Efficient Acceptor Activation in AlxGa1−xN/GaN Doped Superlattices

Published online by Cambridge University Press:  03 September 2012

I. D. Goepfert
Affiliation:
Department of Electrical and Computer Engineering Boston University, Boston, MA 02215
E. F. Schubert
Affiliation:
Department of Electrical and Computer Engineering Boston University, Boston, MA 02215
A. Osinsky
Affiliation:
NZ Applied Technologies, Woburn, MA 01801
P. E. Norris
Affiliation:
NZ Applied Technologies, Woburn, MA 01801
Get access

Abstract

Mg-doped superlattices consisting of uniformly doped AlxGa1−xN and GaN layers are analyzed by Hall-effect measurements. Acceptor activation energies of 70 meV and 58 meV are obtained for superlattice structures with an Al mole fraction of x = 0.10 and 0.20 in the barrier layers, respectively. These energies are significantly lower than the activation energy measured for Mg-doped GaN thin films. At room temperature, the doped superlattices have free hole concentrations of 2 × 1018 cm−3 and 4 × 1018 cm−3 for x = 0.10 and 0.20, respectively. The increase in hole concentration with Al content of the superlattice is consistent with theory. The room temperature conductivity measured for the superlattice structures are 0.27 S/cm and 0.64 S/cm for an Al mole fraction of x = 0.10 and 0.20, respectively.

Type
Research Article
Copyright
Copyright © Materials Research Society 1999

Access options

Get access to the full version of this content by using one of the access options below. (Log in options will check for institutional or personal access. Content may require purchase if you do not have access.)

References

1 Strite, S. and Morkoc, H., GaN, AlN, and InN: A review, Journal of Vacuum Technology B10(4), 1237 (1992)Google Scholar
2 Nakayama, H., Hacke, P., Khan, M.R.H., Detchprohm, T., Hiramatsu, K., and Sawaki, N., Electrical transport properties of p-GaN, Japanese Journal of Applied Physics 35, L282 (1996)Google Scholar
3 Fischer, S., Wetzel, C., Haller, E. E., and Meyer, B. K., On p-type doping in GaN -acceptor binding energies, Applied Physics Letters 67, 1298 (1995)Google Scholar
4 Ronning, C., Carlson, E. P., Thomson, D. B., and Davis, R. F., Optical activation of Be implanted into GaN, Applied Physics Letters 73, 1622 (1998)Google Scholar
5 Lee, J. W., Pearton, S. J., Zolper, J. C., Stall, R. A., Hydrogen passivation of Ca acceptors in GaN, Applied Physics Letters 68, 2102 (1996)Google Scholar
6 Schubert, E. F., Grieshaber, W., and Goepfert, I. D., Enhancement of deep acceptor activation in semiconductors by superlattice doping, Applied Physics Letters 69, 3737 (1996)Google Scholar
7 Katsuragawa, M., Sota, S., Komori, M., Anbe, C., Takeuchi, T., Sakai, H., Amano, H., Akasaki, I., Thermal ionization energy of Si and Mg in AlGaN, Journal of Crystal Growth 189/190, 528 (1998)Google Scholar
8 Tanaka, T., Watanabe, A., Amano, H., Kobayasi, Y., Akasaki, I., Yamazaki, S., and Koike, M., p-type conduction in Mg-doped GaN and Al0.08GaN0.92N grown by metalorganic vapor phase epitaxy, Applied Physics Letters 65, 593 (1994)Google Scholar
9 Saxler, A., Mitchel, W. C., Kung, P., and Razeghi, M., Aluminum gallium nitride shortperiod superlattces doped with magnesium, Applied Physics Letters 74, 2023 (1999)Google Scholar
10 We use εr = 9.0 and εr = 8.5 for the relative dielectric constant for GaN and AlN, respectively. These values are compiled in Reference 1.Google Scholar
11 The experimental effective hole mass in AlxGa1.xN is unknown at this time. Although, Katsuragawa et al. in Reference 7 reported no significant change in the activation energy of Mg in AlxGa1.xN indicating no significant change in the hole mass. See, for instance,Google Scholar
, Gil, Group III Nitride Semiconductor Compounds (Clarendon Press, Oxford, 1998)Google Scholar