Pressure Studies for 1111 and 11 Type Iron-based Superconductors
Published online by Cambridge University Press: 01 February 2011
Abstract
In the recent development of the studies in iron-based superconductors, high-pressure experiments have been played an important role. Large enhancement of Tc with applying pressure and pressure-induced superconductivity were reported in LaFeAsO1-xFx. In this work, electrical, magnetic and structural measurements on 1111 type Ca(Fe1-xCox)AsF and 11 type Fe(Se1-xTex)0.92 under high pressure have been performed. For Ca(Fe1-xCox)AsF, the substitution of Co suppressed the magnetic and structural transitions and raised superconductivity. Pressure-induced superconductivity was observed for x = 0.0 and 0.05. The highest Tc was obtained in parent compound under high pressure, in contrast to LaFeAsO1-xFx. These results suggest that the substitution of Co increases carrier concentration and induces disorder in the FeAs superconducting layer. For FeTe0.92, pressure-induced superconductivity was not detected under high pressure up to 19 GPa, although the resistive anomaly due to the structural and magnetic phase transition was suppressed by applying pressure.
Keywords
- Type
- Research Article
- Information
- Copyright
- Copyright © Materials Research Society 2010