Pulsed electrodeposition of diamond-like carbon films

Published online by Cambridge University Press:  31 January 2011

Hao Wang ,
Ming-Rong Shen ,
Zhao-Yuan Ning ,
Chao Ye  and
He-Sun Zhu
Hao Wang
Affiliation:
Film Material Laboratory, Department of Physics, Suzhou University, Suzhou 215006, People's Republic of China
Ming-Rong Shen
Affiliation:
Film Material Laboratory, Department of Physics, Suzhou University, Suzhou 215006, People's Republic of China
Zhao-Yuan Ning
Affiliation:
Film Material Laboratory, Department of Physics, Suzhou University, Suzhou 215006, People's Republic of China
Chao Ye
Affiliation:
Film Material Laboratory, Department of Physics, Suzhou University, Suzhou 215006, People's Republic of China
He-Sun Zhu
Affiliation:
The Research Center of Materials Science, Beijing Institute of Technology, Beijing 100081, People's Republic of China
Get access

Abstract

Diamond-like carbon (DLC) films have been prepared by electrolysis of methanol solution using a pulse-modulated source. The deposition rate of the films is enhanced significantly compared to that of dc value. That the films do not contain bonded hydrogen is confirmed by infrared spectra. The structures of the films are characterized by Raman spectroscopy. These films show chemical inertness and hardness values in the range 12.5–19 GPa. Current-voltage characteristics of the films are measured, indicating that the resistivity is in the 107 Ω cm range and the breakdown field is larger than 1 MV cm−1.

Type
Articles
Information
Journal of Materials Research , Volume 12 , Issue 11 , November 1997 , pp. 3102 - 3105
Copyright
Copyright © Materials Research Society 1997

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

REFERENCES

1.Rossi, F., Andre, B., van Veen, A., Mijnarends, P. E., Schut, H., Delplancke, M. P., Gissler, W., Haupt, J., Lucazeau, G., and Abello, L., J. Appl. Phys. 75, 3121 (1994).CrossRefGoogle Scholar
2.Namba, Y., J. Vac. Sci. Technol. A 10, 3368 (1992).Google Scholar
3.Suzuki, T., Manita, Y., Yamazaki, T., Wada, S., and Noma, T., J. Mater. Sci. 30, 2067 (1995).CrossRefGoogle Scholar
4.Wang, H., Shen, M. R., Ning, Z. Y., Ye, C., Cao, C.B., Dang, H. Y., and Zhu, H. S., Appl. Phys. Lett. 69, 1074 (1996).CrossRefGoogle Scholar
5.Hatta, A., Kudata, K., Mori, Y., Ito, T., Sasaki, T., Hiraki, A., and Okada, S., Appl. Phys. Lett. 66, 1602 (1995).Google Scholar
6.Matanabe, Y., Shiratani, M., and Makino, H., Appl. Phys. Lett. 57, 1616 (1990).Google Scholar
7.Thaler, B. J., Ketterson, J. B., and Hilliard, J. E., Phys. Rev. Lett. 41, 336 (1978).Google Scholar
8.Cohen, U., Koch, F. B., and Sard, R., J. Electrochem. Soc. 130, 1987 (1983).CrossRefGoogle Scholar
9.Cohen, U., Walton, K. R., and Sard, R., J. Electrochem. Soc. 131, 2489 (1984).CrossRefGoogle Scholar
10.Kondo, K., Yokoyama, M., and Shinohara, K., J. Electrochem. Soc. 142, 2256 (1995).CrossRefGoogle Scholar
11.Angus, J. C., Thin Solid Films 216, 126 (1992).Google Scholar
12.Cho, N-H., Krishnan, K. M., Veirs, D. K., Rubin, M. D., Hopper, C. B., Bhushan, B., and Bogy, D. B., J. Mater. Res. 5, 2543 (1990).Google Scholar
13.Mehta, B. R., Ogeyzlo, E. A., Diamond Relat. Mater. 3, 10 (1993).CrossRefGoogle Scholar
14.Dischler, B., Brandt, G., and Koidl, P., Appl. Phys. Lett. 42, 636 (1983).CrossRefGoogle Scholar
15.Couderc, P. and Catherine, Y., Thin Solid Films 146, 93 (1987).CrossRefGoogle Scholar
16.Richter, A., Scheibe, H-J., Pompe, W., Brezeinka, K-W., and Muhling, I., J. Non-Cryst. Solids 88, 131 (1986).Google Scholar
17.Ramsteiner, M. and Wagner, J., Appl. Phys. Lett. 51, 1355 (1987).CrossRefGoogle Scholar
18.Bacsa, W. S., Lannin, J. S., Pappas, D. L., and Cuomo, J. J., Phys. Rev. B 47, 10931 (1993).CrossRefGoogle Scholar
19.Knight, D. S. and White, W. B., J. Mater. Res. 4, 385 (1989).CrossRefGoogle Scholar
20.Wang, Q., Allred, D. D., and Gonzalez-Hernandez, J., Phys. Rev. B 47, 6119 (1993).CrossRefGoogle Scholar
21.Nicklow, I. R., Wakabayashi, N., and Smith, H. G., Phys. Rev. B 5, 4951 (1991).CrossRefGoogle Scholar
22.Fitchen, D. B., Mol. Cryst. Liq. Cryst. 83, 95 (1982).CrossRefGoogle Scholar
23.Mulazzi, E., Brivio, G. P., Faulques, E., and Lefrant, S., Solid State Commun. 46, 851 (1983).CrossRefGoogle Scholar
24.Khasawinah, S. A., Popovici, G., Farmer, J., Sung, T., Prelas, M. A., Chamberlain, J., and White, H., J. Mater. Res. 10, 2523 (1995).CrossRefGoogle Scholar
25.Dillon, R. O., Woollam, J. A., and Katkanant, V., Phys. Rev. B 29, 3482 (1984).CrossRefGoogle Scholar
26.Beeman, D., Silverman, J., Lynds, R., and Anderson, M. R., Phys. Rev. B 30, 870 (1984).Google Scholar