High Rate Deposition of High Quality ZnO:Al by Filtered Cathodic Arc
Published online by Cambridge University Press: 16 August 2011
Abstract
High quality ZnO:Al (AZO) thin films were prepared on glass substrates by direct current filtered cathodic arc deposition. Substrate temperature was varied from room temperature to 425°C, and samples were grown with and without the assistance of low power oxygen plasma (75W). For each growth condition, at least 3 samples were grown to give a statistical look at the effect of the growth environment on the film properties and to explore the reproducibility of the technique. Growth rate was in the 100-400 nm/min range but was apparently random and could not be easily traced to the growth conditions explored. For optimized growth conditions, 300-600 nm AZO films had resistivities of 3-6 x 10-4 Ωcm, carrier concentrations in the range of 2-4 x 1020 cm3, Hall mobility as high as 55 cm2/Vs, and optical transmittance greater than 90%. These films are also highly oriented with the c-axis perpendicular to the substrate and a surface roughness of 2-4 nm.
Keywords
- Type
- Research Article
- Information
- MRS Online Proceedings Library (OPL) , Volume 1315: Symposium MM – Transparent Conducting Oxides and Applications , 2011 , mrsf10-1315-mm03-25
- Copyright
- Copyright © Materials Research Society 2011
References
- 1
- Cited by