Scholar
29Konstadinidis, K., Thakkar, B., Chakraborty, A., Potts, L.W., Tannenbaum, R., Tirrell, M. and Evans, J.F.: Langmuir 8 1307 (1992).Google Scholar
30Packham, D.E. in Adhesion Aspects of Polymeric Coatings, edited by Mittal, K.L. (Plenum Press, New York 1981), p. 19.Google Scholar
31Schultz, J. and Nardin, M. in Theories and Mechanisms of Adhesion, edited by Mittal, K.L. and Pizzi, A. (Marcel Dekker, New York 1999), p. 2.Google Scholar
32Rance, D.G. in Surface Analysis and Pretreatment of Plastics and Metals, edited by Brewis, D.M. (Macmillan, New York 1982) p. 121.Google Scholar
33Fowkes, F.M. in Electronic Packaging Materials Science, edited by Giess, E.A., Tu, K-N., and Uhlmann, D.R. (Mater. Res. Soc. Symp. Proc. 40 Pittsburgh, PA, 1985), p. 239.Google Scholar
34Chehimi, M.M. in Adhesion Promotion Techniques: Technological Applications, edited by Mittal, K.L. and Pizzi, A. (Marcel Dekker, New York 1999), p. 27.Google Scholar
35Davis, G.D.: Surf. Interface Analysis 17 439 (1991).Google Scholar
36Bolger, J.C. in Adhesion Aspects of Polymeric Coatings, edited by Mittal, K.L. (Plenum Press, New York 1981), p. 3.Google Scholar
37McCafferty, E. and Wightman, J.P.: Surf. Interface Analysis 26 549 (1998).Google Scholar
38Dwight, D.W. in First International Congress on Adhesion Science and Technology, edited by van Ooij, W.J. and And, H.R.erson, Jr. (VSP BV, Utrecht, The Netherlands, 1998), p. 63.Google Scholar
39Mallik, R.R., Pritchard, R.G., Horley, C.C. and Comyn, J.: Polymer 26 551 (1985).Google Scholar
40McCafferty, E., Wightman, J.P. and Cromer, T.F.: J. Electrochem. Soc. 146 2849 (1999).CrossRefGoogle Scholar
41Brockmann, W. in Adhesion Aspects of Polymeric Coatings, edited by Mittal, K.L. (Plenum Press, New York 1981), p. 265.Google Scholar
42Metson, J.B., Hyland, M.M., Gillespie, A. and Hemmingsen-Jensen, M.: Colloids Surf. 93 173 (1994).Google Scholar
43Bowditch, M.R., Hiscock, D. and Moth, D.A.: Int. J. Adhes. Adhes. 12 164 (1992).CrossRefGoogle Scholar
44Arnold, J.C.: J. Mater. Sci. 33 5193 (1998).Google Scholar
45Kusy, R.P., Whitley, J.Q. and Kalachandra, S.: Polymer 42 2585 (2001).Google Scholar