Metastable Structures in Al Thin Films Before the Onset of Corrosion Pitting as Observed using Liquid Cell Transmission Electron Microscopy

  • See Wee Chee (a1), David J. Duquette (a1), Frances M. Ross (a2) and Robert Hull (a1)
Abstract
Abstract

One of the fundamental challenges in understanding the early stages of corrosion pitting in metals protected with an oxide film is that there are relatively few techniques that can probe microstructure with sufficient resolution while maintaining a wet environment. Here, we demonstrate that microstructural changes in Al thin films caused by aqueous NaCl solutions of varying chloride concentrations can be directly observed using a liquid flow cell enclosed within a transmission electron microscope (TEM) holder. In the absence of chloride, Al thin films did not exhibit significant corrosion when immersed in de-ionized water for 2 days. However, introducing 0.01 M NaCl solutions led to extensive random formation of blisters over the sample surface, while 0.1 M NaCl solutions formed anomalous structures that were larger than the typical grain size. Immersion in 1.0 M NaCl solutions led to fractal corrosion consistent with previously reported studies of Al thin films using optical microscopy. These results show the potential of in situ liquid cell electron microscopy for probing the processes that take place before the onset of pitting and for correlating pit locations with the underlying microstructure of the material.

Copyright
Corresponding author
* Corresponding author. see.wee.chee@gmail.com
Footnotes
Hide All

Current address: Hummingbird Scientific, Lacey, WA 98516, USA

Footnotes
References
Hide All
Abd-El-Nabey B., Khalil N. & Khamis E. (1984). Alkaline corrosion of aluminium in water-organic solvent mixtures. Surf Technol 22, 367376.
Abd-El-Nabey B., Khalil N. & Khamis E. (1985). The acid corrosion of aluminium in water-organic solvent mixtures. Corros Sci 25, 225232.
Balázs L. (1996). Corrosion front roughening in two-dimensional pitting of aluminum thin layers. Phys Rev E 54, 11831189.
Balazs L. & Gouyet J. (1995). Two-dimensional pitting corrosion of aluminium thin layers. Physica A 217, 319338.
Bargeron C. & Givens R. (1980). Precursive blistering in the localized corrosion of aluminum. Corrosion 36, 618625.
Chee S.W., Hull R. & Ross F.M. (2012). Liquid cell TEM of the corrosion of metal films in aqueous solutions. Microsc Microanal 18(Suppl 2), 11101111.
Chee S.W., Ross F.M., Duquette D. & Hull R. (2013). Studies of corrosion of Al thin films using liquid cell transmission electron microscopy. MRS Proceedings 1525, mrsf12–1525–ss11–03.
De Jonge N. & Ross F.M. (2011). Electron microscopy of specimens in liquid. Nat Nanotechnol 6, 695704.
Frankel G. (1997). Pit growth in thin metallic films. Mater Sci Forum 247, 18.
Frankel G.S. (1998). Pitting corrosion of metals. J Electrochem Soc 145, 21862198.
Frankel G. & Sridhar N. (2008). Understanding localized corrosion. Mater Today 11, 3844.
Holtz M.E., Yu Y., Gao J., Abruna H.D. & Muller D.A. (2013). In situ electron energy loss spectroscopy in liquids. Microsc Microanal 19, 10271035.
Klein K.L., Anderson I.M. & de Jonge N. (2011). Transmission electron microscopy with a liquid flow cell. J Microsc 242, 117123.
Malladi S.R.K., Tichelaar F.D., Xu Q., Wu M.Y., Terryn H., Mol J.M.C., Hannour F. & Zandbergen H.W. (2013). Quasi in situ analytical TEM to investigate electrochemically induced microstructural changes in alloys: AA2024-T3 as an example. Corros Sci 69, 221225.
Malladi S.R.K., Xu Q., Tichelaar F.D., Zandbergen H.W., Hannour F., Mol J.M.C. & Terryn H. (2012). Early stages during localized corrosion of AA2024 TEM specimens in chloride environment. Surf Interface Anal 45, 16191625.
McCafferty E. (2003). Sequence of steps in the pitting of aluminum by chloride ions. Corros Sci 45, 14211438.
Natishan P.M., McCafferty E. & Hubler G.K. (1989). Localized corrosion behavior of aluminum surface alloys produced by ion implantation and ion beam mixing. Mater Sci Eng 116, 4146.
Noh K.W., Liu Y., Sun L. & Dillon S.J. (2012). Challenges associated with in-situ TEM in environmental systems: The case of silver in aqueous solutions. Ultramicroscopy 116, 3438.
Szklarska-Smialowska Z. (1999). Pitting corrosion of aluminum. Corros Sci 41, 17431767.
Unocic R., Adamczyk L., Dudney N., Alsem D., Salmon N. & More K. (2011). In-situ TEM characterization of electrochemical processes in energy storage systems. Microsc Microanal 17(Suppl 2), 15641565.
Williamson M.J., Tromp R.M., Vereecken P.M., Hull R. & Ross F.M. (2003). Dynamic microscopy of nanoscale cluster growth at the solid-liquid interface. Nat Mater 2, 532536.
Woehl T.J., Jungjohann K.L., Evans J.E., Arslan I., Ristenpart W.D. & Browning N.D. (2013). Experimental procedures to mitigate electron beam induced artifacts during in situ fluid imaging of nanomaterials. Ultramicroscopy 127, 5363.
Recommend this journal

Email your librarian or administrator to recommend adding this journal to your organisation's collection.

Microscopy and Microanalysis
  • ISSN: 1431-9276
  • EISSN: 1435-8115
  • URL: /core/journals/microscopy-and-microanalysis
Please enter your name
Please enter a valid email address
Who would you like to send this to? *
×

Keywords:

Metrics

Full text views

Total number of HTML views: 4
Total number of PDF views: 51 *
Loading metrics...

Abstract views

Total abstract views: 233 *
Loading metrics...

* Views captured on Cambridge Core between September 2016 - 22nd November 2017. This data will be updated every 24 hours.